A kind of microencapsulated polyester aromatic masterbatch and its manufacturing method

A manufacturing method and microencapsulation technology, applied in the direction of one-component polyester rayon, etc., can solve the problems of poor uniformity, poor washability, and unsatisfactory performance, and achieve stable performance and good compatibility. Effect

Active Publication Date: 2017-09-12
JIANGSU ZJA NEW MATERIAL
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the aromatic chemical fiber obtained by this method is made into a fabric, the uniformity is poor, and it is not washable, which is not satisfactory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The present invention will be further described below in conjunction with embodiment;

[0027] It should be understood that the scope of the present invention is not limited to the following examples, and all formal modifications, equivalent replacements and changes made to the present invention shall be included within the protection scope of the present invention.

[0028] Microencapsulated polyester aromatic masterbatch and manufacturing method thereof, the processing steps are as follows:

[0029] a. Take 10 parts of polyurethane prepolymer and prepare a 20-30% solution with acetone;

[0030] b. Add 2 parts of essence, stir and dissolve to obtain a mixed solution;

[0031] C, 3 parts of polyethylene glycols are mixed with deionized water to a concentration of 20%;

[0032] d, the solutions obtained in the above step b and step c are mixed and emulsified by a homogenizer;

[0033] e. Add 0.2 parts of superfine calcium phosphate, stir evenly and react at a temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of microencapsulated polyester fragrant masterbatch, and belongs to the field of functional textile production. The method comprises the following steps: dissolving essences into an organic solution containing a polyurethane prepolymer, and mixing with a water solution containing a polyethylene glycol emulsifier; adding proper superfine sodium phosphate, then carrying out full emulsification and reaction in a homogenizer, filtering and washing after the reaction is ended, and drying and crushing a filter cake to obtain the fine powder containing the essences; and fully mixing the obtained fine powder with low-melting point polyester powder and a dispersing agent by a high-speed mixer, and then feeding the mixture into a double screw extruder to extrude, water-cool and chop, so as to obtain the microencapsulated polyester fragrant masterbatch. The microencapsulated polyester fragrant masterbatch prepared by the method is stable in performance, and good in compatibility with a spinning material by a spinning test; the physical indexes of produced polyester fragrant fiber achieve the design effect; and the requirements of the majority of users are met.

Description

technical field [0001] The invention relates to a microencapsulated polyester aromatic masterbatch and a manufacturing method thereof, belonging to the field of functional textile production. Background technique [0002] Due to the development of science and technology and the improvement of people's living standards, people's pursuit of a better life is no longer limited to food and clothing. The requirements for functional textiles are getting higher and higher. Textiles that can continuously emit bursts of fragrance are also favored by people. of favor. [0003] The aromatic masterbatches in the prior art are prepared from polypropylene with a low melting point. Due to the poor compatibility of polyester and polypropylene when spinning aromatic polyester fibers, the mechanical properties of the fibers are affected to a certain extent. [0004] For the preparation of aromatic chemical fibers, the Chinese patent CN102618960A adopts the process of post-processing the fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/00C08L75/04C08L71/08C08K3/32D01F6/92D01F1/10
Inventor 周焕民
Owner JIANGSU ZJA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com