An environmentally friendly modified pvc resin cable sheath material

A cable sheath and resin technology, used in plastic/resin/wax insulators, organic insulators, climate change adaptation, etc. Long time and other problems, to achieve the effect of good connection performance, enhanced mechanical properties, and obvious low temperature resistance

Active Publication Date: 2016-08-24
ZAOZHUANG POWER SUPPLY COMPANY OF STATE GRID SHANDONG ELECTRIC POWER +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Rubber is a highly elastic polymer material with reversible deformation. It is elastic at room temperature. It can produce a large deformation under the action of a small external force, and it can return to its original shape after the external force is removed. During use, due to friction with other objects, resulting in The surface of the rubber is damaged or even loses its original performance, and the rubber is used for too long, and the aging speed becomes faster, especially the wear and erosion of the rubber pipeline, which will lead to the leakage of the internal transmission medium, and under extreme conditions, Environmental cracking resistance, high and low temperature resistance and weather resistance are poor, and it is not easy to degrade after being discarded and buried, polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] An environment-friendly modified pvc resin cable sheath material, its raw materials include by weight: 70 parts of pvc resin, 40 parts of nanofiber, 10 parts of modified nylon material, 1.5 parts of sulfur powder, 50 parts of white carbon black, nanometer dioxide 40 parts of silicon, 30 parts of organic bentonite, 2 parts of methyl silicone oil, 0.5 parts of anti-aging agent MB, 1.4 parts of anti-aging agent RD, 2 parts of accelerator CZ, 2 parts of accelerator D, 1.5 parts of barium stearate, 3 parts of zinc oxide ; wherein the modified nylon material is prepared by the following process: by weight, 0.3 parts of resorcinol, 3 parts of formaldehyde, 6 parts of water and 26 parts of carboxylated styrene-butadiene rubber are mixed evenly, and then adding a mass fraction of 7.5% sodium hydroxide solution Make the pH value of the material 7.6, after standing for 7 hours, add 25 parts of nylon staple fiber, 20 parts of carboxylated styrene-butadiene rubber, 2 parts of dispers...

Embodiment 2

[0013] An environment-friendly modified pvc resin cable sheath material, its raw materials include by weight: 90 parts of pvc resin, 30 parts of nanofiber, 14 parts of modified nylon material, 1 part of sulfur powder, 54 parts of white carbon black, nanometer dioxide 30 parts of silicon, 35 parts of organic bentonite, 1.5 parts of methyl silicone oil, 1 part of anti-aging agent MB, 1 part of anti-aging agent RD, 2.4 parts of accelerator CZ, 1.6 parts of accelerator D, 3 parts of barium stearate, 2 parts of zinc oxide ; wherein the modified nylon material is prepared by the following process: 0.6 parts of resorcinol, 2 parts of formaldehyde, 12 parts of water and 23 parts of carboxylated styrene-butadiene rubber are mixed uniformly by weight, and then adding mass fraction is 6% sodium hydroxide solution Make the pH value of the material 7.8, after standing for 5 hours, add 30 parts of nylon staple fiber, 16 parts of carboxylated styrene-butadiene rubber, 4 parts of dispersant an...

Embodiment 3

[0015] An environment-friendly modified pvc resin cable sheath material, its raw materials include by weight: 83 parts of pvc resin, 36 parts of nanofiber, 12.4 parts of modified nylon material, 1.35 parts of sulfur powder, 52.6 parts of white carbon black, nanometer dioxide 37 parts of silicon, 32.4 parts of organic bentonite, 1.85 parts of methyl silicone oil, 0.75 parts of anti-aging agent MB, 1.25 parts of anti-aging agent RD, 2.25 parts of accelerator CZ, 1.73 parts of accelerator D, 2.3 parts of barium stearate, 2.4 parts of zinc oxide ; wherein the modified nylon material is prepared by the following process: by weight, 0.5 parts of resorcinol, 2.7 parts of formaldehyde, 8 parts of water and 25.6 parts of carboxylated styrene-butadiene rubber are mixed evenly, and then adding a mass fraction of 7.2% sodium hydroxide solution Make the pH value of the material 7.7, after standing for 6 hours, add 28 parts of nylon staple fiber, 18 parts of carboxylated styrene-butadiene ru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly modified PVC resin cable sheathing material which comprises the following raw materials in parts by weight: 70-90 parts of PVC resin, 30-40 parts of nanofiber, 10-14 parts of modified nylon materials, 1-1.5 part of sulfur powder, 50-54 parts of white carbon black, 30-40 parts of nano silica, 30-35 parts of organic bentonite, 1.5-2 parts of methylsilicone oil, 0.5-1 part of anti-aging agent MB, 1-1.4 part of anti-aging agent RD, 2-2.4 parts of accelerant CZ, 1.6-2 parts of accelerant D, 1.5-3 parts of barium stearate and 2-3 parts of zinc oxide. The environment-friendly modified PVC resin cable sheathing material is environment-friendly, small in environmental pollution after being buried, and high in tensile strength and tear strength and good in anti-aging property in the using process.

Description

technical field [0001] The invention relates to the technical field of environment-friendly cable sheath materials, in particular to an environment-friendly modified PVC resin cable sheath material. Background technique [0002] Rubber is a highly elastic polymer material with reversible deformation. It is elastic at room temperature. It can produce a large deformation under the action of a small external force, and it can return to its original shape after the external force is removed. During use, due to friction with other objects, resulting in The surface of the rubber is damaged or even loses its original performance, and the rubber is used for too long, and the aging speed becomes faster, especially the wear and erosion of the rubber pipeline, which will lead to the leakage of the internal transmission medium, and under extreme conditions, Environmental crack resistance, high and low temperature resistance and weather resistance are poor, and it is not easy to degrade ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L77/00C08L13/00C08K13/02C08K3/06C08K3/36C08K3/34C08K3/22C08K5/098C08K3/04H01B3/44
CPCY02A30/14
Inventor 吕国栋秦桂敏黄芳张晓春曹云雷刘琳孙海涛韩亮刘伟
Owner ZAOZHUANG POWER SUPPLY COMPANY OF STATE GRID SHANDONG ELECTRIC POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com