A nano-modified, wood coating technology, used in antifouling/underwater coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problem of low VOC emission, achieve good storage stability, weather resistance and adhesion. The effect of good focus and convenient construction

Inactive Publication Date: 2013-04-24
高凡
View PDF4 Cites 53 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems existing in the existing water-based wood c...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare raw materials according to the following parts by mass: 30 parts of acrylic resin emulsion; 70 parts of polyurethane resin emulsion; 10 parts of nano-silica sol; 10 parts of nano-alumina; 5 parts of nano-titanium dioxide; 4 parts of nano-silver; 2 parts of propylene glycol methyl ether; Foamaster 50 0.05 parts; DISPERBYK-190 0.1 parts; YK-337 0.05 parts; ASE-60 0.05 parts; wax emulsion 5 parts; APH95 0.05 parts.

Embodiment 2

[0026] Prepare raw materials according to the following mass parts: 70 parts of acrylic resin emulsion; 30 parts of polyurethane resin emulsion; 15 parts of nano-silica sol; 15 parts of nano-alumina; 8 parts of nano-titanium dioxide; 2 parts of nano-silver; parts; BYK345 1 part; BYK338 0.1 part; AB-04 0.1 part; wax emulsion 6 parts; APH95 0.1 part.

Embodiment 3

[0028] Prepare raw materials according to the following mass parts: 40 parts of acrylic resin emulsion; 60 parts of polyurethane resin emulsion; 20 parts of nano-silica sol; 20 parts of nano-alumina; 10 parts of nano-titanium dioxide; 3 parts of nano-silver; 4 parts of dipropylene glycol propyl ether; 0.3 parts; BYK346 0.8 parts; BYK331 0.5 parts; AT-03 0.5 parts; wax emulsion 10 parts; APH95 0.5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Surface dry timeaaaaaaaaaa
Hard work timeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel nano modified antimicrobial water-based woodware paint which comprises acrylic resin emulsion, polyurethane resin emulsion, nano silica sol, nano aluminum oxide, nano titanium dioxide, nano silver, film-forming assistant, defoaming agent, wetting and dispersing agent, leveling agent, thickening agent, wax emulsion and pH regulator. The nano materials dispersed in the water-based paint enhance the hardness of the coated film, so that the coated film has excellent yellowing resistance, aging resistance and mold resistance.

Description

technical field [0001] The invention relates to a wood coating, in particular to a nano-modified antibacterial water-based wood coating. Background technique [0002] 7,000 years ago, the primitive people in Hemudu, Yuyao, Zhejiang Province began to use wooden lacquered bowls. The Xia, Shang, and Western Zhou dynasties have gradually changed from purely using natural lacquer to using pigments to adjust the lacquer. People gradually understand and become familiar with the performance of lacquer, and use and transform the unique properties of lacquer, such as durability, no fading, no fear of moisture, bright and beautiful. , Serving to beautify one's own life, there is exquisite Chinese lacquerware, and people's life has been rich and colorful since then. However, with the development of the wood industry, China has become the largest exporter of wood products. Wood coatings generally use open coating, which causes a large amount of VOC emissions and poses a huge haz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/00C09D175/04C09D7/12C09D5/14
Inventor 高凡
Owner 高凡
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap