High-temperature-resistant hot melt adhesive membrane for aluminum honeycomb boards, and preparation method thereof

A hot-melt adhesive film and aluminum honeycomb technology, applied in the direction of adhesives, adhesive types, grafted polymer adhesives, etc., can solve problems such as safety accidents, structural damage of aluminum honeycomb panels, etc., to improve wettability, adhesion Fast connection speed and good heat resistance

Active Publication Date: 2013-07-17
JIANGSU LUSHAN PHOTOVOLTAIC TECH +1
View PDF4 Cites 52 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main components of the current hot-melt adhesives used for the bonding and compounding of aluminum honeycomb panels are polar group-modified polyethylene and polyethylene-vinyl acetate. The melting point of such materials is generally not higher than 130°C, which limits aluminum Honeycomb panels can only be used in low temperature environments
Otherwise, the melting of the hot melt adhesive layer will damage the aluminum honeycomb panel structure and even cause safety accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the high-temperature-resistant hot-melt adhesive film for bonding aluminum honeycomb panels described in this example: 50% of polyester elastomer with a melting point of 203°C (product source: DuPont Company of the United States, product model: Hytrel 5555HS), 20% maleic anhydride grafted polyethylene-vinyl acetate copolymer (product source: Guangzhou Lushan New Material Co., Ltd., product model: OV-1), 19% polyethylene-vinyl acetate copolymer (product source : Taiwan Plastics Industry Co., Ltd., product model: 7320M), 10% hydrogenated pentaerythritol rosin ester, 1% antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) Propionic acid] pentaerythritol ester) was mixed with a high-speed mixer, extruded and granulated with an extruder at 210 °C. Cast at 210° C. to obtain a hot melt adhesive film with a thickness of 0.4 mm.

Embodiment 2

[0033] The preparation method of the high-temperature-resistant hot-melt adhesive film for bonding aluminum honeycomb panels described in this example: 40% polyester elastomer with a melting point of 190°C (product source: Korea LG Chemical Company, product model: KEYFLEX 1047D) , 10% polyethylene-methyl acrylate-maleic anhydride copolymer (source: Arkema, France, product model: LOTADER 4503), 25% polyethylene-methyl acrylate copolymer (source: DuPont, USA Company, product model: Elvaloy AC 1820), 24% polymer rosin glyceride, 1% antioxidant 1076 (β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid deca Octaester) was mixed with a high-speed mixer, extruded and granulated with an extruder at 205°C, and cast at 210°C to obtain a 0.4mm thick hot melt adhesive film.

Embodiment 3

[0035] The preparation method of the high-temperature-resistant hot-melt adhesive film for bonding aluminum honeycomb panels described in this example: 35% polyester elastomer with a melting point of 202.4°C (product source: Sichuan Chenguang Kexin Plastic Co., Ltd., product model : SUNPRENE TPEE H7560Y), 25% polyethylene-butyl acrylate-maleic anhydride copolymer (source: Arkema, France, product model: LOTADER 3210), 22% terpene phenolic resin, 15% talc Powder and 1.5% silane coupling agent KH550 blend, 1.5% antioxidant B215, mixed with a high-speed mixer, extruded at 210°C with an extruder to granulate, and cast at 210°C to obtain a thickness of 0.4mm hot melt adhesive film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant hot melt adhesive membrane for aluminum honeycomb boards, and a preparation method thereof. The high-temperature-resistant hot melt adhesive membrane for aluminum honeycomb boards is made from, by weight percent, 30-50% of polyester elastomer with above 180 DEG C of melting point, 10-40% of polyolefin copolymer modified by maleic anhydride, 0-40% of polyolefin copolymer, 10-30% of tackifying resin, 0-15% of filler, and 1-3% of functional aid. The components add up to 100%. The high-temperature-resistant hot melt adhesive membrane for aluminum honeycomb boards has the advantages of high adhesion strength, instantaneous resistance to the temperature up to 170-190 DEG C, and long-term resistance to the temperature up to 130 DEG C.

Description

[0001] technical field [0002] The invention relates to a hot-melt adhesive, in particular to a high-temperature-resistant hot-melt adhesive film for bonding aluminum honeycomb panels and a preparation method thereof, belonging to the technical field of polymer hot-melt adhesives. [0003] Background technique [0004] Aluminum honeycomb panel is a multi-layer composite panel composed of metal panel, aluminum honeycomb core, metal bottom plate and polymer adhesive. It has the advantages of light weight, high specific strength, sound insulation and heat insulation performance. Aluminum honeycomb panels can be used as floors and partition walls on trains, floors and ceilings on cars, decks on ships, and curtain walls on buildings. The use of aluminum honeycomb panels It can replace the thick metal aluminum plate to reduce the weight of the material while providing a good decorative effect. [0005] The bonding of aluminum honeycomb panels used structural adhesives such as e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J167/00C09J123/00C09J151/06C09J151/00C09J123/08C09J153/02C09J175/04
Inventor 唐舫成伍金奎汪加胜钟康刘宝玉
Owner JIANGSU LUSHAN PHOTOVOLTAIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com