Foamed rubber sealing material and manufacturing method thereof

A technology of sealing materials and foamed rubber, which is applied in the field of foamed rubber sealing materials, can solve problems such as not being able to meet the use requirements of foamed rubber, and achieve the effects of excellent oil resistance, solvent resistance, excellent resilience, and excellent aging resistance

Active Publication Date: 2014-03-05
扬州动易运动用品有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Obviously, the existing NBR/PVC blended foam rubber cannot meet the requirement...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foamed rubber sealing material and manufacturing method thereof
  • Foamed rubber sealing material and manufacturing method thereof
  • Foamed rubber sealing material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The manufacturing steps of the foam rubber sealing material are as follows: (1) Prepare raw materials according to the following components and weight content, main material: 100 parts; reinforcing colorant carbon black N550: 6 parts; plasticizer and softener: 20 parts; dispersant WB212 Foaming agent FE-558W: 8 parts; Vulcanizing agent zinc oxide: 4 parts; Vulcanizing agent magnesium oxide: 3.5 parts; Vulcanizing agent sulfur: 0.5 parts; Active agent stearic acid: 1 part; Accelerator: 1 parts; protective agent: 3 parts; filler clay: 60 parts; the raw material composition and weight ratio of the main material are neoprene M-40: EPDM 4045: Thailand ADS-XL natural rubber = 7:1:1 ; The raw material components and weight ratio of the plasticizer softener are F-AN brown ointment: naphthenic oil KN4010=1:3; the raw material components and weight ratio of the accelerator are thiourea accelerator DETU: tetramethyl sulfide Base thiuram=1:1; The raw material components and weight ...

Embodiment 2

[0028] The manufacturing steps of the foam rubber sealing material are as follows: (1) Prepare raw materials according to the following components and weight content, main material: 100 parts; reinforcing colorant carbon black N774: 7 parts; plasticizer and softener: 30 parts; dispersant HT204 Foaming agent FE-558W: 10 parts; Vulcanizing agent zinc oxide: 4.5 parts; Vulcanizing agent magnesium oxide: 3.8 parts; Vulcanizing agent sulfur: 0.8 parts; Active agent stearic acid: 1.5 parts; Accelerator : 1.5 parts; protective agent: 4.5 parts; filler: 70 parts; the raw material composition and weight ratio of the main material are neoprene M-41: EPDM 4502: Vietnam SVR-3L natural rubber = 7: 1.5: 1.5; the raw material components and weight ratio of plasticizer and softener are F-NS brown ointment: naphthenic oil K10A=1:3; the raw material components and weight ratio of accelerator are thiourea accelerator DETU: tetrasulfide Methyl thiuram=1:1; the raw material components and weight r...

Embodiment 3

[0035] The manufacturing steps of the foam rubber sealing material are as follows: (1) Prepare raw materials according to the following components and weight content, main material: 100 parts; reinforcing colorant carbon black N880: 8 parts; plasticizer and softener: 40 parts; dispersant Deoflow A: 2 parts; foaming agent FE-558W: 12 parts; vulcanizing agent zinc oxide: 5 parts; vulcanizing agent magnesium oxide: 4 parts; vulcanizing agent sulfur: 1 part; active agent stearic acid: 2 parts; accelerator: 2 parts; protective agent: 6 parts; filler: 80 parts; the raw material components and weight ratio of the main material are neoprene B30: EPDM rubber 4506: Yunnan SCR5 natural rubber = 7:2:2; plasticized and softened The raw material components and weight ratio of the agent are 2L brown ointment:naphthenic oil K10H=1:3; the raw material components and weight ratio of the accelerator are thiourea accelerator DETU:tetramethylthiuram monosulfide=1 : 1; The raw material components a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a foamed rubber sealing material and a manufacturing method thereof. The foamed rubber sealing material is composed of 100 parts of main material, 6-8 parts of reinforcing colorant, 20-40 parts of plasticizer, 1-2 parts of dispersing agent, 8-12 parts of foaming agent, 8-10 parts of vulcanizing agent, 1-2 parts of stearic acid, 1-2 parts of accelerator, 3-6 parts of protective agent and 60-80 parts of filler. The main material CR:EPDM:NR ratio is 70:(10-20):(10-20), the plasticizer brown ointment:naphthenic oil ratio is 1:3, the accelerator DETU:TMTM ratio is 1:1, and the protective wax:anti-aging agent 445:anti-aging agent ODA ratio is 1:1:1. The manufacturing method comprises the following steps: rubber mixing, powder mixing, discharging, primary vulcanizing and foaming, secondary vulcanizing and foaming, and normal-temperature natural cooling for 10-15 days. The foamed rubber sealing material has the advantages of low density, high toughness, low thermal conductivity, water resistance, favorable aging resistance, excellent elasticity, excellent shock-absorbing capacity, excellent flame retardancy, environmental protection and no toxicity.

Description

technical field [0001] The invention relates to a foamed rubber sealing material, belonging to the technical field of foamed rubber sealing materials. The invention also relates to a manufacturing method of the foamed rubber sealing material. Background technique [0002] At present, the NBR / PVC blended foam rubber mainly used in the market has low tensile strength, tear strength and elongation. Ordinary materials with low requirements for shock absorption and sealing, but with the demand for the use of foamed rubber in the fields of automobiles, high-speed rail, and electronics, people have put forward new performance requirements for foamed rubber. [0003] Its performance index of existing NBR / PVC blend foam rubber is as follows: [0004] [0005] Obviously, the existing NBR / PVC blended foam rubber cannot meet the requirements for the use of foam rubber in the fields of automobiles, high-speed rail, and electronics. Contents of the invention [0006] The primary p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L11/00C08L23/16C08L7/00C08K13/02C08K3/04C08K3/06C08K3/22C08K5/09C08K5/01C08K5/405C08K5/40C08K5/18C08K3/34C08K3/26C08K3/38C08J9/06C08J3/24B29C35/02B29C44/08B29C44/10
Inventor 孙建波郜文卫
Owner 扬州动易运动用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap