A li-zn ferrite material

A technology of ferrite material and ferrite magnetism, applied in the field of Li-Zn ferrite material, can solve the problems of low forming density and poor performance of Li-Zn ferrite, so as to improve the magnetic properties and improve the forming density and uniformity, the effect of improving the microstructure

Active Publication Date: 2015-09-23
TAICANG CITY LVDIAN INFORMATION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a Li-Zn ferrite material due to the problems of low molding density and poor performance in existing Li-Zn ferrite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Taking x=1, the Li-Zn ferrite soft magnetic material Li 1.5 ZnFe 1.5 o 4 .

[0021] 1) Add 1 gram of cetyltrimethylamine bromide to 100 grams of ferrous sulfate solution with a mass fraction of 30%, then add 20.68 grams of zinc sulfate and 3.99 grams of lithium acetate and stir for 0.5 hours, and use a mass fraction of 5% The sulfuric acid solution adjustment system pH value is 4;

[0022] 2) Continue to add 5 grams of vinyltrichlorosilane, raise the temperature of the system to 40°C, and keep stirring for 0.5 hours to prepare a dispersion mixture;

[0023] 3) Transfer the dispersed mixed liquid prepared in step 2) to a high-pressure reactor for hydrothermal crystallization reaction, the crystallization temperature is 120°C, and the crystallization time is 36 hours, then filtered, washed, and dried to obtain a mixed powder;

[0024] 4) The mixed powder prepared in step 3) and the silica sol with a mass concentration of silica of 20% were ground and stirred at a mass...

Embodiment 2

[0026] Taking x=2, the Li-Zn ferrite soft magnetic material LiZn is obtained 2 FeO 4 .

[0027] 1) Add 5 grams of cetyltrimethylamine bromide to 100 grams of ferrous sulfate solution with a mass fraction of 45%, then add 93.07 grams of zinc sulfate and 5.98 grams of lithium acetate and stir for 2 hours, and use a mass fraction of 15% The sulfuric acid solution adjustment system pH value is 6;

[0028] 2) Continue to add 15 grams of vinyltrimethoxysilane, raise the temperature of the system to 60°C, and keep stirring for 2 hours to prepare a dispersion mixture;

[0029] 3) Transfer the dispersed mixed solution prepared in step 2) to a high-pressure reactor for hydrothermal crystallization reaction, the crystallization temperature is 160°C, and the crystallization time is 12 hours, then filtered, washed, and dried to obtain a mixed powder;

[0030] 4) The mixed powder prepared in step 3) and the silica sol with a mass concentration of 30% of silica were ground and stirred at ...

Embodiment 3

[0032] Taking x=3, the Li-Zn ferrite soft magnetic material Li 0.5 Zn 3 Fe 0.5 o 4 .

[0033] 1) Add 3 grams of cetyltrimethylamine bromide to 100 grams of ferrous sulfate solution with a mass fraction of 20%, then add 120.22 grams of zinc sulfate and 2.65 grams of lithium acetate and stir for 1 hour, and use a mass fraction of 10% The hydrochloric acid solution adjustment system pH value is 5;

[0034] 2) Continue to add 10 grams of vinyltrimethoxysilane, raise the temperature of the system to 50°C, and keep stirring for 1 hour to prepare a dispersion mixture;

[0035] 3) Transfer the dispersed mixed solution prepared in step 2) to a high-pressure reactor for hydrothermal crystallization reaction, the crystallization temperature is 150°C, and the crystallization time is 24 hours, then filtered, washed, and dried to obtain a mixed powder;

[0036] 4) The mixed powder prepared in step 3) and the silica sol with a mass concentration of silica of 40% were ground and stirred ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a Li-Zn ferrite material. The Li-Zn ferrite material comprises ferrite magnetic powder and an inorganic binder and is prepared through grinding and stirring, cold press forming and high temperature sintering. The Li-Zn ferrite material is characterized in that the ferrite magnetic powder is Li<2-0.5x>ZnxFe<2-0.5x>O4, x is 1, 2 or 3, and the inorganic binder is silica sol. The Li-Zn ferrite material has the advantages that 1) by adding a silane coupling agent, particle agglomeration can be effectively reduced, the dispersibility and flowability of the powder can be improved, and the forming density and uniformity of the Li-Zn ferrite can be improved; 2) the Li-Zn ferrite has good high-frequency soft magnetic properties and relatively low sintering temperature; 3) silica sol is adopted as the inorganic binder and silicon can play a role of doping in the high temperature sintering process, thus improving the magnetic properties and microstructure of the Li-Zn ferrite.

Description

technical field [0001] The invention relates to a ferrite soft magnetic material, in particular to a Li-Zn ferrite material. Background technique [0002] With the development of electronic technology, the research of electromagnetic shielding and absorbing materials has been highly valued by various countries. The development of new electromagnetic shielding and absorbing materials with good structural stability, high absorption, wide frequency band and low density is not only the need of stealth technology , and the civil field also has a very wide range of applications. [0003] Li-Zn ferrite is a very important soft magnetic material with spinel structure, which has high resistivity, squareness ratio and Curie temperature, wide adjustable range of saturation magnetization, low sensitivity of remanence to stress, temperature It is widely used in the manufacture of microwave devices due to its good stability, low magnetostriction coefficient and small microwave dielectric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/26C04B35/632
Inventor 李江太
Owner TAICANG CITY LVDIAN INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com