Antistatic master batch for polyester

A technology of antistatic masterbatch and antistatic agent, applied in the field of antistatic masterbatch for polyester, can solve problems such as processing difficulties, and achieve the effects of low cost, good compatibility and high antistatic performance

Inactive Publication Date: 2014-04-09
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the melting point of most antistatic agents is lower than that of polyester, and has a strong external lubrication effect, if it is directly added during molding processing, it will cause processing difficulties, so it is better to add it to polyester in the form of antistatic masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An antistatic masterbatch for polyester, its components are proportioned by mass percentage: polyethylene terephthalate (PET) 62%, bis(2-hydroxyethyl) octylmethyl bis-p-toluene Ammonium sulfonate 30%, talc powder 1.5%, polyethylene glycol 4%, silane coupling agent 2.5%.

[0015] Preparation method: mix each component according to the weight ratio, then add it to a high-speed mixer or an ultrasonic generator and mix for 10-30 minutes, then put the mixed material into a twin-screw extruder for melting and blending, and the melting temperature is controlled at 270°C ~290°C, extruded through a twin-screw extruder, cooled, pelletized, dried, and packaged to obtain the antistatic masterbatch for polyester of the present invention.

Embodiment 2

[0017] An antistatic masterbatch for polyester, the components of which are: polyethylene terephthalate (PET) 51%, glyceryl monostearate (GMS) 40%, aluminum hydroxide 1.5%, calcium stearate 5%, titanate coupling agent 2.5%.

[0018] Preparation method: mix each component according to the weight ratio, then add it to a high-speed mixer or an ultrasonic generator and mix for 10-30 minutes, then put the mixed material into a twin-screw extruder for melting and blending, and the melting temperature is controlled at 270°C ~290°C, extruded through a twin-screw extruder, cooled, pelletized, dried, and packaged to obtain the antistatic masterbatch for polyester of the present invention.

Embodiment 3

[0020] An antistatic masterbatch for polyester, its components are proportioned by mass percentage: polyethylene terephthalate (PET) 80%, nano-scale antimony-doped tin oxide (ATO) 15%, sodium benzoate 1 %, trimethylolethane 3%, titanate coupling agent 1%.

[0021] Preparation method: mix each component according to the weight ratio, then add it to a high-speed mixer or an ultrasonic generator and mix it for 10-30 minutes, then put the mixed material into a twin-screw extruder for melting and blending, and the melting temperature is controlled at 270°C ~290°C, extruded through a twin-screw extruder, cooled, pelletized, dried, and packaged to obtain the antistatic masterbatch for polyester of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antistatic master batch for polyester. The antistatic master batch comprises, by mass, 20-80% of polyester, 15-40% of an antistatic agent, 0.5-2% of a nucleating agent, 3-5% of a dispersant and 0.5-3% of a coupling agent. The antistatic master batch prepared in the invention has the characteristics of good processability, efficient and lasting antistatic performance, good compatibility, good thermal stability, low cost, use convenience and the like when the antistatic master batch is used in the antistatic modification of the polyester, and polyester prepared by using the antistatic master batch has a guaranteed antistatic performance and allows the surface resistivity of a product to reduce to 10<8>-10<10>omega.cm, so the antistatic master batch has a wide development prospect.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an antistatic masterbatch for polyester. Background technique [0002] Polyethylene terephthalate (PET), referred to as polyester, is a crystalline polymer. Because it has the characteristics of high strength, good wear resistance, good resilience, and low cost, it occupies a considerable proportion in textiles. At the same time, polyester is an engineering plastic with excellent performance and a wide range of uses. However, due to the high resistivity of polyester, under the conditions of 65% relative humidity and 25°C, the moisture absorption rate is only 0.4%, and the resistivity is as high as 10. 14 Ω cm, it is very easy to generate static electricity, which limits its use in electrical and electronic industries. Antistatic polyester is polyester with antistatic properties. Generally, the resistivity of polyester is reduced by adding antistatic agents, so that it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/02C08K5/42C08K3/34C08K5/103C08K3/22C08K5/098C08K5/053C08J3/22
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap