Novel carbon-carbon nanotube lithium ion battery cathode material and preparation method thereof

A technology of lithium-ion batteries and carbon nanotubes, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of large irreversible capacity of carbon nanotubes, affecting physical and electrochemical performance, and no charge-discharge platform, etc., to achieve good performance Axial one-dimensional conductivity, excellent anti-attenuation performance, and the effect of a good voltage platform

Inactive Publication Date: 2015-05-20
YANGZHOU YET NEW ENERGY MATERIAL TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the irreversible capacity of carbon nanotubes is also large, the first cycle efficiency is low, and there is no obvious charge-discharge platform
In addition, due to its small diameter and large aspect ratio, it is easy to agglomerate and not easily dispersed, which affects its physical and electrochemical performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] The preparation method of the novel carbon-carbon nanotube lithium ion battery anode material includes the following steps:

[0017] 1) Prepare raw materials: spherical graphite, carbon nanotubes, organic carbon powder;

[0018] 2) Put the carbon nanotubes and organic carbon powder of step 1) into a ball mill for multiple stages and mixes. When putting them in batches, one of the materials is put in at one time, and the other is divided into five equally. Put it in at a time, the interval time for each putting is 1-2 hours, the total mixing time is 10-12 hours, to obtain the coating material, the particle size of the coating material is 2-6μm; the carbon nanotubes and organic carbon The weight ratio of powder is 3:7;

[0019] 3) The spherical graphite of step 1) and the coating material prepared in step 2) are stirred to fully mix, and the stirring and mixing time is 1-3 hours, so that the coating material is evenly wrapped on the surface of the spherical graphite; the coatin...

Embodiment 1

[0023] The preparation method of the novel carbon-carbon nanotube lithium ion battery anode material includes the following steps:

[0024] 1) Prepare 10KG of spherical graphite as the nucleation matrix, carbon nanotubes, and organic carbon powder;

[0025] 2) Put the carbon nanotubes and organic carbon powder in step 1) into the ball mill in batches for multiple classification and mixing. First put all the carbon nanotubes into the ball mill, and then put the organic carbon powder in five times evenly. The interval between the insertions is 1.5 hours, the total mixing time is 10 hours, and the coating material is 0.87KG, and the particle size of the coating material is 2 μm; the weight ratio of the carbon nanotubes and the organic carbon powder is 3:7;

[0026] 3) Fully stir 10KG of spherical graphite and 0.87KG of coating material in a stirring device for 1 hour, so that the coating material is evenly wrapped on the surface of the spherical graphite; the coating material accounts f...

Embodiment 2

[0030] The preparation method of the novel carbon-carbon nanotube lithium ion battery anode material includes the following steps:

[0031] 1) Prepare 10KG of spherical graphite as the nucleation matrix, carbon nanotubes, and organic carbon powder;

[0032] 2) Put the carbon nanotubes and organic carbon powder in step 1) into the ball mill in batches for multiple classification and mixing. First put all the organic carbon powder into the ball mill, and then put the carbon nanotubes into the ball mill five times evenly. The interval between the insertions is 1 hour, the total mixing time is 10 hours, and the coating material is 1.11KG, and the particle size of the coating material is 3 μm; the weight ratio of the carbon nanotubes and the organic carbon powder is 3:7;

[0033] 3) Fully stir 10KG of spherical graphite and 1.11KG of coating material in a stirring device for 1.5 hours so that the coating material is evenly wrapped on the surface of the spherical graphite; the coating mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel carbon-carbon nanotube lithium ion battery cathode material and a preparation method thereof, and belongs to the technical field of lithium ion batteries and the nanometer technology field. The novel carbon-carbon nanotube lithium ion battery cathode material is characterized in that the novel carbon-carbon nanotube lithium ion battery cathode material is formed by spherical graphite and a cladding material wrapped on the surface of the spherical graphite, and the cladding material accounts for 8-12% of the total weight of the spherical graphite and the cladding material; and the cladding material is prepared through mixing carbon nanotubes with organic carbon powder, and the weight ratio of the carbon nanotubes to the organic carbon powder is 3:7. The novel carbon-carbon nanotube lithium ion battery cathode material prepared in the invention can well solve the carbon nanotube agglomeration phenomenon through multi-time grading diffusion, the cladding material is wrapped on the surface of the spherical graphite, and the carbon nanotubes generate a pompon-like grid structure on the surface of the spherical graphite, so the surface strength is enhanced, the conductive performance and the anti-damping performance are substantially improved, and the first discharge capacity is substantially improved.

Description

Technical field [0001] The invention relates to a lithium ion battery negative electrode material and a preparation method thereof, in particular to a novel carbon-carbon nanotube lithium ion battery negative electrode material and a preparation method thereof, belonging to the technical field of lithium ion batteries and the field of nanotechnology. Background technique [0002] Because lithium-ion batteries have the important advantages of high voltage, high capacity, long cycle life, and good safety performance, they have broad application prospects in the fields of portable electronic devices and electric vehicles. Spherical natural graphite has a high lithium storage capacity, a good voltage platform, and is low in price. It is one of the common anode materials in the current market. However, as spherical graphite is used as a negative electrode material for lithium-ion batteries, the SEI film formed during the charge-discharge process is prone to continue to collapse, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/38
CPCY02E60/10
Inventor 钱承亮
Owner YANGZHOU YET NEW ENERGY MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap