Pyroxene peridotite type ilmenite depressing agent and preparation method thereof

An ilmenite and inhibitor technology, which is applied in the field of olivine-type ilmenite flotation inhibitor and its preparation, can solve the problems of low grade of strong magnetic concentrate, difficulty in flotation separation and the like, and achieve the inhibitory effect Good, solve the effect of low recovery rate, enlarge the difference of surface properties

Inactive Publication Date: 2014-04-16
INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI +1
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The olivine-type vanadium-titanium magnetite iron-separation tailings after stage grinding stage iron selection iron-separation tailings contain a large amount of olivine, and olivine iron content ranges from 10% to 50%, its magnetic properties and Compared with ilmenite, most of them are equivalent, and some are stronger than ilmenite, so it cannot be thrown into the tailings by strong magnetic separation, and it is difficult to separate them even by gravity separation (to maintain a high recovery rate). Throwing into the tailings, a large amount of olivine and ilmenite enter the strong magnetic concentrate at the same time, resulting in the strong magnetic concentrate TiO 2 The grade is not high, and the grade of TFe is higher (relative to the gabbro type), which brings great difficulties to flotation separation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of preparation method of olivine pyroxene type ilmenite flotation inhibitor, concrete preparation steps are as follows:

[0021] Step 1, weigh sodium silicate, ferric nitrate, sulfuric acid, and be mixed with the solution of concentration 10% respectively;

[0022] Step 2, taking out 10 parts of sodium silicate solution, 15 parts of ferric nitrate solution and 1 part of sulfuric acid solution from the three solutions prepared in step 1 and mixing them uniformly to obtain a mixed solution;

[0023] Step 3, stirring and vibrating the mixed solution in step 2 for 10 minutes, and then forming for 30-40 minutes to obtain the olivine pyroxene-type ilmenite flotation inhibitor.

[0024] When configuring the mixed solution in step 2, take out the sodium silicate solution and put it in a container, then add sulfuric acid solution to the sodium silicate solution, and finally add ferric nitrate solution.

[0025] The prepared olivine pyroxene-type ilmenite flotation inhibi...

Embodiment 2

[0027] A kind of preparation method of olivine pyroxene type ilmenite flotation inhibitor, concrete preparation steps are as follows:

[0028] Step 1, weigh sodium silicate, ferric nitrate, sulfuric acid, and be mixed with the solution of concentration 10% respectively;

[0029] Step 2, taking out 15 parts of sodium silicate solution, 10 parts of ferric nitrate solution, and 3 parts of sulfuric acid solution from the three solutions prepared in step 1, and mixing them uniformly to obtain a mixed solution;

[0030] Step 3, stirring and vibrating the mixed solution in step 2 for 10 minutes, and then forming for 30-40 minutes to obtain the olivine pyroxene-type ilmenite flotation inhibitor.

[0031] When configuring the mixed solution in step 2, take out the sodium silicate solution and put it in a container, then add sulfuric acid solution to the sodium silicate solution, and finally add ferric nitrate solution.

[0032] The prepared olivine pyroxene-type ilmenite flotation inh...

Embodiment 3

[0034] A kind of preparation method of olivine pyroxene type ilmenite flotation inhibitor, concrete preparation steps are as follows:

[0035] Step 1, weigh sodium silicate, ferric nitrate, sulfuric acid, and be mixed with the solution of concentration 10% respectively;

[0036] Step 2, taking out 10 parts of sodium silicate solution, 10 parts of ferric nitrate solution, and 5 parts of sulfuric acid solution from the three solutions prepared in step 1, and mixing them uniformly to obtain a mixed solution;

[0037] Step 3, stirring and vibrating the mixed solution in step 2 for 10 minutes, and then forming for 30-40 minutes to obtain the olivine pyroxene-type ilmenite flotation inhibitor.

[0038] When configuring the mixed solution in step 2, take out the sodium silicate solution and put it in a container, then add sulfuric acid solution to the sodium silicate solution, and finally add ferric nitrate solution.

[0039] The prepared olivine pyroxene-type ilmenite flotation inh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the ilmenite flotation technology, and particularly relates to a pyroxene peridotite type ilmenite depressing agent and a preparation method of the pyroxene peridotite type ilmenite depressing agent. The preparation method of the pyroxene peridotite type ilmenite depressing agent comprises the step of carrying out oscillation, stir and curing on a mixed solution formed by sodium silicate, ferric nitrate and sulfuric acid to obtain the pyroxene peridotite type ilmenite depressing agent, wherein oscillation, stir and curing are carried out for 30-40min. The obtained pyroxene peridotite type ilmenite depressing agent comprises, by weight, 5-15 parts of the sodium silicate, 5-15 parts of the ferric nitrate and 1-10 parts of the sulfuric acid. The pyroxene peridotite type ilmenite depressing agent obtained through the preparation method has a good selective depressing effect on olivine and pyroxene, and has extremely important significance in obtaining of good technical indexes of titanium flotation of pyroxene peridotite type ilmenite.

Description

technical field [0001] The invention belongs to ilmenite flotation technology, in particular to an olivine pyroxene type ilmenite flotation inhibitor and a preparation method thereof. Background technique [0002] Titanium concentrate is extracted from ilmenite or titanomagnetite, and it is the raw material for producing titanium materials and titanium dioxide which are widely used. Titanium dioxide scientific name titanium dioxide (TiO 2 ), is a white inorganic pigment with non-toxicity, best opacity, best whiteness and brightness. It is considered to be a white pigment with the best performance in the world. Printing ink, chemical fiber, rubber, ceramics, cosmetics, food additives and pharmaceutical industries. Titanium metal is widely used in military industry, aerospace, marine industry, chemical industry, petroleum refining, automobile industry, medicine, sports and daily necessities, building materials and nuclear industry. With the further development of the indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B03D1/002B03D101/06
Inventor 张渊王文超邓冰邓杰陶章明杨永涛徐明
Owner INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com