A heavy-duty anti-corrosion, saline-alkali technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of short service life, harm, pollution to human beings, etc., and achieve the effect of inhibiting regeneration
Inactive Publication Date: 2014-10-15
张文彬
View PDF5 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to provide a kind of water-based zinc-free heavy-duty anticorrosion paint with rust in marine saline-alkali atmospheric area, to solve the problem that the existing solvent-based anti-corrosion coating has too short service life in chemical enterprises and marine saline-alkali area environment and causes pollution to the environment and damage to the environment. human hazard problem
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] Deionized water: 12%-26%;
[0020] Antifungal agent: BDBDK-1 0.1%;
[0021] Dispersant: 211 0.8%;
[0022] Defoamer: 202 0.5%;
[0023] Coalescing aid: 2.5% alcohol fat twelve;
[0024] Antifreeze: Propylene Glycol 2.5%;
[0025] Neutralizer: AMP-95 0.2%;
[0026] Wetting agent: X-405 0.2%;
[0027] Foam inhibitor: 902W 0.2%;
[0028] Leveling agent: 3580 0.1%;
[0029] Rust agent: schwego corrit (glycolic acid salt solution) 1%;
[0030] Corrosion inhibitor: asconium143 1%;
[0031] Anti-flash rust agent: STAR-102 2%;
[0032] Iron oxide red: S130 10%;
[0033] Aluminum tripolyphosphate: APW-2 7%;
[0034] Rutile titanium dioxide: R258 2%;
[0035] Wollastonite: 9%;
[0036] Wet Sericite: GA-2 8%;
[0037] Modified resin of vinyl tertiary carbonate copolymer: Hiqua3000 40%-50%:
[0038] Anti-swell thickener high shear BD-21 0.4%:
[0039] Anti-swell thickener low shear BD-20 0.3%.
Embodiment 2
[0041] Deionized water: 10%-25%;
[0042] Antifungal agent: BDBDK-1 0.1%:
[0043] Dispersant: 211 0.8%;
[0044] Defoamer: 202 0.5%;
[0045] Coalescing aid: 2.5% alcohol fat twelve;
[0046] Antifreeze: Propylene Glycol 2.5%;
[0047] Neutralizer: AMP-95 0.2%:
[0048] Wetting agent: PE-100 0.2%;
[0049] Foam inhibitor: 902W 0.2%;
[0050] Leveling agent: 3580 0.1%;
[0051] Rust agent: scnwego corrit (glycolic acid salt solution) 1%;
[0052] Corrosion inhibitor: asconium143 1%:
[0053] Anti-flash rust agent: STAR-102 2%;
[0054] Composite iron and titanium powder: W800 9%;
[0055] Aluminum Tripolyphosphate: APW-2 8%:
[0056] Rutile titanium dioxide: R258 3%;
[0057] Wollastonite: 9%;
[0058] Wet Sericite: GA-2 7%;
[0059] Modified resin of vinyl tertiary carbonate copolymer: Hiqua3000 45%-60%;
[0060] Anti-swelling thickener high shear BD-21 0.4%;
[0061] Anti-swell thickener low shear BD-20 0.3%.
[0062] When the iron plate is rusted, a primary...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a marine atmospheric saline alkali zone aqueous zinc strip rust free anticorrosive paint. The paint comprises 10-26% of deionized water, 0.1% of a mildew inhibitor, 0.8% of a dispersant, 0.5% of an antifoaming agent, 2.5% of a film forming assistant, 2.5% of an antifreeze agent, 0.2% of a neutralizer, 0.2% of a wetting agent, 0.2% of a foam inhibitor, 0.1% of a leveling agent, 1% of a corrosion agent, 1% of a corrosion inhibitor, 2% of a flash-rust inhibitor, 10% of iron oxide red or composite iron-titanium powder, 5-10% of aluminum triphosphate, 1-5% of rutile titanium dioxide, 9% of wollastonite, 5-10% of wet sericite, 40-60% of a vinyl versatate copolymer improved resin and 0.5-1% of a swelling reducing and thickening agent. The marine atmospheric saline alkali zone aqueous zinc strip rust free anticorrosive paint prepared by adopting a technical scheme in the invention has the advantages of omission of large rust removal engineering before enterprise coating, saving of huge cost for the enterprise, anticorrosion effect increase and very good market prospect.
Description
technical field [0001] The invention relates to coatings, in particular to a water-based zinc-free heavy-duty anti-corrosion paint with rust, in particular to a water-based zinc-free heavy-duty anti-corrosion paint in marine saline-alkali atmospheric regions. Background technique [0002] Water-based heavy-duty anti-corrosion paint refers to the paint used in harsh corrosive environments. It has a long service life and can adapt to more harsh environments. In the chemical environment and marine saline environment, the water-based heavy-duty anti-corrosion paint can be used for 10 or 15 years. The development direction of water-based heavy-duty anti-corrosion paint is environmental protection, energy saving, high performance and functionalization. It is the main direction for the future development of anti-corrosion coatings. In order to promote the upgrading and development of my country's new material technology and industry, it can make a significant contribution to human ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more