A steel-iron-based cermet composite and its sintering and welding integration process

An iron-based metal, cermet technology, applied in the direction of metal layered products, chemical instruments and methods, layered products, etc. Large-scale promotion and use, solving welding problems, and the effect of simple process

Active Publication Date: 2017-01-04
南京彬华新材料有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Iron-based cermets are much more expensive than steel
Many application fields are very suitable for the application of iron-based cermets, but the overall iron-based cermets are too expensive, which restricts the promotion and application of iron-based cermets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A steel-iron-based cermet composite and its sintering and welding integration process
  • A steel-iron-based cermet composite and its sintering and welding integration process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] see figure 1 : A kind of steel and iron-based metal-ceramic composite body and its sintering and welding integration process, wherein the composite body is successively high ceramic layer, high metal layer, and metal layer from outside to inside, and the specific formula of the high ceramic layer is 50wt % of 400 mesh TiC powder, Fe powder is 39wt%, Mo powder is 1wt%, Ni powder is 3wt%, Cr powder is 7wt%; the transition layer is a high metal layer, and the specific formula is 25wt% 400 mesh TiC powder, Fe Powder is 62wt%, Mo powder is 1wt%, Ni powder is 4wt%, Cr powder is 8wt%; the particle size of the above metal powders is 200 mesh; the complex sintering and welding integration process is as follows, 1) After the good powders are mixed evenly, they pass through the mold, and the upper surface of the steel 3 is first laid with a high metal layer 2, also called a high metal transition layer, and then a high ceramic layer 1 is laid, and pressed to form an outer high cera...

Embodiment 2

[0021] Example 2 ： see figure 1, a steel and iron-based cermet composite body and its sintering and welding integration process, wherein the composite body consists of a high ceramic layer 1, a high metal layer 2, and a metal layer 3 from outside to inside, and the specific details of the high ceramic layer The formula is: 40wt% 400 mesh TiC powder, 47wt% Fe powder, 1wt% Mo powder, 4wt% Ni powder, 8wt% Cr powder; 400 mesh TiC powder of 20wt% inner layer formula, Fe powder is 67wt%, Mo powder is 1wt%, Ni powder is 4wt%, Cr powder is 8wt%; the particle size of the above metal powders are all 200 mesh. The details of the complex sintering and welding integration process are as follows: 1) After mixing the prepared powders evenly, pass through the mold, and lay the high metal layer 2 on the upper surface of the steel 3, also called the high metal transition layer, and then lay the High ceramic layer 1, pressed into a composite blank with an outer high ceramic layer, a high me...

Embodiment 3

[0022] Example 3 ： see figure 1 , a steel and iron-based cermet composite body and its sintering and welding integration process, wherein the composite body consists of a high ceramic layer 1, a high metal layer 2, and a metal layer 3 from outside to inside, and the specific details of the high ceramic layer The formula is: 30wt% 400 mesh TiC powder, 57wt% Fe powder, 2wt% Mo powder, 4wt% Ni powder, 7wt% Cr powder; 400 mesh TiC powder of 15wt% inner layer formula, Fe powder is 72wt%, Mo powder 2wt%, Ni powder 4wt%, Cr powder 7wt%; the particle size of the above metal powders are all 200 mesh. The details of the complex sintering and welding integration process are as follows: 1) After mixing the prepared powders evenly, pass through the mold, and lay the high metal layer 2 on the upper surface of the steel 3, also called the high metal transition layer, and then lay the High ceramic layer 1, pressed into a composite blank with an outer high ceramic layer, a high metal tran...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
widthaaaaaaaaaa
depthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a steel and iron-based metal-ceramic composite body. The composite body consists of a high ceramic layer, a high metal layer and a metal layer in sequence from the outside to the inside. The specific formula of the high ceramic layer is 30wt%-70wt% 400 mesh TiC powder, Fe powder is 35wt%-60wt%, Mo powder is 1wt%-3wt%, Ni powder is 2wt%-5wt%, Cr powder is 6wt%-8wt%; the transition layer is a high metal layer, specifically The formula is 15wt%-25wt% of 400 mesh TiC powder, 60wt%-75wt% of Fe powder, 1wt%-2wt% of Mo powder, 3wt%-5wt% of Ni powder, and 6wt%-9wt% of Cr powder.

Description

technical field [0001] The invention relates to a metal-ceramic composite body, in particular to a sintering and welding integrated process of steel and iron-based metal-ceramic composite body. Background technique [0002] Tungsten is a rare metal widely used in gun manufacturing, metal cutting blades, drill bits, superhard dies, wire drawing dies, etc. Tungsten has a wide range of uses, involving mining, metallurgy, machinery, construction, transportation, electronics, chemical industry, Light industry, textile, military industry, aerospace, science and technology, various industrial fields. Cobalt is not only an important metal for making alloy steel, but also an important raw material for various advanced pigments. Due to the limitation of tungsten and cobalt resources, many western countries focus on the development of tungsten-free cobalt cemented carbide with TiC ceramics as the reinforcement phase and nickel and nickel alloy as the binder phase, and have been mass-p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/04B32B15/01C22C29/10C22C38/44B22F7/04
Inventor 王华彬
Owner 南京彬华新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap