Brick made of rubbish and manufacturing method thereof

A garbage brick and garbage technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problem of high manufacturing cost and achieve the effect of reducing manufacturing cost

Active Publication Date: 2013-11-20
张玉 +3
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the existing technical problem of high manufacturing cost of making bricks from garbage, and provides a new brick made from garbage and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] 1. A material formula for paving bricks made of garbage concrete and garbage plastics is as follows:

[0059] (1) Surface material

[0060] Fine stone particles with a maximum dimension of 0.8mm: 63.50kg;

[0061] Lightly burned magnesium powder with the largest dimension not exceeding 20 microns: 21.68kg;

[0062] Blending agent: 7.38kg each of halogen flakes and ferrous sulfate;

[0063] (2) Base material

[0064] Garbage concrete particles with a maximum dimension of 2mm: 170.10kg;

[0065] Garbage plastics with a maximum external dimension of 50mm: 207.90kg;

[0066] 2. The steps of making paving bricks with the above raw materials are as follows:

[0067] (1) prepare surface material, comprise the following steps:

[0068] ①Add 7.38kg of halogen flakes and ferrous sulfate to 15.66kg of water to make 30.42kg of blending agent solution;

[0069] ②Put 63.50kg of fine stone particles with a maximum external dimension of 0.8mm and 21.68kg of lightly burned magnes...

Embodiment 2

[0081] 1. A road cliff stone made of waste bricks and waste plastics. The material formula used is as follows:

[0082] (1) Surface material

[0083] Sand particles with a maximum external dimension of 1.2mm: 52.00kg;

[0084] Lightly burned magnesium powder with the largest dimension not exceeding 20 microns: 18.00kg;

[0085] Blending agent: 6.00kg each of halogen flakes and ferrous sulfate;

[0086] Nano powder: 18.00kg of 1nm silicon dioxide;

[0087] (2) Base material

[0088] Waste brick particles with a maximum dimension of 2.0 mm: 170.10 kg;

[0089] Garbage plastics with a maximum external dimension of 60mm: 207.90kg;

[0090] 2. The steps to make road cliff stones with the above raw materials are as follows:

[0091] (1) prepare surface material, comprise the following steps:

[0092] ①Add 6kg of halogen flakes and ferrous sulfate to 15.60kg of water to make 27.60kg of blending agent solution;

[0093] ②Put 52.00kg of sand particles with a maximum external di...

Embodiment 3

[0105] 1. A kind of used material formula of the lawn brick that sand and rubbish plastics are made are as follows:

[0106] (1) Surface material

[0107] Sand particles with a maximum external dimension of 1.0mm: 70.00kg;

[0108] Lightly burned magnesium powder with the largest dimension not exceeding 20 microns: 16.00kg;

[0109] Blending agent: 12.00kg of halogen chips;

[0110] Nano powder: 0.50kg of 50nm calcium carbonate;

[0111] Modifier: 0.10kg each of phosphoric acid, ferrous sulfate, copper sulfate, magnesium sulfate and urea-formaldehyde resin, 0.25kg each of ethyl silicate, sodium lignosulfonate, polyvinyl butyral and sodium melamine formaldehyde resin sulfonate;

[0112] (2) Base material

[0113] Sand particles with a maximum external dimension of 0.5mm: 170.10kg;

[0114] Garbage plastics with a maximum external dimension of 55 mm: 207.90 kg;

[0115] 2. The steps of making lawn bricks with the above raw materials are as follows:

[0116] (1) prepare su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a brick made of rubbish. The brick is composed of a surface layer and a base layer. The surface layer comprises fine stone particles or sand particles, caustic-burned magnesia powder and a blending agent. The base layer comprises plastic rubbish which is cured after being melted or waste plastic which is cured after being melted and sand particles. The invention further discloses a method for manufacturing the brick by the rubbish. The manufacturing method comprises the following steps that: in the preparation process of a base layer material, the sand particles are firstly added into a stirring kettle for one time, and stirred while being heated, so that moisture in the sand particles is easily evaporated and discharged out from the top of the stirring kettle; when the temperature inside the stirring kettle is 95-105 DEG C, the plastic rubbish or the waste plastic is successively added into the stirring kettle, the successively added plastic rubbish or waste plastic is successively melted and successively mixed with the sand particles so that the plastic rubbish or waste plastic can be uniformly mixed with the sand particles; and when the temperature inside the stirring kettle is 135-145 DEG C, the plastic rubbish or waste plastic is completely melted and completely and uniformly mixed with the sand particles to form the base layer material, wherein no bubbles are formed in the base layer material.

Description

(1) Technical field [0001] The invention belongs to waste utilization, and in particular relates to a brick made from waste and a manufacturing method thereof. (2) Background technology [0002] Publication No. is CN1219518A Chinese invention patent application discloses - a kind of brick made of rubbish and its manufacturing process. This kind of brick is made of garbage, lightly burned magnesia, blending agent and modifier. The manufacturing process is to dissolve the blending agent with water first to prepare a blending agent solution, then add the modifier and light-burned magnesium into the blending agent solution, stir evenly, and make a binder, and finally make the binder and crush it into a certain size The garbage is fully stirred and mixed, and the mixed materials are transported to the construction site for paving the roadbed; or the mixed materials are injected into the mold to form, and the finished product is made after curing. Using this manufacturing proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B30/00C04B18/30
CPCY02W30/91
Inventor 张玉段冬丽吴振明徐金海
Owner 张玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More