Modified EPDM composition used in submerged pump cable rubber insulation

A technology of rubber insulation and rubber composition, applied in the directions of rubber insulators, insulated conductors, insulated cables, etc., can solve the problems of poor electrical performance and poor oil resistance, and achieve the effects of easy cross-linking, improved mechanical strength, and high electrical performance.

Inactive Publication Date: 2014-01-15
SHANGHAI QIFAN CABLE CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional EPDM rubber insulation has the problem of contradictory oil resistance and electrical properties. The traditional EPDM formula has excellent electrical properties but poor oil resistance. If the oil resistance of EPDM rubber is simply improved, it will The electrical performance is poor and cannot meet the standard requirements, and the EPDM insulation produced by the traditional f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] 100 parts of ethylene propylene rubber and 15 parts of polyethylene powder are banned. And put in nano-scale zinc oxide, stearic acid, anti-hydrophobic agent red lead powder (coating grade), paraffin oil 2280, alkane coupling agent A-172, silane modified calcined clay, and peroxide vulcanizing agent for mixing. After mixing, move the mixed rubber to an open mill for reprocessing. After the rubber is smelted, it is filtered. After filtering the glue, move to the forming machine for rolling and slicing.

Example Embodiment

[0033] Example 2

[0034] Mix 100 parts of ethylene propylene rubber with 11 parts of polyethylene powder, and put in nano-scale zinc oxide, stearic acid, red lead powder (coating grade), paraffin oil 2280, and alkane coupling agent A-172. , Silane modified calcined clay, peroxide vulcanizing agent for mixing. After mixing, move the mixed rubber to the open mill for reprocessing. After the rubber is smelted, it is filtered. After filtering the glue, move to the forming machine for rolling and slicing.

Example Embodiment

[0035] Example 3

[0036] Mix 100 parts of ethylene propylene rubber with 10 parts of polyethylene powder, and put in nano-scale zinc oxide, stearic acid, red lead powder (coating grade), paraffin oil 2280, and alkane coupling agent A-172. , Silane modified calcined clay, peroxide vulcanizing agent for mixing. After mixing, move the mixed rubber to the open mill for reprocessing. After the rubber is smelted, it is filtered. After filtering the glue, move to the forming machine for rolling and slicing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a rubber composition, and especially relates to an ethylene-propylene rubber composition used in submerged pump cable rubber insulation. The composition is characterized by comprising, by weight, 100 parts of EPDM, 10-15 parts of polyethylene powder, 5-10 parts of nano-scale zinc oxide, 1-2 parts of stearic acid, 1-1.5 parts of water repellent red lead powder (paint grade), 10-18 parts of paraffin oil 2280, 1.5-2 parts of a silane coupling agent A-172, 100-120 parts of silane-modified calcined clay, and 3.5-4 parts of a peroxide vulcanizing agent. EPDM and polyethylene powder in the above proportion are subjected to open milling; the other materials are added, and the mixture is subjected to mixing and open milling; and gstraining, tabletting, and slicing are carried out, such that the EPDM composition is obtained. With the EPDM composition, various performance requirements of export submerged pump cable can be completely satisfied.

Description

technical field [0001] The invention relates to a rubber composition, in particular to an ethylene-propylene rubber composition used for rubber insulation of cables of submersible oil pumps. Background technique [0002] Traditional EPDM rubber insulation has the problem of contradictory oil resistance and electrical properties. The traditional EPDM formula has excellent electrical properties but poor oil resistance. If the oil resistance of EPDM rubber is simply improved, it will As a result, the electrical performance is poor and cannot meet the standard requirements, and the EPDM insulation produced by the traditional formula is generally used on the cables of submersible pumps at 150°C and below. The submersible pump cable requires that the insulation not only have high flexibility but also have excellent electrical properties, oil resistance and high temperature resistance. Therefore, the electrical insulation performance and oil resistance of EPDM rubber become a contr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L23/06C08L91/06C08K13/06C08K9/06C08K3/34C08K3/22C08K5/09H01B3/44H01B7/28
CPCC08L23/16C08L2201/08C08L2203/202C08L2205/03C08L2207/32H01B3/28C08L23/06C08L91/06C08K13/06C08K9/06C08K3/346C08K2003/2296C08K5/09
Inventor 王国福陈志远高文起高俊威丁永国孙学鹏
Owner SHANGHAI QIFAN CABLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap