Compound functional agricultural machinery finishing powder coating and production process thereof

A powder coating and functional technology, applied in powder coatings, bulk chemical production, polyester coatings, etc., can solve the problems of cumbersome production process, not very easy, and many devices, so as to reduce production costs, reduce electric energy, The effect of lowering the baking temperature

Active Publication Date: 2014-10-22
ZHANG ZHOU SAN PAINTS
View PDF12 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this production process can overcome the steps of melting and mixing epoxy/polyester resins, extruding tablets, and crushing extruded tablets in the traditional powder coating product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound functional agricultural machinery finishing powder coating and production process thereof
  • Compound functional agricultural machinery finishing powder coating and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1

[0041] Preparation of polyester / acrylic resin composite 1: The polyester resin and acrylic resin are mixed at 7:3 by weight, and reacted in a high-temperature reactor at 150° C. for 1 hour.

[0042] Preparation of epoxy modified acrylic resin: methyl methacrylate, acrylic acid, octyl acrylate, styrene, hydroxypropyl acrylate, trimethylolpropane triacrylate as monomers, benzoyl peroxide as initiator, E-44 epoxy resin is a modifier, polymerized.

[0043] Preparation of nano composite cross-linking agent: 4,5-imidazole dicarboxylic acid and benzimidazole-5,6-dicarboxylic acid as sensitizing organic ligands, grafted to mesoporous SiO through covalent bonds 2 On the nano particles, a nano composite crosslinking agent is prepared.

[0044] The glass powder used is VX-SP imported from Japan.

[0045] The polyester resin adopts 9855 polyester resin supplied by Baotian New Materials.

[0046] The raw material components of the powder coating are shown in Table 1, and they are ...

Example Embodiment

[0049] Example 2

[0050] This embodiment is basically the same as embodiment 1, the difference lies in:

[0051] When preparing polyester / acrylic resin composite 2, react for 1.5 hours.

[0052] The method of CN103467714A was used to prepare high hydroxyl polyester resin.

[0053] The crosslinking agent is trimethylolpropane.

[0054] The nanometer glass powder is Jingshan nanometer glass powder JLH-T90 produced and sold by Shenzhen Jinlonghui Industrial Co., Ltd.

[0055] In addition, the additives are different, see Table 1 for details.

Example Embodiment

[0056] Example 3

[0057] This embodiment is basically the same as embodiment 1, the difference is that the additives are different, the temperature of the supercritical fluid kettle is set to 120°C, the temperature is kept constant for 5 minutes after heating to the set temperature, and the rotation speed of the shearing element is 150 rpm , The shear mixing time is 10 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a compound functional agricultural machinery finishing powder coating and a production process thereof. The powder coating comprises the following components in parts by weight: 2-8 parts of a polyester/acrylic resin compound, 30-50 parts of polyester resin, 12-22 parts of epoxy modified acrylic resin, 20-35 parts of nano glass powder, 1-5 parts of a cross-linking agent and 1-2.5 parts of an assistant. A supercritical carbon dioxide fluid method is adopted in the production process. The powder coating is corrosion-proof, rust-proof and excellent in weather resistance, the production process of the powder coating is low in energy consumption and high in efficiency, and the production processing temperature is reduced.

Description

technical field [0001] The invention relates to the technical field of powder coatings for agricultural machinery, and particularly discloses a composite functional agricultural machinery finishing powder coating and a production process thereof. Background technique [0002] As powder coatings become more and more important in the coatings industry, powder coatings have achieved rapid development in recent years. At the same time, because the powder coating formula does not contain organic solvents such as VOC, benzene, toluene, xylene, etc. , is an environmentally friendly product with excellent environmental benefits. Epoxy resin has good anti-corrosion performance, and acrylic resin has good weather resistance. In recent years, powder coatings involving epoxy or acrylic resin have also developed rapidly. For example, the authorized announcement patent CN1202184C discloses a thermosetting scratch-resistant outdoor low-gloss powder Coating, its main components include epo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/02C09D151/08C09D5/03C09D7/14C09D7/80
CPCY02P20/54
Inventor 许绍凰项椿烨蓝文烽
Owner ZHANG ZHOU SAN PAINTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap