Preparation method of ferrum-aluminum titanium carbide composite material
A composite material and titanium carbide technology, which is applied in the field of preparation of Fe3Al-TiC composite materials, can solve problems such as the reduction of plasticity at room temperature, and achieve the effect of improving hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0011] Example 1:
[0012] Weigh the mass percentage Fe 3 85% of Al powder and 15% of TiC powder are put into a sealed tank, and dry mixed in a ball mill for 4 hours at a speed of 200r / min to obtain Fe 3 The composite powder of Al and 15% TiC, the mixed composite powder is put into a graphite mold, and placed in a vacuum hot press sintering furnace for hot press molding and sintering, the vacuum degree is 1×10 -1 Pa, the heating rate is 10°C / min, the sintering temperature is 1250°C, the sintering pressure is 30MPa, and the sintering time is 30min. After sintering, cool to room temperature and take out the material to obtain Fe 3 Al-15%TiC composite material, the material properties are given in the table below.
[0013]
Example Embodiment
[0014] Example 2:
[0015] Weigh the mass percentage Fe 3 Al powder 75%, TiC powder 25%, put into a sealed tank, dry mixed in a ball mill for 6 hours, the speed of which is 200r / min, to obtain Fe 3 The composite powder of Al and 25% TiC, put the mixed composite powder into a graphite mold, and place it in a vacuum hot-pressing sintering furnace for hot-press molding and sintering, the vacuum degree is 1×10 -1 Pa, the heating rate is 10°C / min, the sintering temperature is 1300°C, the sintering pressure is 35MPa, and the sintering time is 35min. After sintering, cool to room temperature and take out the material to obtain Fe 3 Al-25%TiC bulk composite material, the material properties are given in the table below.
[0016]
Example Embodiment
[0017] Example 3:
[0018] Weigh the mass percentage Fe 3 Al powder 65%, TiC powder 35%, put into a sealed tank, dry mixed in a ball mill for 6 hours, the speed of which is 250r / min, to obtain Fe 3 The composite powder of Al and 35% TiC, put the mixed composite powder into a graphite mold, and place it in a vacuum hot-press sintering furnace for hot-press molding and sintering, the vacuum degree is 1×10 -2 Pa, the heating rate is 15°C / min, the sintering temperature is 1300°C, the sintering pressure is 40MPa, and the sintering time is 40min. After sintering, the furnace is cooled to room temperature, and the material is taken out to obtain Fe 3 Al-35%TiC bulk composite material, the material properties are given in the table below.
[0019]
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap