Method for preparing polymer protected fluorescent copper nanoclusters

A nanocluster and polymer technology, applied in nanotechnology, chemical instruments and methods, luminescent materials, etc., can solve the problems of less research on Cu nanoclusters, easy oxidation, large size of Cu nanoparticles, etc. Stable performance and mild reaction conditions

Active Publication Date: 2014-11-12
WUUHAN NUOWEIKAI BIOLOGICAL MATERIAL CO LTD +1
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current research on transition metal nanoclusters at the subnanometer scale mainly focuses on the noble metals Au and Ag, while relative

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing polymer protected fluorescent copper nanoclusters
  • Method for preparing polymer protected fluorescent copper nanoclusters

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for preparing polymer-protected fluorescent copper nanoclusters, comprising the steps of:

[0019] (1) Dissolve 500 μL of polyethyleneimine (PEI) solution with a concentration of 0.1 g / mL and 300 μL of 4-hydroxyethylpiperazineethanesulfonic acid (HEPES) solution with a concentration of 10 mmol / l in 2020 μL of pure water , stir for 5min;

[0020] (2) Add 150 μL of copper nitrate solution with a concentration of 100 mmol / l to the solution in step (1), and stir for 20 min;

[0021] (3) Add 30 μL of formaldehyde to the solution in step (2) under magnetic stirring, and heat at 50° C. for 20 min to obtain a blue solution, which is a polymer-protected fluorescent copper nanocluster. The electron microscope patterns of the polymer-protected fluorescent copper nanoclusters are as follows: figure 1 As shown, the fluorescence spectrum is as figure 2 shown.

Embodiment 2

[0023] A method for preparing polymer-protected fluorescent copper nanoclusters, comprising the steps of:

[0024] (1) 800 μL of chitosan solution with a concentration of 0.1 g / mL and 500 μL of 10 mmol / l 4-hydroxyethylpiperazineethanesulfonic acid (HEPES) solution were dissolved in 1390 μL of pure water and stirred for 20 min;

[0025] (2) Add 300 μL of 100 mmol / l copper nitrate solution to the solution in step (1), and stir for 5 min;

[0026] (3) Add 10 μL of formaldehyde to the solution in step (2) under magnetic stirring, and heat at 70° C. for 50 min to obtain a blue solution, which is a polymer-protected fluorescent copper nanocluster.

Embodiment 3

[0028] A method for preparing polymer-protected fluorescent copper nanoclusters, comprising the steps of:

[0029] (1) Dissolve 300 μL of lysine solution with a concentration of 0.1 g / mL and 600 μL of 4-hydroxyethylpiperazineethanesulfonic acid (HEPES) solution with a concentration of 10 mmol / l in 1980 μL of pure water, and stir for 10 min;

[0030] (2) Add 100 μL of copper nitrate solution with a concentration of 100 mmol / l to the solution in step (1), and stir for 15 min;

[0031] (3) Add 20 μL of formaldehyde to the solution in step (2) under magnetic stirring, and heat at 80° C. for 80 min to obtain a blue solution, which is a polymer-protected fluorescent copper nanocluster.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing polymer protected fluorescent copper nanoclusters. The method is characterized by comprising the following steps of 1, dissolving a polymer solution and a 4-(2-hydroxyerhyl) piperazine-1-erhaesulfonic acid solution in a proper amount of pure water, and stirring to blend uniformly; 2, adding a cupric nitrate solution into the solution in the step 1, and continuously stirring; 3, adding a proper amount of methanol into the solution in the step 2 and heating at the temperature of between 50 and 90DEG C for 10 to 100 minutes to obtain a blue polymer protected fluorescent copper nanocluster solution. According to the method, a polymer is taken as a stabilizer, the methanol is taken as a reducing agent, 4-(2-hydroxyerhyl) piperazine-1-erhaesulfonic acid is taken as an auxiliary, cupric nitrate is taken as a Cu source, and reaction conditions are mild. The copper nanoclusters synthesized by the method have the advantages of low price, stable performance, no toxicity and the like, serve as a potential fluorescent label to be expectedly applied to the fields such as optical imaging, biomarkers and chemical sensors, and have wide application prospect in the fields such as environment analysis, biochemical analysis and food safety.

Description

technical field [0001] The invention belongs to the field of nanometer material preparation, and relates to a new method for preparing highly stable polymer-protected fluorescent copper nanoclusters. Background technique [0002] Clusters are relatively stable aggregates composed of several to thousands of atoms, molecules, and ions through physical and chemical binding forces, and their spatial dimensions range from several angstroms to hundreds of angstroms. Because nanoclusters have a large proportion of surface atoms, there are significant differences between the environment of this part of atoms and the atoms inside the cluster, making nanoclusters have a series of physical properties different from single atoms, molecules, and bulk solid materials. And chemical properties, such as the extremely high specific surface makes it have exceptionally high chemical activity and catalytic performance, the quantum size effect and nonlinear effect of light, the geometric size eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/24B82Y40/00C09K11/58C09K11/02
Inventor 宋功武王仁宗何瑜刘裕钟亚平葛伊利朱晶晶
Owner WUUHAN NUOWEIKAI BIOLOGICAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap