Chrome manganese tungsten and molybdenum high alloy wear-resistant cast iron ball and preparation method thereof

A technology of tungsten-molybdenum and alloys, which is applied in the field of chromium-manganese-tungsten-molybdenum high-alloy wear-resistant cast iron balls and its preparation, can solve the problems of insufficient hardenability and toughness, poor wear resistance of the casting core, and early fracture, etc., to achieve The effect of low out-of-round rate and broken rate, reduced power consumption, and simple preparation method

Inactive Publication Date: 2013-02-13
HUNAN CHANGJIANG WEARPROOF NEW MATERIAL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to insufficient hardenability and toughness of single chromium alloyed cast iron, the core of the casting has poor wear resistance or early fracture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The technical scheme of the present invention will be further described below through specific embodiments:

[0011] The invention provides a chromium-manganese-tungsten-molybdenum high-alloy wear-resistant cast iron ball, which contains 18-24% chromium, 1.0-1.2% manganese, 0.2-0.3% tungsten, 0.1-0.3% molybdenum, and The amount of vanadium is 0.1~0.15%, and the rest is iron and impurities.

[0012] The preparation method of the chromium manganese tungsten molybdenum high alloy wear-resistant cast iron ball comprises the following steps:

[0013] S1: Prepare carbon steel, ferrochrome, ferromanganese, ferrotungsten, ferromolybdenum, and ferrovanadium, and add a small amount of rare earth as auxiliary materials, and melt them together in an intermediate frequency electric furnace at 1700 degrees for 15 minutes;

[0014] S2: grinding and polishing the obtained step S1 after casting;

[0015] S3: Quenching the product obtained in step S2 at a high temperature of 980°C for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a chrome manganese tungsten and molybdenum high alloy wear-resistant cast iron ball and a preparation method thereof. The preparation method comprises the following steps: preparing materials of carbon steel, chrome iron, manganese iron, tungsten iron, molybdenum iron and vanadium iron, adding a small amount of rare earth as an auxiliary material, melting into a whole at a high temperature of 1700 DEG C in a medium frequency furnace for 15 min, moulding by casting and grinding and polishing, and then quenching at a high temperature of 980 DEG C for 20 h and annealing at a low temperature of 300 DEG C, so as to obtain the chrome manganese tungsten and molybdenum high alloy wear-resistant cast iron ball containing the components by weight percent: 18-24 percent of chrome, 1.0-1.2 percent of manganese, 0.2-0.3 percent of tungsten, 0.1-0.3 percent of molybdenum, 0.1-0.15 percent of vanadium and the balance of iron and impurities. The chrome manganese tungsten and molybdenum high alloy wear-resistant cast iron ball has the strict requirement for matching precision of various elements, so as to lower the out-of-roundness rate and the breakage rate in the operation; and the preparation method is simple in process, effectively reduces the electric energy loss, and achieves the energy conservation and consumption reducing effects.

Description

technical field [0001] The invention relates to a wear-resistant cast iron material, in particular to a chromium-manganese-tungsten-molybdenum high-alloy wear-resistant cast iron ball and a preparation method thereof. Background technique [0002] Due to the high content of alloying elements, high chromium cast iron material has intermittent network distribution of eutectic carbides, high hardness and impact toughness, especially when preparing wear-resistant liners for cement industry ball mills, it shows excellent wear resistance and toughness , and the production cost is low, and it has been rapidly popularized and applied in industries such as metallurgy, mining, building materials, and thermal power generation. However, due to the lack of hardenability and toughness of single chromium alloyed cast iron, the core of the casting has poor wear resistance or early fracture. Contents of the invention [0003] Aiming at the problems in the prior art, the present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/06C22C33/08C21D5/00
Inventor 戴益群戴利华戴勃群
Owner HUNAN CHANGJIANG WEARPROOF NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2023 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap