Self-crosslinking polymer dust suppressant and preparation method

A technology of polymer and dust suppressant, applied in the field of environmental pollution control, can solve the problems of single function, high price and toxicity.

Active Publication Date: 2017-02-15
廊坊浩北化工有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Various chemical dust suppressants have also been developed, but they all generally have single functions or high prices, and have disadvantages such as toxicity, corrosion, refractory degradation, and secondary pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Add 10 parts of ionic water to the reaction kettle, add 0.25 parts of disodium alkyl diphenyl ether disulfonate (DSB), stir, heat, and raise the temperature to 84°C;

[0021] (2) Add 30 parts of deionized water to the pre-emulsification tank, add 0.5 parts of disodium alkyl diphenyl ether disulfonate (DSB), 0.75 parts of allyloxy nonylphenol polyoxyethylene ether ammonium sulfate (DNS-86) , under stirring, add 20 parts of styrene (St), 18 parts of ethyl acrylate (EA), 6 parts of 2-ethylhexyl acrylate (2-EHA), 3 parts of acrylic acid (AA), 3 parts of acrylamide (AM) , 1.5 parts of diacetone acrylamide (DAAM), stirred rapidly for 30-60 minutes to make a pre-emulsion;

[0022] (3) Dissolve 0.3 part of sodium persulfate in 4.7 parts of deionized water to prepare initiator solution;

[0023] (4) Add 1.2 parts of ADH to 5 parts of deionized water, stir, dissolve, and prepare an ADH solution;

[0024] (5) The temperature of the reactor rises to 84°C, add 10% of the pre-e...

Embodiment 2

[0026] (1) Add 10 parts of ionic water to the reaction kettle, add 0.25 parts of disodium alkyl diphenyl ether disulfonate (DSB), stir, heat, and raise the temperature to 84°C;

[0027] (2) Add 30 parts of deionized water to the pre-emulsification tank, add 0.75 parts of disodium alkyl diphenyl ether disulfonate (DSB), 0.5 parts of allyloxy nonylphenol polyoxyethylene ether ammonium sulfate (DNS-86) , under stirring, add 20 parts of styrene (St), 20 parts of ethyl acrylate (EA), 2 parts of acrylic acid (AA), 4 parts of acrylamide (AM), 1.5 parts of diacetone acrylamide (DAAM), and stir rapidly for 30~ 60 minutes to make a pre-emulsion;

[0028] (3) 0.3 parts of sodium persulfate are dissolved in 4.7 parts of deionized water to prepare initiator solution;

[0029] (4) Add 1.2 parts of ADH to 5 parts of deionized water, stir, dissolve, and prepare an ADH solution;

[0030] (5) The temperature of the reactor rises to 84°C, add 10% of the pre-emulsion, and at the same time add 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a self-crosslinking macromolecular dust suppressant and a preparation method thereof and belongs to the technical field of environmental pollution improvement and particularly relates to the self-crosslinking macromolecular dust suppressant and the preparation method thereof. The self-crosslinking macromolecular dust suppressant is characterized by being prepared by taking styrene (St) as a hard monomer, ethyl acrylate (EA), 2-ethyl hexyl acrylate (2-EHA) as a soft monomer, introducing acrylic acid (AA) and acrylamide (AM) as a functional monomer, diacetone-acryloamide (DAAM) and adipic dihydrazide (ADH) as a self-crosslinking monomer, taking persulfate as an initiator, alkyl diphenyl ether disulfonate (DSB) as an emulsifier and allyloxyl nonylphenol ether ammonium sulfate (DNS-86) as a reactive emulsifier by virtue of a seed emulsion polymerization method. The self-crosslinking macromolecular dust suppressant provided by the invention has excellent wear resistance, water resistance, resistance to acid and base and corrosion resistance and is an environment-friendly green product.

Description

technical field [0001] The invention belongs to the technical field of environmental pollution control, and specifically relates to a self-crosslinking polymer dust suppressant and a preparation method thereof, which are mainly used for controlling coal powder, mineral powder, muck transportation, municipal construction, open-pit mining, and bare land Wait for the flying of dust. Background technique [0002] With the development of industry and the improvement of people's living standards, environmental protection and effective use of resources have become the focus of attention of all countries in the world. Dust pollution is one of the world's public hazards. The dust pollution caused by open dusty sites such as various municipal engineering sites, material storage yards, demolition sites and other bare grounds has greatly endangered people's normal life and health, and destroyed the ecological environment. environment. According to data, dust pollution has become a com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F220/56C08F222/38C08J3/24
Inventor 梁文庆
Owner 廊坊浩北化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com