Nature fiber reinforced thermoplastic resin unidirectional prepreg tape and preparation method thereof

A thermoplastic resin, unidirectional prepreg tape technology, applied in the field of composite material production and preparation, can solve the problems of screw wear, limited reinforcement effect, small fiber length and diameter of natural fiber reinforced materials, etc., to ensure performance stability, porosity, etc. low effect

Active Publication Date: 2014-02-12
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF8 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The natural fiber reinforced material prepared by this method has a relatively small fiber length and diamet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nature fiber reinforced thermoplastic resin unidirectional prepreg tape and preparation method thereof
  • Nature fiber reinforced thermoplastic resin unidirectional prepreg tape and preparation method thereof
  • Nature fiber reinforced thermoplastic resin unidirectional prepreg tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] (1) Weigh 30 parts of jute fiber, 70 parts of polypropylene fiber (polypropylene fiber), 0.5 parts of emulsion (wherein the content of mineral oil is 20%, the content of milk soap is 0.9%, and the content of water is 79.1%), and Coupling agent vinyltrimethoxysilane 0.5 part; Utilize conveyor belt 1 to transport jute raw hemp (that is: natural fiber raw material) 2 into the opening machine 3 for opening ( figure 1 ), during the opening process, after adding emulsion and vinyltrimethoxysilane to open, store for 3 days;

[0065] (2) Evenly spread the stocked jute and polypropylene segment fibers (that is, the natural fibers after opening) 4, and send them to the first carding machine 5 to form a roll; then put the roll into the second carding machine 6 In the second carding, a jute fiber / polypropylene fiber mixed roll with a width of about 20mm is formed ( figure 2 );

[0066] (3) Put the jute fiber / polypropylene fiber mixed roll into the heating oven 7 for heating, and...

Embodiment 2

[0069] (1) Weigh 60 parts of hemp fiber and 40 parts of polylactic acid fiber. The hemp fiber selected here is in the form of commercially available strips, which are directly mixed with polylactic acid;

[0070] (2) Spread the hemp fiber and the polylactic acid fiber evenly, and send them into the first carding machine 5 to form a roll; then put the roll into the second carding machine 6 for secondary carding to form a width of 30mm left and right hemp / polylactic acid mixed rolls;

[0071] (3) Put the hemp fiber / polylactic acid fiber mixed roll into the heating oven 7 for heating, and the heating temperature is 185°C;

[0072] (4) Then use the pressure roller 8 to roll the heated hemp fiber / polylactic acid fiber unidirectional prepreg tape, roll it once, the pressure is 8MPa, and then roll the rolled jute fiber / polypropylene fiber unidirectional The prepreg tape is wound up by a winder 9 . Obtain hemp fiber / polylactic acid fiber unidirectional prepreg tape. Its performance...

Embodiment 3

[0074] (1) Weigh 50 parts of ramie fiber and 50 parts of spandex fiber (polyurethane); the ramie fiber selected here is commercially available strips, which are directly mixed with spandex fiber;

[0075] (2) if figure 2 The ramie fiber and spandex fiber of alkali treatment are paved evenly as shown, and wherein ramie fiber is 50 parts, and spandex fiber is 50 parts, is sent in the head road carding machine 5, becomes roll; Then roll is put into secondary carding machine 6 During the second carding, because in the carding process, the fiber of ramie is relatively fine, and the dispersion is uneven, so the ramie fiber / spandex fiber roll needs to be carded three times;

[0076] (3) Put the ramie fiber / spandex fiber mixed roll into the heating oven 7 for heating, and the heating temperature is 210°C;

[0077] (4) Then use the pressure roller 8 to roll the heated ramie fiber / spandex fiber unidirectional prepreg tape, roll it twice, and the pressure is 2MPa, and then roll the rol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Widthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of composite material production and preparation, and relates to a fiber reinforced thermoplastic resin unidirectional prepreg tape and a preparation method thereof. The prepreg tape is prepared from the following components, by weight: 30-70 parts of a thermoplastic resin, 30-70 parts of nature fibers, 0-1 part of a coupling agent, and 0-1 part of an emulsion. Compared with the prepreg tape in the prior art, the prepared nature fiber/thermoplastic resin unidirectional prepreg tape of the present invention has the following advantages and beneficial effects that: mechanical strength is high, the prepreg tape can be stored for a long time, the nature fibers are completely impregnated by the resin and are not exposed to the outside so as to maintain the dry state of the material, particularly the nature fibers, the nature fibers are not easily subjected to mildew deterioration, and the porosity is low so as to ensure performance stability of the product. With the method, the width of the reinforcing material and the nature fibers can be limited so as not to cause nature fiber deviation phenomenon during the subsequent production process.

Description

technical field [0001] The invention belongs to the field of production and preparation of composite materials, and relates to a fiber-reinforced thermoplastic resin unidirectional prepreg tape and a preparation method thereof. Background technique [0002] Continuous fiber reinforced thermoplastic resin composite unidirectional prepreg tape has excellent mechanical properties, such as high tensile strength, flexural strength / modulus, high and low temperature impact strength, etc., and has the characteristics of relatively low density and recyclability , so it has developed rapidly in recent years, and the corresponding preparation technology has also made major breakthroughs. [0003] In Chinese patent CN200610070280, Fang Kun uses the method of mixed yarn to prepare continuous glass fiber reinforced PP pellets, mixes the composite mixed yarn containing glass fiber with PP resin and processing aids, heats, melts and blends, and extrudes through an extruder Granulate. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L67/04C08L67/02C08L75/04C08L97/02C08L89/00C08K5/098C08K5/01
CPCB29C70/504C08L1/02C08L23/06C08L23/12C08L75/04C08L2205/03C08L2205/035C08L2205/16C08L97/005C08K5/098C08L67/04C08L67/02
Inventor 刘密密
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap