Metal antirust paint and preparation method thereof

A technology for metal rust prevention and quality, applied in anti-corrosion coatings, coatings, etc., can solve the problems of slow drying speed of organic solvents and paint films, and achieve the effect of fast drying speed

Inactive Publication Date: 2014-04-30
SUZHOU CITY BANGCHENG ELECTRICITY TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: Aiming at the shortcomings of the existing metal antirust paint containing organic solvents harmful to the human body and the environment and slow drying speed of the paint film, the present invention provides a Metal antirust paint and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] This embodiment provides a metal anti-corrosion paint, which contains the following ingredients in parts by mass: 45 parts of styrene-acrylic emulsion, 25 parts of iron oxide yellow, 16 parts of anti-rust yellow, 23 parts of zinc phosphate, 6 parts of zinc oxide, dodecane 5.5 parts of sodium benzene sulfonate, 13 parts of mica powder, 5.5 parts of tannic acid, 5.8 parts of dihydrogen phosphate, 4.5 parts of polyacrylic acid copolymer emulsion, 3.7 parts of organosiloxane, 3.2 parts of sodium nitrite, 92 parts of deionized water Copies.

[0010] The preparation steps of a kind of metal anti-rust paint are as follows: add deionized water and sodium dodecylbenzene sulfonate into a stainless steel reaction kettle, stir to make it evenly mixed, and heat up to 55°C, then add iron oxide yellow and anti-rust Yellow, zinc phosphate, zinc oxide, styrene-acrylic emulsion, mica powder, tannic acid, dihydrogen phosphate, organosiloxane, polyacrylic acid copolymer emulsion and sodium ni...

Embodiment 2

[0013] This embodiment provides a metal anti-corrosion paint, which contains the following components in parts by mass: 35 parts of styrene-acrylic emulsion, 16 parts of iron oxide yellow, 8 parts of anti-rust yellow, 15 parts of zinc phosphate, 2 parts of zinc oxide, dodecane 2.5 parts of sodium benzene sulfonate, 7 parts of mica powder, 2.3 parts of tannic acid, 2.2 parts of dihydrogen phosphate, 3 parts of polyacrylic acid copolymer emulsion, 1.3 parts of organosiloxane, 2.3 parts of sodium nitrite, and 80 deionized water Copies.

[0014] The preparation steps of a kind of metal anti-rust paint are as follows: add deionized water and sodium dodecylbenzene sulfonate into a stainless steel reaction kettle, stir to make it evenly mixed, and heat up to 45°C, then add iron oxide yellow and anti-rust Yellow, zinc phosphate, zinc oxide, styrene acrylic emulsion, mica powder, tannic acid, dihydrogen phosphate, organosiloxane, polyacrylic acid copolymer emulsion and sodium nitrite, sti...

Embodiment 3

[0017] This embodiment provides a metal anti-corrosion paint, which contains the following ingredients in parts by mass: 40 parts of styrene-acrylic emulsion, 21 parts of iron oxide yellow, 12 parts of anti-rust yellow, 19 parts of zinc phosphate, 4 parts of zinc oxide, dodecane 4 parts of sodium benzene sulfonate, 10 parts of mica powder, 3.9 parts of tannic acid, 4 parts of dihydrogen phosphate, 3.7 parts of polyacrylic acid copolymer emulsion, 2.5 parts of organosiloxane, 2.8 parts of sodium nitrite, 86 parts of deionized water Copies.

[0018] The preparation steps of a kind of metal anti-rust paint are as follows: add deionized water and sodium dodecylbenzene sulfonate into a stainless steel reaction kettle, stir to make it evenly mixed, and heat up to 50°C, then add iron oxide yellow and anti-rust Yellow, zinc phosphate, zinc oxide, styrene-acrylic emulsion, mica powder, tannic acid, dihydrogen phosphate, organosiloxane, polyacrylic acid copolymer emulsion and sodium nitrit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a metal antirust paint and a preparation method thereof. The metal antirust paint consists of the following ingredients in parts by mass: 35-45 parts of styrene-acrylic emulsion, 16-25 parts of iron oxide yellow, 8-16 parts of antirust yellow, 15-23 parts of zinc phosphate, 2-6 parts of zinc oxide, 2.5-5.5 parts of sodium dodecyl benzene sulfonate, 7-13 parts of mica powder, 2.3-5.5 parts of gallotannic acid, 2.2-5.8 parts of dihydric phosphate, 3-4.5 parts of polyacrylic copolymer emulsion, 1.3-3.7 parts of organic siloxane, 2.3-3.2 parts of sodium nitrite and 80-92 parts of deionized water. The metal antirust paint disclosed by the invention is harmless to the human body and the environment; a paint film is dried rapidly; furthermore, a metal is enabled to have passivation, rusting and rust prevention functions, and the metal can be directly painted without a rust prevention treatment, so the labor and time are saved.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a metal antirust paint and a preparation method thereof. Background technique [0002] Metal is easily damaged by the action of the surrounding medium, that is, rust. When corroded, the mechanical properties such as strength, plasticity and toughness of the metal are destroyed, which greatly shortens the service life of the metal and causes a waste of resources. There are many types of metal antirust paints available on the market, but they generally contain organic solvents that are harmful to the human body and the environment, and the paint film dries slowly. Contents of the invention [0003] Technical problem to be solved: In view of the shortcomings of the existing metal antirust paint containing organic solvents harmful to the human body and the environment and slow drying speed of the paint film, the invention provides a metal antirust paint and a preparation method thereof. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D133/00C09D7/12C09D5/08
Inventor 陈汉刚
Owner SUZHOU CITY BANGCHENG ELECTRICITY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More