Coating graphite protective lubricant, and preparation method and application method thereof

A technology of lubricants and graphite, which is applied in lubricating compositions, petroleum industry, etc., can solve problems such as easy adhesion and wear of molds, short life of molds, and low precision of forgings

Active Publication Date: 2014-05-28
QINGDAO YUANDA GRAPHITE
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no coating to protect the lubricant, so the mold is prone to adhesion and wear during warm forging and closed forging, the life of the mold is short, and the precision of the forging is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A coating graphite protective lubricant comprises the following formula components in parts by mass:

[0048] Monoethanolamine: 1.5-2 parts; Sodium silicate: 2.2-3 parts; Gelatin: 1.8-2 parts; Borax: 4.7-5 parts; Oxazolidine: 0.4-0.5 parts; -1.5 parts; ethylene-vinyl acetate copolymer: 4.2-5 parts; 2-ethyl acrylate: 0.8-1 parts; diacetone alcohol: 2.2-3 parts; graphite: 14-15 parts; Ionized water: 60-62 parts.

[0049] The preparation method of described graphite protective lubricant comprises the following steps:

[0050] (1) Add 2.2-3 parts of diacetone alcohol to 0.8-1 part of 2-ethyl ethyl acrylate to dilute to obtain A solution;

[0051] (2) Fully stir and dissolve 1.8-2 parts of gelatin with 10 parts of distilled water or deionized water at 70°C-100°C to obtain solution B;

[0052] (3) After fully dissolving 2.2-3 parts of sodium silicate, 4.7-5 parts of borax, and 1.5-2 parts of monoethanolamine in solution B, add 1.3-1.5 parts of methylene bis-naphthalenesulf...

Embodiment 2

[0056] A coating graphite protective lubricant comprises the following formula components in parts by mass:

[0057] Monoethanolamine: 2 parts; Sodium silicate: 3 parts; Gelatin: 2 parts; Borax: 5 parts; Oxazolidine: 0.5 parts; 5 parts; 2-ethyl ethyl acrylate: 1 part; diacetone alcohol: 3 parts; graphite: 15 parts; distilled or deionized water: 62 parts.

[0058] The preparation method of described graphite protective lubricant comprises the following steps:

[0059] (1) Add 1 part by mass of 2-ethyl ethyl acrylate to 3 parts of diacetone alcohol for dilution to obtain A solution;

[0060] (2) Fully stir and dissolve 2 parts of gelatin with 10 parts of distilled water or deionized water at 70°C to obtain solution B;

[0061] (3) After dissolving the sodium silicate of 3 parts of quality, 5 parts of borax, and the monoethanolamine of 2 parts in the B solution, after fully dissolving, add the sodium methylene bis-naphthalene sulfonate of 1.5 parts of quality and 5 parts of eth...

Embodiment 3

[0065] A coating graphite protective lubricant comprises the following formula components in parts by mass:

[0066] Monoethanolamine: 1.8 parts; Sodium silicate: 2.6 parts; Gelatin: 1.9 parts; Borax: 4.8 parts; Oxazolidine: 0.45 parts; 4.7 parts; 2-ethyl ethyl acrylate: 0.9 parts; diacetone alcohol: 2.6 parts; graphite: 14.5 parts; distilled water or deionized water: 61 parts.

[0067] The preparation method of described graphite protective lubricant comprises the following steps:

[0068] (1) Add 0.9 parts of 2-ethyl ethyl acrylate to 2.6 parts of diacetone alcohol for dilution to obtain A solution;

[0069] (2) Fully stir and dissolve 1.9 parts of gelatin with 10 parts of distilled water or deionized water at 90°C to obtain solution B;

[0070] (3) After dissolving the sodium silicate of 2.6 parts of quality, 4.7 parts of borax, and the monoethanolamine of 1.8 parts in the B solution, after fully dissolving, add the sodium methylene bis-naphthalene sulfonate of 1.4 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a coating graphite protective lubricant, and a preparation method and application method thereof. The coating graphite protective lubricant comprises the following ingredients by mass: 1.5-2 parts of monoethanolamine, 2.2-3 parts of sodium silicate, 1.8-2 parts of gelatins, 4.7-5 parts of sodium borate, 0.4-0.5 part of oxazolidine, 1.3-1.5 parts of sodium methylene bis-naphthalene sulfonate, 4.2-5 parts of ethylene-vinyl acetate copolymer, 0.8-1 part of crylic acid-2-ethylhexyl, 2.2-3 parts of diacetone alcohol, 14-15 parts of graphite and 60-62 parts of distilled water or deionized water. According to the invention, the coating graphite protective lubricant doesn't fall off, can't be oxidized, and has a good lubricating property and rejection capability.

Description

technical field [0001] The invention relates to the field of high-temperature lubrication, in particular to a coated graphite protective lubricant, a preparation method and a use method thereof. Background technique [0002] Forging is a system engineering involving many links, and forging technology is the basic technology supporting modern industry. Can be divided into cold forging, hot forging, warm forging, sub-hot forging, closed forging, ring rolling forging. The most important and critical link in the forging process is the mold. Forging dies usually have to withstand high pressure at a high temperature of hundreds of degrees or even thousands of degrees to complete metal forming. Fierce market competition forces customers to put forward higher requirements for forgings. Therefore, improving the quality of forgings, reducing the cost of forgings, and prolonging the life of the die are forging key to business survival. [0003] Undoubtedly, improving the life of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10M177/00B21J3/00C10N40/24
Inventor 邴岐杰
Owner QINGDAO YUANDA GRAPHITE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap