Breakdown-resistant and small-size isotatic polypropylene capacitor metalized film and preparation method thereof

An isotactic polypropylene and metallized film technology, applied in fixed capacitor electrodes, fixed capacitor dielectrics, fixed capacitor components, etc., can solve problems such as hidden dangers of electrical equipment or power grid safety, capacitor stability degradation, capacitor failure and other problems , to achieve the effect of reducing scrap rate, small contact resistance and preventing breakdown

Inactive Publication Date: 2014-04-30
TONGLING QILI ELECTRONICS MATERIALS
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing polypropylene capacitor film has a relatively large shrinkage rate and poor temperature resistance. As the working time of the capacitor wound by this film increases, the internal temperature rises rapidly, resulting in a sharp decline in the stability of the capacitor. It may even cause the capacitor to fail, bringing serious safety hazards to the electrical machine or the power grid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The present invention will be described in detail below through specific examples.

[0015] A metallized film of isotactic polypropylene capacitor with small breakdown resistance, made of the following raw materials in parts by weight (kg): isotactic polypropylene 200, high-density polyethylene 12, talcum powder 2, turpentine 4, butyric acid Isoamyl Ester 2, Sodium Allyl Sulfonate 1, Nano Clay 1, Stearic Acid 1, Glycerin Triacetate 3, Auxiliary 5;

[0016] The auxiliary agent is made of the following raw materials in parts by weight (kg): metallocene linear low-density polyethylene 12, acetyl triethyl citrate 14, vinyl propionate 3, basswood ash 2, crosslinking agent TAC1, 2 - Ethylhexyl diphenyl phosphate 5, polyvinyl alcohol 2, rose essential oil 0.1; the preparation method is to heat metallocene linear low-density polyethylene to a molten state, then add polyvinyl alcohol and basswood ash and stir for 10-15 Minutes, finally add other ingredients, stir to disperse ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention discloses a breakdown-resistant and small-size isotatic polypropylene capacitor metalized film which is characterized by being prepared from the following raw materials in parts by weight: 200 parts of isotatic polypropylene, 12-14 parts of high-density polyethylene, 2-3 parts of talcum powder, 4-6 parts of turpentine, 2-3 parts of isoamyl butyrate, 1-2 parts of sodium allysulfonate, 1-2 parts of nano-clay, 1-2 parts of stearic acid, 3-4 parts of glycerol triacetate and 5-6 parts of auxiliaries. The breakdown-resistant and small-size isotatic polypropylene capacitor metalized film is simple in processing technology; and a film capacitor prepared from the breakdown-resistant and small-size isotatic polypropylene capacitor metalized film is low in contact resistance, so that the product feature is good, the prepared capacitor is relatively small in size and also has relatively good high-temperature stability; impurities in raw materials are removed through filtering, so that the performances of the raw materials are good, the scrap rate of the film is reduced, and the film is not easy to fracture; and the film is subjected to corona treatment, so that the compression strength of the film is improved, the film is prevented from being broken down, and the service life of the film is prolonged.

Description

technical field [0001] The invention relates to the field of capacitor manufacturing, in particular to a metallized film of an isotactic polypropylene capacitor with small breakdown resistance and a preparation method thereof. Background technique [0002] Biaxially oriented polypropylene film for capacitors has high mechanical and electrical properties. Compared with capacitors made of ordinary films, capacitors made of polypropylene films have low thermal shrinkage, stable performance, high temperature resistance, High voltage resistance, breakdown prevention and other significant advantages make capacitors made of polypropylene film more and more widely used. [0003] The existing polypropylene capacitor film has a relatively large shrinkage rate and poor temperature resistance. As the working time of the capacitor wound by this film increases, the internal temperature rises rapidly, resulting in a sharp decline in the stability of the capacitor. It even causes the capac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L23/08C08K13/02C08K3/34C08K5/101C08K5/42C08K5/09C08K5/103B29D7/01H01G4/18
CPCC08L23/12B29C48/0018C08J5/18C08J2323/12C08J2423/06C08J2423/08C08J2429/04C08K2201/011C08K2201/014C08L2201/08C08L2203/16C08L2203/20C08L2205/035C08L2207/062H01G4/008H01G4/015C08L23/06C08L23/0815C08L29/04C08K13/02C08K3/34C08K5/101C08K5/42C08K5/09C08K5/103
Inventor 荚朝辉
Owner TONGLING QILI ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products