A kind of regeneration method of zinc oxide desulfurization waste agent

A technology of zinc oxide and desulfurizer, which is applied in chemical instruments and methods, separation methods, and separation of dispersed particles, can solve problems such as high cost and unsuitability for industrial application, reduce regeneration costs, benefit industrial production, and increase reaction yield. rate effect

Active Publication Date: 2016-08-17
福建三聚福大化肥催化剂国家工程研究中心有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention solves the problem that the regeneration method of zinc oxide desulfurization waste agent in the prior art is unsuitable for industrial application due to its high cost, and further provides a regeneration method that not only has a high recycling rate of zinc, but also can greatly reduce the regeneration cost. Regeneration method of zinc oxide desulfurization waste agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of regeneration method of zinc oxide desulfurization waste agent
  • A kind of regeneration method of zinc oxide desulfurization waste agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The regeneration method of zinc oxide desulfurization waste agent described in the present embodiment is:

[0022] Add 1g of zinc oxide desulfurization waste agent and 70mL of deionized water to a 100mL hydrothermal reaction kettle in sequence, place the hydrothermal reaction kettle in an oven at 200°C for 24 hours, cool naturally after the reaction is completed, and filter the reaction solution. Collect the filter residue, wash the filter residue 6 times with deionized water, and dry at 110° C. for 10 hours to obtain a regenerated zinc oxide desulfurizer. Grind the regenerated zinc oxide desulfurizer into a powder of more than 200 meshes, and use X-ray diffractometer (XRD) to carry out structural characterization, such as figure 1 As shown, the diffraction peak changes of zinc oxide and zinc sulfide were observed.

Embodiment 2

[0024] The regeneration method of zinc oxide desulfurization waste agent described in the present embodiment is:

[0025] Add 1g of zinc oxide desulfurization waste agent, 60mL of deionization and 10mL of ammonia water to a 100mL hydrothermal reaction kettle in sequence, place the hydrothermal reaction kettle in an oven at 250°C for 12 hours, cool naturally after the reaction is completed, and dissolve the reaction solution filtering, collecting the filter residue, washing and drying the filter residue to obtain a regenerated zinc oxide desulfurizer.

Embodiment 3

[0027] The regeneration method of zinc oxide desulfurization waste agent described in the present embodiment is:

[0028] Add 1g of zinc oxide desulfurization waste agent, 50mL of deionization and 20mL of ammonia water to a 100mL hydrothermal reaction kettle in sequence, place the hydrothermal reaction kettle in an oven at 200°C for 24 hours, cool naturally after the reaction is completed, and dissolve the reaction solution Filter, collect the filter residue, wash the filter residue 6 times with deionized water, and dry at 110° C. for 10 hours to obtain a regenerated zinc oxide desulfurizer. Grind the regenerated zinc oxide desulfurizer into a powder of more than 200 mesh, and use XRD for structural characterization, such as figure 2 As shown, the diffraction peak changes of zinc oxide and zinc sulfide were observed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for regenerating zinc oxide desulfurization waste agent, which comprises reacting the zinc oxide desulfurization waste agent with deionized water at a temperature of 150-250°C for 12-48 hours in a hydrothermal reaction kettle, wherein the The mass ratio of zinc oxide desulfurization waste agent to deionized water is 1:70. After the reaction is completed, the reaction solution is filtered, and the filter residue is collected, and the filter residue is washed and dried to obtain a regenerated zinc oxide desulfurizer. Since the reaction is carried out in a closed environment with high temperature and high pressure, the insoluble zinc sulfide in the zinc oxide desulfurization waste agent is fully contacted with deionized water to undergo a chemical reaction, and the regenerated zinc oxide desulfurizer can be obtained in only one step reaction Therefore, the regeneration method of zinc oxide desulfurization waste agent described in the present invention has short steps, low energy consumption, time saving and labor-saving and convenient operation, which greatly reduces the regeneration cost of zinc oxide desulfurization waste agent and is beneficial to industrial production.

Description

technical field [0001] The invention relates to a method for regenerating waste zinc oxide desulfurization agent, which belongs to the field of preparation of zinc oxide desulfurization agent. technical background [0002] As a medium and high temperature desulfurizer, zinc oxide desulfurizer is widely used in synthetic ammonia, hydrogen production, synthetic methanol, coal chemical industry, petroleum refining and other industries because of its good desulfurization performance, easy use and stable performance. field plays an important role. During the desulfurization process, the zinc oxide desulfurizer chemically reacts with the sulfide in the material to be desulfurized to produce extremely stable zinc sulfide (its solubility product constant is as high as 1.2×10 -23 ), so that the gaseous sulfur in the material to be desulfurized is solidified to achieve the purpose of desulfurization, and the desulfurized zinc oxide is discarded due to loss of activity. Nearly 10,000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D53/96
Inventor 林科陈崇启林性贻江莉龙
Owner 福建三聚福大化肥催化剂国家工程研究中心有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com