A kind of natural charm antique ceramic tile with furnace slag as main material and manufacturing method thereof
A technology of hearth slag and tiles, which is applied in the field of antique tiles and its manufacture, to achieve the effects of reducing pollution, high wear resistance and stain resistance, and clear texture
Active Publication Date: 2015-12-30
内蒙古建亨能源科技有限公司
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] The purpose of the present invention is to overcome the defects of the existing natural charm antique tiles and their manufacturing methods, and provide a kind of ceramic tile with good decorative effect, fine texture, strong three-dimensional effect of lines, compact and uniform structure, strong wear resistance, and good antifouling performance. Antique ceramic tile with natural charm and its manufacturing method with furnace slag as main material, easy to maintain, moisture-proof and long service life
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0040] Below in conjunction with specific embodiment the present invention is described in further detail:
[0041] see table below
[0042]
[0043]
[0044]
[0045] According to the process steps of the above-mentioned embodiment: raw material procurement → formula formulation → batching ball mill → slurry → slurry stale → sieving iron removal → spray drying → powder → powder stale → distribution of powder → cloth forming → drying → glaze spraying →Glaze pouring→glazing→glazing→printing→firing→edging→grading→packaging→warehousing; to make natural charm antique tile products with furnace slag as the main material.
[0046] In the manufacturing process of the present invention, the specific gravity of the glaze after the antique tiles are ball-milled is: 1.78-1.86kg / m 3 ; Glaze 250 mesh sieve remaining 100 grams of glaze slurry sieve content is: 0.1 ~ 0.2%.
[0047] The amount of glaze in grams of the blank after the glaze line is sprayed: 160±20g / 600mm 2 .
[00...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| flexural strength | aaaaa | aaaaa |
| shrinkage | aaaaa | aaaaa |
| water absorption | aaaaa | aaaaa |
Login to View More
Abstract
A natural romantic charm antique-finished tile mainly composed of hearth slag and a manufacture method thereof are provided. The blank of the tile is mainly composed of the following raw materials in percentage by weight: 50 to 55% of hearth slag, 10 to 20% of white sandstone, 13 to 25% of clay, 2 to 5% of bentonite, 5 to 20% of coal gaugue, and 5 to 20% of feldspar. The glaze is mainly composed of the following raw materials in percentage by weight: 25 to 40% of potassium feldspar, 10 to 26% of calcite, 5 to 10% of barium carbonate, 2 to 5% of zirconium silicate, 3 to 8% of aluminum oxide, 2 to 5% of zinc oxide, 10 to 20% of calcined talcum, 3 to 10% of calcined kaolin, and 5 to 10% of quartz. The technology comprises the following steps: purchasing raw materials, determining the formula, ball-grinding the ingredients, preparing slurry, aging the slurry, sieving to remove iron, spray-drying so as to obtain a powder material, aging the powder material, delivering the powder material, moulding into cloth, drying, spraying glaze, pouring glaze, spreading glaze, printing, burning to finish, polishing the edges, dividing into different grades, packaging, and finally storing in warehouse. The tile is mainly composed of hearth slag, and the goals of energy saving and discharge reducing are achieved.
Description
technical field [0001] The invention relates to an antique ceramic tile and a manufacturing method thereof, in particular to a natural charm antique ceramic tile with furnace slag as the main material and a manufacturing method thereof. Background technique [0002] In modern society, the shapes of buildings are becoming more and more diverse, and the functions are becoming more and more perfect. High-tech is being used more and more in the construction field. All products are developed to meet market demand. From the early gorgeous decorative effects to the present It is becoming more and more natural, elegant, and has individual elements, and it needs to be durable, environmentally friendly, and keep pace with the market demand of the times. [0003] Ceramic products are characterized by their strong adaptability, high density, wide variety, rich colors, good decorative effects and easy maintenance. When they are used in suitable environments, due to the maturity of produc...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information