Adhesive tape used for solar cell assembly and preparation method thereof
A technology of solar cells and tapes, applied in the direction of electrical components, circuits, adhesives, etc., can solve the problems of affecting the sealing performance of adhesives, affecting the application effect, slow curing speed, etc., and achieve good initial adhesion, cost reduction, and easy bonding.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1:
[0028] The adhesive applied on the front surface of the tape substrate is mainly used for bonding. In parts by weight, the components and content of the adhesive are:
[0029] Ammonium Sulfate (APS)
[0030] Tackifying resin
[0031] First, prepare the adhesive in a reactor equipped with a condenser, a mechanical stirrer, a dropping funnel, nitrogen inlet and outlet, and a thermometer. Adopt pre-emulsification process, pass in nitrogen protection, weigh according to the above formula components: HAM, BA, MMA, AA, HEA, AMPS, SDS, OP-10 and 300ml deionized water into the reactor, stir to pre-emulsify 1 hour. Then take 200ml of pre-emulsion, add sodium bicarbonate to adjust the pH to about 5, add 10ml initiator APS (20%) solution, add it to the reactor, continue to pass nitrogen protection, control the temperature at 85 ℃, turn on the stirrer, and control the speed At 400r / min. When the material in the reactor gradually turned into a blue seed emulsion, th...
Example Embodiment
[0033] Example 2:
[0034] 1. Adhesive which is coated on the front surface of the tape substrate and mainly used for bonding. In parts by weight, the components and content of the adhesive are:
[0035] Ammonium Sulfate (APS)
[0036] 3-methacryloxypropyl trimethoxysilane (MPTS)
[0037] First, prepare the adhesive in a reactor equipped with a condenser, a mechanical stirrer, a dropping funnel, nitrogen inlet and outlet, and a thermometer. Weigh according to the above formula components: HAM, BA, MMA, AA, HEA, AMPS, SDS, OP-10 and 300ml of deionized water into the reactor, stir and pre-emulsify for 1 hour. Then take 200ml of pre-emulsion, add sodium bicarbonate to adjust the pH to about 5, add 15ml of initiator APS (20%) solution, add it to the reactor, continue to pass nitrogen protection, control the temperature at 85℃, start the stirrer, and control the speed At 400r / min. When the material in the reactor gradually turned into a blue seed emulsion, the remaining monomers...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap