Method for preparing cadmium sulphide/graphite oxide composite material in solid phase

A composite material, solid-phase preparation technology, applied in cadmium sulfide, graphite, nanotechnology for materials and surface science, etc., can solve the problems of harsh experimental conditions and high energy consumption, and achieve simple operation, high yield and low cost. Effect

Inactive Publication Date: 2013-06-19
XINJIANG UNIVERSITY
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the methods for preparing cadmium sulfide and graphene composites include hydrothermal method and microwave method. However, these methods involve harsh exp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cadmium sulphide/graphite oxide composite material in solid phase

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0011] Embodiment 1: Accurately weigh 0.01 mole of cadmium acetate and place it in an agate mortar, add 20 mg of graphite oxide after fully pulverizing it, grind for 60 minutes and mix evenly, add 0.01 mole of thioacetamide, then mix it Grind thoroughly for 60 minutes and let stand for 3 hours to ensure complete solid phase reaction. Wash it with deionized water and absolute ethanol, filter it with suction, and dry it in a drying oven at 60°C for 2 hours to obtain the cadmium sulfide / graphite oxide composite material.

specific Embodiment approach 2

[0012] Embodiment 2: Accurately weigh 0.01 mole of cadmium chloride and place it in an agate mortar, add 20 mg of graphite oxide after it is fully ground, grind for 60 minutes and mix evenly, add 0.01 mole of thioacetamide, and then It was thoroughly ground for 60 minutes and left for 3 hours to ensure complete solid phase reaction. Wash it with deionized water and absolute ethanol, filter it with suction, and dry it in a drying oven at 60°C for 2 hours to obtain the cadmium sulfide / graphite oxide composite material.

specific Embodiment approach 3

[0013] Specific embodiment 3: Accurately weigh 0.01 mole of cadmium sulfate and place it in an agate mortar, add 20 mg of graphite oxide after fully pulverizing it, grind for 60 minutes and mix evenly, add 0.01 mole of thioacetamide, then mix it Grind thoroughly for 60 minutes and let stand for 3 hours to ensure complete solid phase reaction. Wash it with deionized water and absolute ethanol, filter it with suction, and dry it in a drying oven at 60°C for 2 hours to obtain the cadmium sulfide / graphite oxide composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a cadmium sulphide/graphite oxide composite material in a solid phase and belongs to the field of preparation of nano materials. The method provided by the invention comprises that cadmium metal salt, graphite oxide and thioacetamide react at room temperature, and low heat solid-phase synthesis of the cadmium sulphide/graphite oxide composite material is achieved. The low heat solid-phase chemical method for preparing the cadmium sulphide/graphite oxide composite material has the characteristics of easy operation, no solvent, high yield, low cost and simple synthetic process; and the cadmium sulphide/graphite oxide composite material prepared by the invention has large specific surface area and high reaction activity and has a broad application prospect in the fields of solar cells, photocatalysis and the like.

Description

technical field [0001] The invention relates to a method for preparing a cadmium sulfide / graphite oxide composite material in a solid phase, and belongs to the field of nanometer material preparation. Background technique [0002] In recent years, nanomaterials have attracted extensive attention of researchers because of their unique physical and chemical properties. As a very important semiconductor nanomaterial, cadmium sulfide has great application prospects in the fields of semiconductor light-emitting devices, nonlinear optical materials, and photocatalysis because of its specific optical, electrical, thermal, and magnetic properties. However, due to the small size effect and surface effect of cadmium sulfide nanomaterials, it is easy to agglomerate during the preparation process, which affects its performance and practical application. Therefore, various methods have been adopted to slow down the agglomeration of CdS nanomaterials. Among them, the use of templates as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G11/02B82Y30/00C01B32/23
Inventor 贾殿赠陈凤娟曹亚丽
Owner XINJIANG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap