Binder for electrode of lithium battery and lithium battery containing the binder

A binder and lithium battery technology, applied in battery electrodes, adhesives, secondary batteries, etc., can solve problems such as difficult to achieve the required capacity of non-carbon materials, and achieve the effect of increasing life and improving conduction paths

Active Publication Date: 2013-07-10
SAMSUNG SDI CO LTD
View PDF4 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Non-carbon-based materials can have very high capacity due to a capacity density 10 times or more that of graphite, but are difficult to achieve due to very

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Binder for electrode of lithium battery and lithium battery containing the binder
  • Binder for electrode of lithium battery and lithium battery containing the binder
  • Binder for electrode of lithium battery and lithium battery containing the binder

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0071] Preparation Example 1: Preparation of Pretreated Carbon Nanotube (CNT) Composition

[0072] (1) Introduction of carboxyl groups by acid treatment of CNT

[0073] 2 g of multi-walled CNTs having a diameter of about 10 nm to 20 nm and a length of about 10 μm to 50 μm were treated with 300 ml of a 20 wt% nitric acid solution at 40° C. for 24 hours. Then, 1 g of the cleaned CNTs was soaked in 200 ml of a 3:1 (v / v%) solution of concentrated sulfuric acid and concentrated nitric acid, treated with ultrasonic waves at room temperature for 3 hours, and then stirred at 70 °C for 6 hours. Next, the acid solution on the CNTs was removed by filtration and washed with pure water several times, and then the resulting product was dried in a vacuum oven at 80 °C for 24 hours to prepare CNTs with carboxyl groups (raw material A).

[0074] (2) Modification of CNTs with carboxyl groups (1)

[0075] Carboxyl groups on the surface of CNTs were modified into chloroacyl groups by subj...

preparation example 2

[0080] Preparation Example 2: Preparation of Water-Based Adhesive Composition

[0081] 3 g of poly(vinyl alcohol) (PVA, saponified: about 87% to about 89%, average Mw: about 31,000 g / mol to about 50,000 g / mol) dried under vacuum at 110°C for 24 hours and 27 g of anhydrous di Methylacetamide (DMAc) was mixed in a reaction vessel, stirred and heated at 100 °C under a nitrogen atmosphere for 6 h to completely dissolve the PVA in DMAc. Then, the temperature of the reaction vessel was lowered to room temperature, and 0.2 g of calcium hydride (CaH 2 ) into a reaction vessel, stirred for 24 hours to remove the remaining moisture, and filtered to obtain a solution. 18 g of the solution and 0.2 g of material B were placed in a reaction vessel, sonicated for 10 minutes, then stirred for 1 hour. Then, 0.1 ml of purified triethylamine was injected into the reaction vessel with a syringe, and then the temperature of the reaction vessel was raised to 60° C. and the reaction vessel was s...

preparation example 3

[0085] Preparation Example 3: Preparation of Water-Based Adhesive Composition

[0086] 0.9 g of poly(acrylic acid) (PAA, average Mw: about 450,000 g / mol) dried in vacuum at 110°C for 24 hours and 19 g of pure water were mixed in a reaction vessel, stirred and heated at 60°C for 6 hours to make PAA Completely soluble in pure water. Then, the temperature of the reaction vessel was lowered to room temperature, 0.1 g of raw material C was put into the reaction vessel, treated with ultrasonic waves for 10 minutes, and then stirred for 24 hours to prepare an aqueous binder composition (solution F), in which CNTs are ionically linked to PAA. Here, the chemical structure of the binder contained in Solution F has a repeating unit shown in General Formula 2 below.

[0087] Formula 2

[0088]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

A binder for an electrode of a lithium battery, and a lithium battery containing the binder. The binder includes: a carbon nanotube; and a polymer chemically bonded to the carbon nanotube, and thus a conducting path may be formed by improving dispersion of the carbon nanotube. Accordingly, the lithium battery may have high capacity and the life of the lithium battery can be improved.

Description

technical field [0001] One or more embodiments relate to a binder for a lithium battery electrode and a lithium battery including the same. Background technique [0002] Lithium secondary batteries used in portable electronic devices for information communication (such as personal digital assistants (PDAs), mobile phones, and notebook computers), electric bicycles, and electric vehicles have at least twice the discharge voltage compared with other batteries, so Can exhibit high energy density. [0003] The lithium secondary battery includes an organic electrolyte or a polymer electrolyte filled between a positive electrode and a negative electrode, the positive electrode and the negative electrode contain active materials capable of intercalating and deintercalating lithium ions, and the lithium secondary battery Electricity is generated through redox reactions during intercalation / deintercalation. [0004] The positive active material of the lithium secondary battery can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/62H01M10/0525H01M10/058C09J129/04C09J133/02C09J179/08C09J163/00
CPCY02E60/10Y02P70/50
Inventor 李范旭郑惠先李惠兰
Owner SAMSUNG SDI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap