Permeable water plugging modified phenolic resin injecting paste material for underground coal mine and preparation method

A technology of phenolic resin and grouting materials, applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve problems such as not fundamentally solving water leakage, unable to withstand long-term water pressure, and unsatisfactory water blocking effect, etc. Achieve the effect of simple construction, high pressure and fast curing time

Inactive Publication Date: 2013-10-02
HUAIBEI WANYUAN IND TRADE
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Guidance and drainage cannot fundamentally solve the water leakage situation, and the existing grouting method is mainly to use polyurethane to drill holes in the leakage area and use the characteristics of rapid solidification of polyurethane to seal the coal and rock cracks to achieve water effect
[0004] However, during the polymerization process of polyurethane materi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example one:

[0024] A component preparation

[0025] Put 30 parts of phenol, 60 parts of formaldehyde, and 4 parts of barium hydroxide into the reactor and heat to 40 parts. 0 C stops heating and automatically rises to 70 0 C keep warm, take samples and test every 30 minutes, when the emulsification point reaches 25-35ml, add 1 part of oxalic acid for neutralization, when the pH is 7-8, add 5 parts of urea for dehydration, take samples every 30 minutes for testing, when the viscosity is 40 —80 mpa﹒ s (25 0 C) When, re-sampling and testing, qualified discharge sealed packaging;

[0026] B component preparation

[0027] Put 40 parts of phenol sulfonic acid, 40 parts of phosphoric acid, and 20 parts of p-toluene sulfonic acid into the mixing tank for stirring. After 30 minutes, samples are taken for testing, and the materials are sealed and packaged after passing the test.

[0028] The inspection product indicators are as follows:

[0029] Viscosity 25 0 C A component 60 mpa﹒ s ...

Example Embodiment

[0038] Embodiment two:

[0039] A component preparation

[0040] Put 65 parts of formaldehyde, 25 parts of phenol and 5 parts of barium hydroxide into the reaction kettle, and heat to the material temperature of 40 0 C, stop heating, automatically rise to 65 0 Keep the temperature at C and take samples every 30 minutes for testing. When the emulsification point reaches between 35-40ml, add 1.2 parts of oxalic acid for neutralization. When the PH value reaches 7-8, add 3.8 parts of urea and then dehydrate. Take samples every 30 minutes for testing. When the viscosity is 40-80 mpa. s (25 0 C), take samples for testing, discharge the materials and seal the package after passing the test;

[0041] B component preparation

[0042] Put 60 parts of phenol sulfonic acid, 20 parts of phosphoric acid, and 20 parts of p-toluene sulfonic acid into the mixing tank for stirring. After 30 minutes, samples will be taken for testing, and the materials will be sealed and packaged after passing the tes...

Example Embodiment

[0052] Example three

[0053] A component preparation

[0054] Put 64 parts of formaldehyde, 22 parts of phenol, and 6 parts of barium hydroxide into the reactor and heat to the material temperature of 40 0 C, stop heating, automatically rise to 65 0 Keep the temperature at C and take samples every 30 minutes for testing. When the emulsification point reaches 35-40ml, add 1.5 parts of oxalic acid for neutralization, when the PH value reaches 7-8, add 6.5 parts of urea for dehydration, take samples every 30 minutes for testing, when the viscosity is 40-80 mpa. s (25 0 C), take another sample for testing, and seal the package after passing the test;

[0055] B component preparation

[0056] Put 80 parts of phenol sulfonic acid, 10 parts of phosphoric acid, and 10 parts of p-toluene sulfonic acid into the mixing tank for stirring. After 30 minutes, samples will be taken for testing, and the materials will be sealed and packaged after being qualified.

[0057] The inspection product indic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a permeable water plugging modified phenolic resin injecting paste material for an underground coal mine and a preparation method and aims to solve the problem that a water plugging effect is not ideal by adopting a traditional material. The preparation method is characterized by comprising the following steps of preparing a component A from phenol, formaldehyde, barium hydroxide, oxalic acid and urea, preparing a component B from phenolsulfonic acid, phosphoric acid and para-toluenesulfonic acid, and then, mixing the component A and the component B in weight ratio of 1:1. The material disclosed by the invention is low in viscosity and high in liquidity and is capable of completely plugging ultra-thin cracks, is high in curing time which is adjustable on site within a range of 5-60 seconds; a polymer cannot be pulverized, is stable when meeting water and is capable of permanently plugging the cracks. The material reaches a fire-retardant level and is environmentally friendly; production raw materials are completely domesticated and are pollution-free; the construction is simple; the operation is simple and easy to implement; the environment cannot be polluted during a production process, and the health of workers is not influenced.

Description

technical field [0001] The invention relates to a seepage and water blocking material for underground coal mines, in particular to a modified phenolic resin grouting material. Background technique [0002] In the process of coal mining, due to geological changes, the coal rock formations are fractured and broken, and rich formation water flows into the roadway through the broken cracks, which not only brings inconvenience to safe production, but also increases with the long-term erosion of the water flow. Large, it may also cause roof fall, collapse, etc., which will affect the lives of miners. [0003] Coal mines mainly adopt the methods of guiding, pumping and injecting chemical slurry to control the underground water. Guidance and drainage cannot fundamentally solve the water leakage situation, and the existing grouting method is mainly to use polyurethane to drill holes in the leakage area and use the characteristics of rapid solidification of polyurethane to seal the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K8/44C08G14/08
Inventor 赵军冯万良张子光刘谦
Owner HUAIBEI WANYUAN IND TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap