Aluminum fins

A fin and aluminum plate technology, which is applied in the field of aluminum fin materials for heat exchangers, can solve the problems of reduced hydrophilicity, easy blockage of fins, and maintenance of hydrophilicity on the surface of fins, achieving the effect of improved stamping processability

Inactive Publication Date: 2016-03-16
KOBE STEEL LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] However, in the invention of the above-mentioned patent document, if the hydrophilic resin film is in contact with water, the hydrophilicity decreases with time, and it is difficult to maintain the hydrophilicity of the fin surface for a long time.
That is, with long-term use, the dew condensation water adhering to the fins tends to become hemispherical, and as a result, the fins tend to be clogged.
Therefore, it is difficult to say that the problem of the heat exchange function of the heat exchanger being hindered has been solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum fins
  • Aluminum fins
  • Aluminum fins

Examples

Experimental program
Comparison scheme
Effect test

no. 1 Embodiment approach

[0032]

[0033] Such as figure 1 As shown, the aluminum fin material (hereinafter referred to as the fin material) 10A of the present invention includes in order: an aluminum plate or an aluminum alloy plate (hereinafter referred to as the aluminum plate) 1 , and a hydrophilic film layer 2 formed on the surface of the aluminum plate 1 and a lubricating film layer3. In addition, the lubricating film layer 3 includes a resin composition containing a lubricating resin and a crosslinking agent 6, and the ratio of the solid content of the crosslinking agent 6 to the total solid content of the lubricating resin and the crosslinking agent 6 is 0.2 to 70%. % by mass, the hydrophilic film layer 2 contains a resin composition containing a polymer having a carboxyl group or the like. Each configuration will be described below.

[0034] (aluminum plate)

[0035] The aluminum plate 1 used in the present invention is a plate material made of aluminum or an aluminum alloy. Such aluminu...

no. 2 Embodiment approach

[0050] Such as figure 2 As shown, the fin material 10B preferably further includes a corrosion-resistant coating layer 5 containing a resin composition (corrosion-resistant resin composition) containing a corrosion-resistant resin between the aluminum plate 1 and the hydrophilic coating layer 2 .

[0051] (corrosion-resistant film layer)

[0052] The corrosion-resistant coating layer 5 improves the corrosion resistance of the fin material 10B, and also improves the adhesion of the hydrophilic coating layer 2 . In addition, since the corrosion-resistant film layer 5 is hydrophobic, it is possible to suppress the generation of unpleasant smell due to sub-film corrosion (corrosion of the aluminum plate 1 ) caused by water penetrating into the aluminum plate 1 .

[0053] The corrosion-resistant resin constituting the corrosion-resistant film layer 5 contains one or more types selected from polyester-based resins, polyolefin-based resins, epoxy-based resins, acrylic resins, and p...

no. 3 Embodiment approach

[0057] Such as image 3 As shown, the fin material 10C preferably includes the chemical conversion treatment film layer 4 between the aluminum plate 1 and the hydrophilic film layer 2 .

[0058] (Chemical treatment film layer)

[0059] The presence of the chemical conversion treatment film layer 4 improves the corrosion resistance of the fin material 10C, and further improves the adhesion of the hydrophilic film layer 2 to the aluminum plate 1 . Therefore, the durability of the heat exchanger can be improved. In addition, the chemical conversion treatment film layer 4 is formed by subjecting the surface of the aluminum plate 1 to a chemical conversion treatment before forming the hydrophilic film layer 2 .

[0060] The chemical conversion treatment film layer 4 is preferably formed by performing an inorganic oxide treatment such as phosphoric acid chromate treatment or coating type zirconium treatment, or a known chemical conversion treatment such as organic-inorganic compos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Adhesion amountaaaaaaaaaa
Login to view more

Abstract

Provided is an aluminum fin material in which the hydrophilicity of a fin material surface is sustained for a long period time. A fin material (10A) having a hydrophilic film layer (2) and a lubricant film layer (3) provided to the surface of an aluminum plate (1) in the stated order, the fin material being characterized in that: the hydrophilic film layer (2) is composed of a polymer configured solely from a monomer having a carboxyl group, a copolymer containing a monomer having a carboxyl group, or a resin substance containing a hydrophilic resin as a mixture thereof; and the lubricant film layer (3) is composed of a resin composition in which a crosslinking agent (6) has a solids ratio of 0.2 to 70 mass%, the lubricant film layer (3) containing one or more lubricant resins selected from the group consisting of polyethylene glycol, carboxymethyl cellulose, and an alkali metal salt of carboxymethyl cellulose, and one or more crosslinking agents (6) selected from the group consisting of a water-soluble epoxy resin, a water-soluble carbodiimide compound, a water-dispersible carbodiimide compound, and a water-soluble oxazoline group-containing resin.

Description

technical field [0001] The present invention relates to an aluminum fin material made of aluminum or an aluminum alloy having a film layer formed on its surface, and particularly relates to an aluminum fin material for heat exchangers suitable for use in heat exchangers such as air conditioners. Background technique [0002] Due to global warming and the rapid increase in resource prices in recent years, there has been an increasing demand for performance improvements such as high efficiency and miniaturization of air conditioners. Aluminum plates excellent in thermal conductivity, workability, corrosion resistance, etc. (hereinafter, aluminum alloy plates are suitably included) are widely used in heat exchangers of air conditioners that reflect such demands. In addition, in order to reduce the volume of the heat exchanger of the air conditioner, fins are arranged side by side at narrow intervals. [0003] However, when the temperature of the surface of the fins falls below...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F28F13/18C10M107/34C10M107/36C10M177/00F28F1/32F28F19/04C10N30/00C10N40/00C10N70/00
CPCC10M159/12C10M177/00C10M2209/1023C10M2209/1045C10M2209/123C10M2217/0403C10N2050/025F28F1/12F28F17/005F28F19/04F28F21/084F28F2245/02
Inventor 馆山庆太太田阳介
Owner KOBE STEEL LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap