High-wear-resistant ceramic tile and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A ceramic tile, high wear-resistant technology, applied in the field of building ceramic materials, can solve the problems of large amount of wear, affecting the service life of tiles, poor wear resistance, etc., and achieve long service life, strong erosion resistance, and good heat resistance Effect
Active Publication Date: 2014-07-30
安徽省亚欧陶瓷有限责任公司
View PDF4 Cites 30 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, ceramic tiles on the market have poor wear resistance and a large amount of wear during use, which seriously affects the service life of the tiles.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] A high wear-resistant ceramic brick made of the following raw materials in weight (kg): 45 zircon sand, 25 sea sand, 30 soapstone, 15 turpentine rock, 10 coal gangue, 25 white corundum, 12 diatomaceous earth, and viola Bluestone 18, nano-titanium carbide 6, light magnesium oxide 8, graphite powder 4, cement slag 8, modified clay 16, precipitated barium sulfate 4;
[0016] The preparation method of the modified clay is as follows: a. Take bauxite, kaolin, and attapulgite in a mass ratio of 6:4:2, mix them evenly, put them into a hydrochloric acid solution with a concentration of 120%, and heat them in a water bath to 65 ℃, keep warm for 0.5h, filter, wash with distilled water until neutral, dry, calcine at 480°C for 2h, pulverize, pass through a 200-mesh sieve, and set aside; b. Weigh a certain amount of chitosan and add it to a volume concentration of 1%. In the acetic acid solution, stir and dissolve, and prepare a chitosan colloid solution with a concentration of ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
wear volume
aaaaa
aaaaa
wear volume
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a high-wear-resistant ceramic tile and a preparation method thereof. The high-wear-resistant ceramic tile is prepared from the following raw materials in parts by weight: 40-50 parts of zircon sand, 20-30 parts of sea sand, 25-35 parts of soapstone, 10-20 parts of pitchstone, 5-15 parts of coal gangue, 20-30 parts of white corundum, 10-15 parts of diatomite, 12-24 parts of cordierite, 4-8 parts of nano titanium carbide, 6-12 parts of light magnesium oxide, 3-6 parts of a graphite powder, 5-10 parts of cement slag, 15-20 parts of modified clay, and 2-5 parts of precipitated barium sulfate. The zircon sand, the white corundum, the precipitated barium sulfate, nano titanium carbide and other raw materials are added into the ceramic tile, so that the wear resistance of the ceramic tile can be significantly improved, the room-temperature wearing capacity is not more than 10 cm<3>, and the ceramic tile has the advantages of high strength, good heat resistance, good water resistance, strong anti-erosion ability, long service life, and wide market prospect.
Description
technical field [0001] The invention relates to a high wear-resistant ceramic brick and a preparation method thereof, belonging to the field of building ceramic materials. Background technique [0002] Ceramic bricks are plate or block ceramic products produced by clay, quartz sand and other inorganic non-metallic raw materials through batching, ball milling, powder making, molding, sintering and other processes. They are widely used in decoration and protection of walls of buildings and structures. face and ground. With the rapid development of the real estate industry, the production and consumption of ceramic tiles have achieved greater development. At present, the ceramic tiles on the market have poor wear resistance, and the amount of wear is relatively large during use, which seriously affects the service life of the tiles. Contents of the invention [0003] The object of the present invention is to address the deficiencies of the prior art, to provide a high wear...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more