Special material for permanent antistatic flexible PE (polyethylene) pipes

A polyethylene pipe, antistatic technology, applied in the field of composite materials, can solve the problems of loss of antistatic ability, constant impact strength, low flexural modulus, etc., to achieve good environmental adaptability, reduced modulus, and good compatibility Effect

Active Publication Date: 2015-01-07
YANGZHOU UNIV
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a special material for permanent antistatic flexible polyethylene pipes, to solve the problem of the polymer-based conductive carbon black composite system prepared by the existing general process, whose conductivity decreases sharply with the increase of temperature, and at 70 The problem of losing antistatic ability above ℃, through the invention, while maintaining the excellent mechanical properties of PE-RT pipes, that is, the tensile strength is 14.0MPa, the bending strength is 12.3MPa, the bending modulus is 325.5MPa, and the impact strength of the cantilever beam is constant. , the composite material has a lower flexural modulus, the pipe can be bent into a roll within a certain radius, and has permanent antistatic properties, good environmental adaptability, acid and alkali corrosion resistance, and good thermal creep resistance. Can maintain antistatic performance from room temperature to 125°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special material for permanent antistatic flexible PE (polyethylene) pipes
  • Special material for permanent antistatic flexible PE (polyethylene) pipes
  • Special material for permanent antistatic flexible PE (polyethylene) pipes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1, a special material for permanent antistatic flexible polyethylene pipes, the parts by weight of each component are: 100 parts of medium density polyethylene PE-RT, 25 parts of EVA carrier conductive carbon black masterbatch, thermoplastic elastic Body POE 5.5 parts, dispersant EBS 1.5 parts, antioxidant 1010 0.2 parts, antioxidant 168 0.2 parts, release agent zinc stearate 0.2 parts, liquid paraffin 0.2 parts.

[0033] The medium-density polyethylene PE-RT base material adopts a melt index MFR=0.6-0.8g / 10min, a test pressure load of 2.16 kg, and a temperature of 195°C.

[0034] Melt index is a parameter to measure the fluidity of polymers, denoted as MFR, defined as the polymer weight of thermoplastic resin passing through the standard pore diameter within 10 minutes under specified temperature and pressure load, the unit is g / 10min.

[0035] The preparation method comprises the following steps:

[0036] 1) Dry 1.5Kg medium density polyethylene PE-RT bas...

Embodiment 2

[0042] Example 2, a special material for permanent antistatic flexible polyethylene pipes, the parts by weight of each component are: 100 parts of medium density polyethylene PE-RT, 30 parts of EVA carrier conductive carbon black masterbatch, thermoplastic elastic Body POE-g-MAH 3 parts, dispersant EBS 1.5 parts, antioxidant 1010 0.2 parts, antioxidant 168 0.2 parts, release agent zinc stearate 0.2 parts, methyl silicone oil 0.2 parts.

[0043]The medium-density polyethylene PE-RT base material adopts a melt index MFR=0.6-0.8g / 10min, a test pressure load of 2.16 kg, and a temperature of 195°C.

[0044] Melt index is a parameter to measure the fluidity of polymers, denoted as MFR, defined as the polymer weight of thermoplastic resin passing through the standard pore diameter within 10 minutes under specified temperature and pressure load, the unit is g / 10min.

[0045] The preparation method comprises the following steps:

[0046] 1) Dry 1.5Kg medium-density polyethylene PE...

Embodiment 3

[0052] Example 3, a special material for permanent antistatic flexible polyethylene pipes, the parts by weight of each component are: 100 parts of medium density polyethylene PE-RT, 30 parts of LLDPE carrier conductive carbon black masterbatch, thermoplastic elastic Body POE 4 parts, dispersant EBS 1.5 parts, antioxidant 1010 0.2 parts, antioxidant 168 0.2 parts, release agent zinc stearate 0.2 parts, liquid paraffin 0.2 parts.

[0053] The medium-density polyethylene PE-RT base material adopts a melt index MFR=0.6-0.8g / 10min, a test pressure load of 2.16 kg, and a temperature of 195°C.

[0054] Melt index is a parameter to measure the fluidity of polymers, denoted as MFR, defined as the polymer weight of thermoplastic resin passing through the standard pore diameter within 10 minutes under specified temperature and pressure load, the unit is g / 10min.

[0055] The preparation method comprises the following steps:

[0056] 1) Dry 1.5Kg medium-density polyethylene PE-RT bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a special material for permanent antistatic flexible PE (polyethylene) pipes. 100 parts of PE-RT resin by weight, 20-35 parts of a conductive master-batch by weight, 2-8 parts of a thermoplastic elastomer by weight, 1-5 parts of a dispersing agent by weight, 0-0.5 part of an antioxidant by weight, 0-0.5 part of a release agent by weight and 0-0.5 part of a liquid lubricant by weight are evenly mixed in a high-speed stirrer, then extruded by twin screws, cooled with water and granulated, and the machining temperature is in a range of 180-195 DEG C. The special material for the pipes is dried, then extruded to form the pipes, cooled and drawn to be prepared into finished products. Compared with the prior art, the special material has the advantages that the antistatic property is good, the permanent antistatic effect is realized, the tensile strength, the flexural strength and the impact strength are equivalent to those of pure PE-RT, the flexural modulus is lower, the advantage of the flexibility of the PE pipes is kept, the special material is convenient to transport, construct and install, good in environment resistance and low in cost, and the volume resistivity of the special material for the permanent antistatic flexible PE pipes can be stabilized at 106 ohm / cm.

Description

technical field [0001] The invention relates to a special material for permanent antistatic bendable polyethylene pipes, which belongs to the technical field of composite materials. Background technique [0002] Under the call of "replacing steel with plastic", plastics are more and more widely used. However, plastics have extremely high electrical resistance. During use, contact, friction, collision, etc. will accumulate static charges on the surface of plastic products. Moreover, the generated static charge is difficult to transfer, and when it accumulates to a certain extent, it will bring potential safety hazards. [0003] PE-RT is heat-resistant polyethylene. It adopts the method of copolymerization of ethylene and octene, and obtains a unique molecular structure by controlling the number and distribution of side chains to improve the heat resistance and toughness of PE. PE-RT pipe has good stability, aging resistance, long service life, excellent creep resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L51/06C08K13/02C08K3/04C08J3/22
CPCC08K2201/001C08L23/06C08L2201/04C08L2201/08C08L2203/18C08L2205/025C08L2205/035C08L2207/04C08L23/0853C08L23/0815C08L91/06C08K13/02C08K3/04C08L51/06C08L83/04
Inventor 张明于金平曹振东
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com