Twist-resisting polyvinyl chloride synthetic leather and manufacturing method thereof

A polyvinyl chloride and synthetic leather technology, applied in chemical instruments and methods, synthetic resin layered products, textiles and papermaking, etc., can solve problems such as hydrolysis resistance, insufficient weather resistance, product quality problems, residues, etc., and achieve good results Vapor permeability, moisture absorption, conductivity, increased flexibility, and high bonding fastness

Inactive Publication Date: 2013-03-27
HEFEI ANSHAN COATING FABRICS
View PDF5 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other issues limit its further wide application
The twist-resistant PVC synthetic leather has excellent hydrolysis resistance, abrasion resistance, scratch resistance, flame retardant and other advantages, but there are problems in product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] A twist-resistant polyvinyl chloride synthetic leather, including a surface layer, a foam layer and an adhesive layer, a raised cloth,

[0026] The surface layer is prepared from the following raw materials in parts by weight (kg):

[0027] SG-2 type PVC resin 60, SG-6 type PVC resin 40, isophthalate 20, phthalate polyester 10, trioctyl trimellitate 15, PVC color paste 6, zinc stearate 1. Protein powder 1, zinc oxide 20, magnesium oxide 15, N660 carbon black 15, modified attapulgite 10, bis(dioctyloxypyrophosphate) ethylene titanate 1, antioxidant 168 2, Crosslinking agent TAC 2, aluminate coupling agent DL-411 2;

[0028] The foam layer is made of the following raw materials in parts by weight (kg):

[0029] SG-3 type PVC resin 40, SG-6 type PVC resin 50, SG-2 type PVC resin 30, isophthalate 20, phthalate polyester 15, trioctyl trimellitate 15, acetyl Triethyl citrate 35, N,N-dinitrosopentamethylenetetramine 1, foaming agent (909DU80) 1, ammonium carbonate 2, protei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses twist-resisting polyvinyl chloride synthetic leather which comprises a surface layer, a foaming layer, a bonding layer and fluffing cloth. The twist-resisting polyvinyl chloride synthetic leather is characterized by being prepared from the following components in parts by weight: 50-60 parts of SG-2 PVC (Polyvinyl Chloride) resin, 30-40 parts of SG-6 PVC resin, 20-25 parts of isophthalic ester, 10-15 parts of phthalic polyester, 10-15 parts of trioctyl trimellitate, 5-6 parts of PVC color cream, 1-2 parts of zinc stearate, 1-2 parts of protein powder, 20-25 parts of zinc oxide, 10-15 parts of magnesium oxide, 10-15 parts of N660 carbon black, and 5-10 parts of modified attapulgite. Through improvement of formula and process provided by the invention, the flexibility of the synthetic leather is enhanced, and the synthetic leather has a natural and comfortable handfeel similar to that of natural leather. The synthetic leather is not easy to damage or tear within 3-5 years.

Description

technical field [0001] The invention belongs to the technical field of chemical synthetic leather fabric processing, in particular to a twist-resistant polyvinyl chloride synthetic leather and a manufacturing method thereof. Background technique [0002] At present, polyurethane and twist-resistant polyvinyl chloride synthetic leather are widely used in commercial furniture and household furniture and other furniture fields. Polyurethane synthetic leather has the advantages of high imitation and good hand feeling, and has been widely favored by the market. However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other problems limit its further wide application. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/06B32B27/12B32B27/18B32B37/02B32B37/12C08L27/06C08K13/06C08K5/12C08K3/22C08K3/34C09C1/42C09C3/08C09C3/06
Inventor 藏德虎
Owner HEFEI ANSHAN COATING FABRICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap