A kind of far-infrared bamboo charcoal viscose fiber and preparation method thereof

A bamboo charcoal viscose and far-infrared technology, applied in the field of viscose in the textile industry, can solve the problems of poor spinnability of viscose fiber, achieve good heat storage and moisturizing effects, promote blood circulation, and reduce loss

Active Publication Date: 2015-10-28
YIBIN HIEST FIBER +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention provides a kind of far-infrared bamboo charcoal viscose fiber and its preparation method in order to make up for the blank of the current far-infrared bamboo charcoal viscose fiber, adapt to the needs of customers in the product market, and solve the problem of poor spinnability of the current viscose fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of far-infrared bamboo charcoal viscose fiber, the far-infrared bamboo charcoal solution is mixed with viscose by injection before spinning, and the finished product is obtained through wet spinning and post-treatment. The far-infrared bamboo charcoal solution is composed of zinc and aluminum far-infrared Infrared masterbatch mixed with bamboo charcoal solution, by weight, the content of zinc and aluminum in the fiber is 0.01%, the content of bamboo charcoal is 0.1%, the ammonia absorption rate is ≥50%, the air permeability is ≥500mm / s, and the color fastness to washing is grade 4.

Embodiment 2

[0047] A bamboo charcoal viscose filament with far-infrared, the far-infrared bamboo charcoal solution is mixed with viscose by injection before spinning, and the finished product is obtained through wet spinning and post-treatment. The far-infrared bamboo charcoal solution is composed of zinc and aluminum Far-infrared masterbatch and bamboo charcoal solution are mixed. By weight, the content of zinc and aluminum in the fiber is 1%, the content of bamboo charcoal is 2%, the ammonia absorption rate is ≥50%, the air permeability is ≥500mm / s, and the color fastness to washing is 4 grades. . Dry strength 2.0cN / dtex, dry elongation 16%, dry elongation variation ≤ 8%.

Embodiment 3

[0049] A bamboo charcoal viscose filament with far-infrared, the far-infrared bamboo charcoal solution is mixed with viscose by injection before spinning, and the finished product is obtained through wet spinning and post-treatment. The far-infrared bamboo charcoal solution is composed of zinc and aluminum It is made by mixing far-infrared masterbatch and bamboo charcoal solution. By weight, the content of zinc and aluminum in the fiber is 0.8%, the content of bamboo charcoal is 3%, the ammonia absorption rate is ≥50%, the air permeability is ≥500mm / s, and the color fastness to washing is grade 5. . The dry strength is 2.7cN / dtex, the dry elongation is 22%, and the dry elongation variation is ≤8%.

[0050] The ingredients of the far-infrared ceramic powder include: 10% magnesium oxide, 45% calcium oxide, 7% zirconium oxide, 10% silicon oxide, and 5% germanium.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

In order to make up for the blank of the current far -infrared bamboo charcoal sticky glue fiber and solve the problem of poor texture of bamboo charcoal sticky fiber, it provides a method of far -infrared bamboo charcoal sticky fiber and its preparation method.It is characterized by: according to the weight meter, the content of far -infrared ceramic powder in the fiber is 1 ~ 10%, the content of bamboo charcoal is 0.1 ~ 10%, the far -infrared emission rate is> 80%, the ammonia absorption rate is ≥50%, the breathability is ≥500mm / s, the water -resistant washing resistance is resistant to water washingSection 4 ~ 5.The far -infrared vibraous glue fiber of the invention not only has the effect of insulation, but also the radiation far -infrared rays also have a health care function of activating cell tissue and promoting blood circulation.

Description

technical field [0001] The invention relates to the technical field of viscose in the textile industry, in particular to a far-infrared bamboo charcoal viscose fiber and a preparation method thereof. Background technique [0002] Bamboo charcoal is mainly composed of carbon, hydrogen, oxygen and other elements. It is hard, fine and porous, and has strong adsorption capacity. Excellent deodorizing, antiseptic, and odor-absorbing functions. Nano-scale bamboo charcoal powder also has good antibacterial and bactericidal effects, can absorb and neutralize the acidic substances contained in sweat, and achieve the effect of whitening the skin. Not only that, bamboo charcoal is also a very good emission material for far infrared and negative ions. Bamboo-charcoal blended health-care fiber can emit negative ions without damaging equipment during processing, which overcomes the serious disadvantage of grinding needles when processing fabrics with negative ion fibers, and is deeply w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F2/08D01D13/00D01D5/06
Inventor 邓传东贺敏范贤珍陈明付陈晓芳
Owner YIBIN HIEST FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com