A resin-based friction material

A friction material and resin-based technology, applied in the field of friction materials, can solve the problems of complex production process, special raw materials, complex components, etc., and achieve the effects of low wear rate, stable friction coefficient and good thermal recession resistance.

Active Publication Date: 2015-11-04
杭州泰明顿摩擦材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned patents have defects such as complex production process, special raw materials or complex components.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A resin-based friction material
  • A resin-based friction material
  • A resin-based friction material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] According to the mass percentage, it contains the following components: 10% resin, 3% aramid pulp, 8% glass fiber, 10% potassium titanate whisker, 12% wollastonite, 6% graphite (particle size 120~200 mesh), three Antimony sulfide 4%, alumina 1.5% (particle size 320-400 mesh), zirconium silicate 1% (particle size 320-400 mesh), expanded vermiculite 6% (particle size 80-120 mesh), and the balance barium sulfate.

[0022] According to the resin-based friction material made by the formula of the present invention, when the friction and wear test is carried out at 250°C, the coefficient of friction (μ) and the wear rate (v) are respectively 0.34 and 0.29×10 -7 cm 3 / (N m), when the friction and wear test is carried out at 350°C, the friction coefficient (μ) and wear rate (v) are 0.31 and 0.40×10 respectively -7 cm 3 / (N·m).

Embodiment 2

[0024] According to the mass percentage, it contains the following components: 10% resin, 3% aramid pulp, 8% glass fiber, 10% potassium titanate whisker, 12% wollastonite, 6% graphite (particle size 80~120 mesh), three Antimony sulfide 4%, alumina 1.5% (particle size 320-400 mesh), zirconium silicate 1% (particle size 200-320 mesh), expanded vermiculite 6% (particle size 40-80 mesh), and the balance barium sulfate.

[0025] According to the resin-based friction material made by the formula of the present invention, when the friction and wear test is carried out at 250°C, the coefficient of friction (μ) and the wear rate (v) are respectively 0.37 and 0.26×10 -7 cm 3 / (N m), when the friction and wear test is carried out at 350°C, the coefficient of friction (μ) and wear rate (v) are 0.27 and 0.79×10 -7 cm 3 / (N·m).

Embodiment 3

[0027] According to the mass percentage, it contains the following components: 10% resin, 3% aramid pulp, 8% glass fiber, 10% potassium titanate whisker, 12% wollastonite, 6% graphite (particle size 120~200 mesh), three Antimony sulfide 4%, alumina 1.5% (particle size 200-320 mesh), zirconium silicate 1% (particle size 200-320 mesh), expanded vermiculite 6% (particle size 40-80 mesh), and the balance barium sulfate.

[0028] According to the resin-based friction material made by the formula of the present invention, when the friction and wear test is carried out at 250°C, the coefficient of friction (μ) and the wear rate (v) are respectively 0.39 and 0.81×10 -7 cm 3 / (N m), when the friction and wear test is carried out at 350°C, the friction coefficient (μ) and wear rate (v) are 0.28 and 0.74×10 -7 cm 3 / (N·m).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a resin-based friction material comprising the components of, by mass, 8-12% of resin, 2-4% of aramid fiber pulp, 7-9% of glass fiber, 8-12% of potassium titanate whisker, 10-12% of wollastonite, 5-7% of graphite, 3-5% of antimony trisulfide, 1-2% of alumina, 0.5-1.5% of zirconium silicate, 5-7% of expanded vermiculite, and balance of barium sulfate. A total amount of the components of the friction material is 100%. The friction material has the following advantages: the raw material sources of the resin-based friction material are wide, and can be common industrial products; and a preparation process is simple. The resin-based friction material has stable friction coefficient (mu), low wear rate (v), and good heat fade resistance under high temperature.

Description

technical field [0001] The invention relates to the field of friction materials, in particular to a resin-based friction material for automobiles. Background technique [0002] In recent years, with the rapid development of my country's automobile technology, people pay more and more attention to the safety and comfort of automobiles. Friction material is the key material for brakes and clutches. It is mainly composed of fillers, fibers and binders. Among them, the filler has a great influence on its physical and mechanical properties and wear performance. Traditional friction materials will thermally decompose when the working temperature exceeds 250°C, resulting in a significant decrease in the friction coefficient and a significant increase in the wear rate, seriously affecting people's driving safety. Therefore, the present invention improves the performance of the resin-based friction material in a high-temperature environment from the perspective of the filler and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/14
Inventor 姚冠新牛华伟王玉玲陶飞
Owner 杭州泰明顿摩擦材料有限公司