Leaching method of lithium cobaltate waste battery positive electrode material

A technology for positive electrode materials and waste batteries, which is applied in the leaching field of positive electrode materials for lithium cobalt oxide waste batteries, and can solve problems such as troublesome storage, transportation and use of industrial pure oxygen, uneconomical use of industrial pure oxygen for personal use, and small amount of industrial pure oxygen. , to achieve obvious economic and environmental benefits, reduce pollution treatment costs, and increase the metal leaching rate

Inactive Publication Date: 2014-04-30
SICHUAN NORMAL UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The consumption of nitric acid in the nitric acid leaching method is large, and a large amount of nitrogen oxides will be produced, polluting the environment
All wet processes have the problem of how to economically increase the leaching speed, increase the metal leaching rate, and reduce the consumption of acid and other auxiliary materials.
Although the pure oxygen leaching method in the nitric acid processing industry and the pure oxygen leaching method in the mixed acid processing industry have solved the above problems, the leaching equipment is more complicated, and the amount of industrial pure oxygen required for the leaching of waste batteries is not large, and waste battery treatment enterprises produce on-site Industrial pure oxygen is not economical for personal use, and the storage, transportation and use of industrial pure oxygen are troublesome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1: Add 100 g of lithium cobalt oxide waste battery cathode material (containing 53.6% cobalt, 5.3% lithium, 8.2% copper, 3.4% aluminum) and 30 g of corn cob powder ≤ 1.5 mm into a titanium-lined pressure reactor with a volume of 2 L , add 1180ml of a mixed acid solution with a sulfuric acid concentration of 1.5mol / L and a nitric acid concentration of 5g / L, leaching at 60°C to 70°C with closed stirring (stirring speed 80r / min) for 4.0h, and liquid-solid separation after leaching, to obtain 1160ml leaching solution (excluding leaching slag washing water). The leaching rates of cobalt, lithium, copper and aluminum are 99.2%, 99.2%, 98.3% and 98.6% respectively (calculated based on cobalt, lithium, copper and aluminum entering the leaching solution and leaching slag washing solution).

Embodiment 2

[0019] Example 2: Add 500g of lithium cobalt oxide waste battery positive electrode material (containing 53.6% cobalt, 5.3% lithium, 8.2% copper, 3.4% aluminum)≤1.5mm corncob powder 190g into a titanium-lined pressure reactor with a volume of 5L, Add 3500ml of a mixed acid solution with a concentration of sulfuric acid of 3.0mol / L and a concentration of nitric acid of 10g / L, and leaching at 70°C to 80°C (stirring speed 70r / min) for 2h in a closed manner. solution (excluding leaching slag washing water), the leaching rates of cobalt, lithium, copper and aluminum are 99.4%, 99.5%, 99.0% and 98.8% respectively (according to the cobalt, lithium, copper in the leaching solution and leaching slag washing solution and aluminum calculations).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a leaching method of a lithium cobaltate waste battery positive electrode material, which comprises the following steps: adding a positive electrode material subjected to roasting pretreatment separated from lithium cobaltate waste batteries and corn cob powder into a pressure-resistant sulfuric-acid / nitric-acid-corrosion-resistant reaction kettle, adding a sulfuric acid-nitric acid mixed solution, and carrying out agitation leaching under sealed conditions.

Description

technical field [0001] The invention relates to a method for leaching lithium cobalt oxide waste battery cathode materials. Background technique [0002] Lithium cobalt oxide battery is a type of battery widely used, and a large amount of waste batteries will be generated after the battery is scrapped. Because this type of battery contains a large amount of heavy metals, if it is discarded into the environment, it will cause great direct and potential harm to the environment. The positive electrode material of lithium cobalt oxide waste batteries mainly contains cobalt, lithium, copper and aluminum, and the total content of cobalt, lithium and copper is more than 60%, which is very valuable for recycling. At present, the processes for recovering cobalt, lithium and copper from the positive electrode materials of lithium cobalt oxide waste batteries mainly include fire process and wet process. The products obtained by the fire process are alloy materials, and it is difficu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B7/00C22B1/02C22B3/06C22B15/00C22B21/00C22B23/00C22B26/12
CPCY02P10/20
Inventor 龙炳清崔伟张章
Owner SICHUAN NORMAL UNIVERSITY