Eco-friendly glaze ink for ceramic jet printing and preparation method thereof

A technology of ceramic inkjet and ceramic glaze, applied in inks, applications, household appliances, etc., can solve the problems of thickening and thixotropy, high process pollution, waste of resources, etc., and achieve good inkjet printing performance and uniform particle size distribution. , the effect of good quality stability

Active Publication Date: 2014-12-24
FOSHAN DOWSTONG TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These reports are all ceramic inks prepared based on pigments, but ceramic inks prepared based on ceramic glazes, especially environmentally friendly water-based glaze inks, are rarely reported.
For glazes, its preparation does not need to be fired between 900-1400°C like pigments. It contains a large amount of plastic material, which makes it easy to cause great thickening and thixotropy after ultra-fine, especially in the water phase. Phenomenon, making it difficult to realize the preparation of low viscosity and high solid content water-based glaze ink
[0004] The construction technology of ceramic glazes is usually through glaze spraying, spraying glaze, screen printing or roller printing, etc. These processes have high pollution, low efficiency, and waste resources to a large extent. It is to decorate the concave and convex surface of ceramics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Eco-friendly glaze ink for ceramic jet printing and preparation method thereof
  • Eco-friendly glaze ink for ceramic jet printing and preparation method thereof
  • Eco-friendly glaze ink for ceramic jet printing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of the above-mentioned environment-friendly ceramic ink-jet printing glaze ink comprises the following steps:

[0037] 1) Prepare water-based dispersion: add resin to the mixed solvent of ethylene glycol, propylene glycol and water, stir to dissolve, add dispersant, water reducer and defoamer respectively, and stir evenly;

[0038] 2) Prepare the glaze slurry, add the glaze into the aqueous dispersion, pre-disperse with a high-speed disperser to fully wet the glaze, and then transfer it to a sand mill for grinding, and control the average particle size of the glaze particles at 200 ~400 nm, the maximum particle size is less than 1 μm, to obtain glaze slurry;

[0039]3) Add leveling agent, pH regulator, viscosity regulator, preservative and remaining solvent to the glaze slurry, stir evenly, and filter with a 1 μm filter membrane to obtain glaze ink for ceramic inkjet printing.

[0040] The method of using the glaze ink of the present invention: i...

Embodiment 5

[0049] The composition of the glaze material used in embodiment 5 is: SiO 2 50 parts, Al 2 o 3 26 copies, K 2 O 0.2 parts, Na 2 O 2.0 parts, CaO 1.0 parts, MgO 0.2 parts, Fe 2 o 3 0.1 parts, TiO 2 0.2 parts, ZnO 3 parts, by mass parts.

Embodiment 6

[0050] The composition of the glaze material used in embodiment 6 is: SiO 2 65 parts, Al 2 o 3 20 copies, K 2 O 1.0 parts, Na 2 O 4.0 parts, CaO 0.2 parts, MgO 0.02 parts, Fe 2 o 3 0.3 parts, TiO 2 0.05 parts, ZnO 1.0 parts, by mass parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
surface tensionaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention discloses an eco-friendly glaze ink for ceramic jet printing and preparation method thereof, the ink comprises, based on the mass percentage, 30-50% of ceramic glaze, 15-25% of organic solvent, 4-10% of dispersant, 2-5% of water reducing agent, 2-5% of resin, 0.3-0.6% of defoaming agent, 0.1-0.2% of leveling agent, 0.1-0.2% of pH modulators, 2-5% of viscosity regulator, 0.1-0.3% of preservative and the balance for water. The eco-friendly glaze ink for ceramic jet printing provided by the invention has good stability for long-term storage and good performance for ink-jet printing, with low ink viscosity and uniform distribution of particle diameter, wherein the regulable viscosity is between 10 and 40.0mPa.s, and the surface tension is between 32 and 40mN / m, and the pH value is between 7.5 and 8.5, and the average particle diameter is between 200 and 400nm, and the maximum particle diameter is less than 1 Mum.

Description

technical field [0001] The invention belongs to the technical field of ceramic inkjet, and in particular relates to an environment-friendly glaze ink for ceramic inkjet printing and a preparation method thereof. Background technique [0002] Ceramic inkjet technology is a non-contact digital printing technology. It is ink made of ceramic color glaze powder, and small ink droplets are sprayed from a nozzle with a diameter of tens of microns onto the surface of architectural ceramics, and fired. The decorative technique of post-color rendering, the shape and geometric size of the decorative pattern are controlled by the computer. Compared with the traditional decoration method of ceramic tiles, ceramic inkjet technology has the advantages of low energy consumption, low pollution, high efficiency, especially the ability to decorate concave and convex surfaces, so ceramic inkjet technology has become a mainstream technology. [0003] Chinese invention patent application numbers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/30
Inventor 张翼余水林陈奕
Owner FOSHAN DOWSTONG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap