Catalyst for synthesizing isopropyl trifluoroacetate by esterification and preparation method thereof

A technology of isopropyl acetate and neodymium trifluoroacetate is applied in the field of catalysts for esterification to synthesize isopropyl trifluoroacetate, and can solve the problems of increased reactant limitation, toxicity of hydrofluoric acid, high corrosiveness, complicated product refining and the like , to achieve the effect of improving adsorption performance, high specific surface area and firm adsorption

Active Publication Date: 2014-03-05
NANTONG FINC PHARMA CHEM
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Isopropyl trifluoroacetate generally reacts with chlorine trifluoroacetate and isopropanol. Because chlorine trifluoroacetate has a high solubility in isopropyl trifluoroacetate, it is not conducive to separation, and chlorine trifluoroacetate is very toxic, which is not conducive to Environmental protection; trifluoroacetic acid and isopropanol are used to react, and hydrofluoric acid is generally used as a catalyst. Because hydrofluoric acid is very toxic and corrosive, it is not easy to operate, and the pressure on environmental protection is also great, so the process route needs to be optimized.
[0003] US4916256 provides a kind of process method that utilizes chlorine trifluoroacetate and isopropanol reaction to prepare isopropyl trifluoroacetate, but this method requires excessive chlorine trifluoroacetate, and chlorine trifluoroacetate is more expensive and toxic, so economical Not high, and there are certain restrictions on environmental protection
In addition, this patent requires that the separation of the product isopropyl trifluoroacetate be carried out at a temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1:

[0028] Carrier material: resin-based spherical activated carbon, produced by Shanxi Cuihong Technology Co., Ltd., the diameter of the ball is 0.3-1.2mm, and the specific surface area (BET) is 950-1200 (m) 2 / g), pore volume 0.6-0.75ml / g.

[0029] Preparation:

[0030] 1). Preparation of carrier:

[0031] The resin-based spherical activated carbon is transferred to a tubular electric furnace with nitrogen flow for pyrolysis, and slowly rises from room temperature to 800°C at a temperature rise rate of 80°C per hour. When the temperature is reached, the nitrogen is switched to 5L / hour flow rate hydrogen fluoride activation treatment 5 After hours, the product was cooled to room temperature. Get the carrier.

[0032] 2). Load operation

[0033] Soak the carrier in trifluoroacetic acid 1.8 times its mass for 4h, add 8% neodymium trioxide of carrier mass and 0.3% citric acid of carrier mass at the same time, react at 60℃ for 15h, finally wash with ethanol and dry , The ...

Example Embodiment

[0034] Example 2

[0035] In step 2), the amount of neodymium trioxide added was changed to 5% of the carrier mass, and the others were the same as in Example 1. The product number obtained is M-2.

Example Embodiment

[0036] Example 3

[0037] In step 2), the amount of neodymium trioxide added was changed to account for 10% of the carrier mass, and the others were the same as in Example 1. The product number obtained is M-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Diameteraaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides a catalyst for synthesizing isopropyl trifluoroacetate by esterification. The preparation method comprises the following steps: carrying out high-temperature roasting on a support resin-base spherical activated carbon with high specific area and micropore structure, activating with hydrogen fluoride to obtain a support with high specific area and mesopore structure, loading neodymium trifluoroacetate on the support by a liquid-phase sedimentation process, and meanwhile, modifying with a complexing agent. The catalyst has the advantages of very high specific area and proper pore structure, thus, has excellent adsorbability, and finally has favorable property for catalyzing the synthesis of isopropyl trifluoroacetate. The invention also provides a preparation method of the catalyst.

Description

technical field [0001] The invention relates to a catalyst, in particular to a catalyst for synthesizing isopropyl trifluoroacetate through esterification, and a preparation method thereof. Background technique [0002] Isopropyl trifluoroacetate is the basic substance of organic synthesis, and is a fine chemical intermediate, widely used in the production of drugs, the synthesis of pesticides, liquid crystals, dyes and chemical industrial products, and also widely used as organic solvents. Isopropyl trifluoroacetate generally reacts with chlorine trifluoroacetate and isopropanol. Because chlorine trifluoroacetate has a high solubility in isopropyl trifluoroacetate, it is not conducive to separation, and chlorine trifluoroacetate is very toxic, which is not conducive to Environmental protection: trifluoroacetic acid and isopropanol are used to react, and hydrofluoric acid is generally used as a catalyst. Because hydrofluoric acid is very toxic and corrosive, it is not easy t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/04
Inventor 张玲
Owner NANTONG FINC PHARMA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap