A kind of acidic transparent silicone weather-resistant sealant for construction

A construction and sealant technology, applied in the direction of adhesives, adhesive additives, dyed low-molecular-weight organic compounds, etc., can solve the problems of harsh sizing environment, yellowing of colloids, and high surface cleaning requirements of bonded materials

Active Publication Date: 2016-01-27
ZHEJIANG TIME NEW MATERIAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The research on silicone sealants in my country started later than in Europe and the United States, and foreign high-end products have long occupied the dominant position in the market. Domestic silicone sealants have been able to compete with similar foreign products in terms of mechanical properties, hydrophobicity and air permeability, but in terms of weather resistance and There is still a big gap between the application and installation compared with foreign countries, which is mainly reflected in the fact that the colloids of the same kind of domestic products have been used on large glass curtain walls for one year, and the yellowing phenomenon has occurred, especially when used in humid and hot coastal areas, the yellowing phenomenon is more serious; On the one hand, domestic silicone sealants take a long time to crosslink and cure at room temperature when sizing, and have high surface cleaning requirements for the bonded materials, and are also relatively harsh on the sizing environment (temperature, humidity, etc.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acidic transparent silicone weather-resistant sealant for construction

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022] Hydroxyl-terminated polydimethylsiloxane 80000mPa·s: 25 parts

[0023] Hydroxyl-terminated polydimethylsiloxane 200000mPa·s: 25 parts

[0024] Methyl-terminated polydimethylsiloxane 500mPa·s: 20 parts

[0025] Modified fumed silica 150m 2 / g: 10 parts

[0026] Methyltriacetoxysilane: 5 parts

[0027] Dibutyltin diacetate: 0.05 parts

[0028] 2,3-dihydroxy-4-n-decyloxybenzophenone: 0.04 parts

[0029] Tris(1,2,2,6,6-pentamethylpiperidinyl) phosphite: 0.01 parts

[0030] The preparation method of the modified fumed silica is as follows: (1) firstly carry out a coupling modification treatment on the surface of fumed silica with vinyl tris (β-methoxyethoxy) silane; (2 ) The primary modified silica and vinyl silicone oil are subjected to secondary coating and grafting modification under peroxide conditions.

[0031] The above-mentioned acidic transparent silicone weather-resistant sealant for construction is prepared by the following steps: (1) adding hydroxyl-termina...

example 2

[0033] Hydroxyl-terminated polydimethylsiloxane 10000mPa·s: 50 parts

[0034] Hydroxyl-terminated polydimethylsiloxane 1000000mPa·s: 100 parts

[0035] Methyl-terminated polydimethylsiloxane 1000mPa·s: 140 parts

[0036] Modified fumed silica 400m 2 / g: 60 parts

[0037] Methyltriacetoxysilane: 25 parts

[0038] Ethyltriacetoxysilane: 10 parts

[0039] Propyltriacetoxysilane: 5 parts

[0040] Dibutyltin dilaurate: 0.5 parts

[0041] 2,3-dihydroxy-4-n-decyloxybenzophenone: 0.1 parts

[0042] Tris(1,2,2,6,6-pentamethylpiperidinyl) phosphite: 0.4 parts

[0043] The above raw materials were uniformly mixed according to the method of Example 1 to prepare an acidic transparent silicone weather-resistant sealant.

example 3

[0045] Hydroxyl-terminated polydimethylsiloxane 10000mPa·s: 10 parts

[0046] Hydroxyl-terminated polydimethylsiloxane 400000mPa·s: 90 parts

[0047] Methyl-terminated polydimethylsiloxane 100mPa·s: 50 parts

[0048] Modified fumed silica 200m 2 / g: 25 servings

[0049] Ethyltriacetoxysilane: 15 parts

[0050] Dibutyltin dilaurate: 0.1 parts

[0051] Dioctyltin dilaurate: 0.1 parts

[0052] 2,3-dihydroxy-4-n-decyloxybenzophenone: 0.1 parts

[0053] Tris(1,2,2,6,6-pentamethylpiperidinyl) phosphite: 0.1 parts

[0054] The above raw materials were uniformly mixed according to the method of Example 1 to prepare an acidic transparent silicone weather-resistant sealant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an acidic and transparent silicone weather-resistant sealant for construction, and belongs to the technical field of adhesives. The acidic and transparent silicone weather-resistant sealant is prepared from the following components in parts by weight: 50-150 parts of hydroxyl terminated polydimethylsiloxane, 20-140 parts of methyl terminated polydimethylsiloxane, 10-60 parts of fumed silica, 5-40 parts of a cross-linking agent, 0.05-0.5 part of a catalyst and 0.05-5 parts of a composite anti-yellowing agent. The acidic and transparent silicone weather-resistant sealant has the advantages of high strength, good adhesive performance, excellent weather resistance, quick crosslinking curing at room temperature and the like, and can be widely applied to weather-resistant sealing of glass curtain walls, glass daylighting roofs and other constructional engineering.

Description

technical field [0001] The invention relates to an acidic transparent silicone weather-resistant sealant for construction and a preparation method thereof, belonging to the technical field of adhesives. Background technique [0002] Silicone sealant is a kind of building sealing material, which can withstand the outward movement of joints to achieve the purpose of airtightness and watertightness. The molecular structure of silicone sealant contains Si-O bond, and its bond energy is as high as 425kJ / mol, which is far greater than the C-C bond energy (345kJ / mol) and C-O bond energy (351kJ / mol). Therefore, it has good stability and has Strong mechanical properties; coupled with the large molecular volume and low cohesive energy density of polysiloxane, it has excellent stain resistance, high and low temperature resistance, high hydrophobicity and good air permeability, etc., and can be used in Long-term use in the range of -60~200°C, its mechanical properties such as tensile s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J183/06C09J183/04C09J11/06C09J11/04C09C1/28C09C3/08C09C3/10
Inventor 林菊琴
Owner ZHEJIANG TIME NEW MATERIAL