Method for extracting chromium from chromium-containing waste liquor

A technology of waste liquid and ferrochrome, which is applied in the field of comprehensive utilization of sewage resources, can solve the problems of high cost and low efficiency, and achieve the effects of convenient operation, cost reduction, and efficient separation and recovery

Active Publication Date: 2014-11-19
CENT SOUTH UNIV
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the deficiencies in the various methods for treating chromium-containing wastewater in the prior art, mainly reflected in defects such as high cost and low efficiency, the purpose of the present invention is to provide a method that can quickly, efficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for extracting chromium from chromium-containing waste liquor
  • Method for extracting chromium from chromium-containing waste liquor
  • Method for extracting chromium from chromium-containing waste liquor

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Example 1

[0037] Treatment of Cr by this process 3+ The chromium-containing waste liquid with a mass concentration of 1.66g / L, the used laterite-nickel ore leaching solution contains 20.24g / L of iron.

[0038] Preparation of magnetic fluid: Pulverize magnetite powder with a purity of more than 90% to below 38 microns, sieve through a 400-mesh standard Taylor sieve, and use the sieved product as a magnetic crystal nucleus. The ore (containing more than 55wt% iron) is mixed in a mass ratio of 5:1, and ground in a ceramic ball mill for 30min, so that the hematite is coated on the surface of the magnetic crystal nucleus, and the magnetic material and water are in a mass ratio of 1:2. Proportional mixing, namely magnetic fluid.

[0039] Add 5g / L magnetic fluid to the reaction kettle containing 0.5L distilled water and stir, add an appropriate amount of dilute H 2 SO 4solution so that the pH of the solution is around 3. Mix the laterite nickel ore sulfuric acid leachin...

Example Embodiment

[0042] Example 2

[0043] Treatment of Cr by this process 3+ Chromium-containing waste liquid with mass concentration of 5.28g / L, laterite nickel ore leaching solution Fe 3+ The mass concentration is 20.24g / L.

[0044] Preparation of magnetic fluid: Pulverize magnetite powder with a purity of more than 90% to below 38 microns, sieve through a 400-mesh standard Taylor sieve, and use the sieved product as a magnetic crystal nucleus. The ore (containing more than 55wt% iron) is mixed in a mass ratio of 5:1, and ground in a ceramic ball mill for 35min, so that the hematite is coated on the surface of the magnetic crystal nucleus, and the magnetic material and water are in a mass ratio of 1:3. Proportional mixing, namely magnetic fluid.

[0045] Add 8g / L magnetic fluid to the reaction kettle containing 0.5L distilled water and stir, add an appropriate amount of dilute H 2 SO 4 solution so that the pH of the solution is around 3. The laterite nickel ore leaching solution and t...

Example Embodiment

[0049] Example 3

[0050] Treatment of Cr by this process 3+ Chromium-containing waste liquid with mass concentration of 10.64g / L, laterite nickel ore leaching solution Fe 3+ The mass concentration is 20.24g / L.

[0051] Preparation of magnetic fluid: Pulverize magnetite powder with a purity of more than 90% to below 38 microns, sieve through a 400-mesh standard Taylor sieve, and use the sieved product as a magnetic crystal nucleus. The ore (containing more than 55% iron) is mixed in a mass ratio of 4:1, and ground in a ceramic ball mill for 40 minutes, so that the hematite is coated on the surface of the magnetic crystal nucleus, and the magnetic material and water are in a mass ratio of 1:2.5. Proportional mixing, namely magnetic fluid.

[0052] Add 10g / L magnetic fluid to the reaction kettle containing 0.5L distilled water and stir, add an appropriate amount of dilute H 2 SO 4 solution so that the pH of the solution is around 2.7. The laterite nickel ore leaching solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for extracting chromium from chromium-containing waste liquor. According to the method, magnetite powder is taken as a magnetic crystal nucleus, a compound which mainly comprises chromium and iron is generated by reacting chromium-containing waste water with laterite-nickel ore acid leach liquor, and the compound is wrapped on the surface of the magnetic crystal nucleus through adsorption and then separated by utilizing the magnetism of the magnetic crystal nucleus. The method disclosed by the invention can be used for preparing chromium-rich iron slag by fast, efficiently and selectively extracting the chromium from the chromium-containing waste liquor by adopting low cost and sufficiently recovering the iron resources contained in the laterite-nickel ore acid leach liquor, is simple in process and convenient to operate and meets the requirement for industrialized production.

Description

technical field [0001] The invention relates to a method for extracting chromium from chromium-containing waste liquid, and belongs to the technical field of comprehensive utilization of sewage resources. Background technique [0002] In the process of material surface treatment, chromium electroplating, metal passivation, coloring and cleaning will all produce chromium-containing wastewater. If it is directly discharged, it will not only waste resources, but also pollute the environment and seriously endanger human health. The national wastewater discharge standard stipulates that the maximum allowable concentration of residual Cr(VI) in wastewater is 0.5mg / L, and the total chromium is 1.2mg / L. Therefore, it is very necessary to treat electrochrome plating wastewater. At present, the treatment of chromium-containing wastewater at home and abroad mainly adopts chemical reduction method, electrochemical method, ion exchange method, and activated carbon adsorption method. In a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F1/48C02F1/52C22B7/00C22B34/32C02F101/22
CPCY02P10/20
Inventor 孙伟韩海生唐鸿鹄刘文莉吕德良岳彤
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap