Colored adhesive ink for 3D printers and preparation method thereof

A technology of 3D printers and adhesives, applied in the direction of non-polymer organic compound adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problem of corrosion, small application range, adhesion Insufficient strength and other problems, to achieve the effect of simple preparation process, wide application range and high adhesive strength

Inactive Publication Date: 2015-02-18
HUNAN SURPLUS BO DIGITAL TECH DEV CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There are some drawbacks in the existing color adhesive ink materials for 3D printers in China. They are corrosive, slow in bonding speed, and not strong enough to meet the requirements of 3D printers, that is, fluidity, bonding strength, Adhesion time, color, transparency, corrosion and safety cannot meet the requirements at the same time
The existing 3D printer color adhesive ink materials are only suitable for the above-mentioned 650-850 models, and the scope of application is small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of proportioning of the colored adhesive ink that 3D printer is used:

[0031] Glycerol: 10 parts

[0032] Ethylene glycol: 12 parts

[0033] Ethylenediamine: 0.6 parts

[0034] Monoethanol: 1 part

[0035] Distilled water: 74 parts

[0036] Castor oil sulfate anionic surfactant: 1.6 parts

[0037] Dye (black b168): 0.6 parts

[0038] Vinyl acetate: 0.2 parts.

[0039] A kind of preparation method of the colored binder ink that 3D printer is used, specifically comprises the steps:

[0040] (1) Weigh 10 parts of glycerol, 12 parts of ethylene glycol, 0.6 parts of ethylenediamine, 1 part of monoethanol, 74 parts of distilled water, 1.6 parts of castor oil sulfate anionic surfactant, dye (black b168) 0.6 parts, 0.2 parts of vinyl acetate for standby;

[0041] (2) Put the components into the mixing tank and mix them together, and stir for 40 minutes under vacuum conditions, the stirring speed is 110r / min, and the temperature is controlled at 30°C-40°C;

[00...

Embodiment 2

[0044] A kind of proportioning of the colored adhesive ink that 3D printer is used:

[0045] Glycerol: 9 parts

[0046] Ethylene glycol: 11 parts

[0047] Ethylenediamine: 0.5 parts

[0048] Monoethanol: 0.8 parts

[0049] Distilled water: 76 parts

[0050] Alkyl betaine zwitterionic surfactant: 1.7 parts

[0051] Dye (direct rose red r227): 0.85 parts

[0052] Vinyl acetate: 0.15 parts.

[0053] A kind of preparation method of the colored binder ink that 3D printer is used, specifically comprises the steps:

[0054] (1) Weigh 9 parts of glycerol, 11 parts of ethylene glycol, 0.5 parts of ethylenediamine, 0.8 parts of monoethanol, 76 parts of distilled water, 1.7 parts of alkyl betaine zwitterionic surfactant, dye (direct Rose red r227) 0.85 parts, 0.15 parts of vinyl acetate for use;

[0055] (2) Put all the components into the mixing tank and mix them together, and stir for 45 minutes under vacuum conditions, the stirring speed is 115r / min, and the temperature is con...

Embodiment 3

[0058] A kind of proportioning of the colored adhesive ink that 3D printer is used:

[0059] Glycerol: 9 parts

[0060] Ethylene glycol: 11 parts

[0061] Ethylenediamine: 0.5 parts

[0062] Monoethanol: 0.8 parts

[0063] Distilled water: 76 parts

[0064] Alkyl betaine zwitterionic surfactant: 1.7 parts

[0065] Dye (red light yellow y86): 0.85 parts

[0066] Vinyl acetate: 0.15 parts.

[0067] A kind of preparation method of the colored binder ink that 3D printer is used, specifically comprises the steps:

[0068] (1) Weigh 9 parts of glycerol, 11 parts of ethylene glycol, 0.5 parts of ethylenediamine, 0.8 parts of monoethanol, 76 parts of distilled water, 1.7 parts of octylphenol polyoxyethylene ether nonionic surfactant, dye (Red light yellow y86) 0.85 parts and 0.15 parts of vinyl acetate for use;

[0069] (2) Put each component into a mixing tank and mix together, and stir for 50 minutes under vacuum conditions, the stirring speed is 120r / min, and the temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a colored adhesive ink for 3D printers, which is composed of the following components in parts by weight: 8-10 parts of glycerol, 10-12 parts of ethylene glycol, 0.4-0.6 part of ethylenediamine, 0.6-1 part of monoethanol, 70-88 parts of distilled water, 1-2 parts of activator, 0.5-1 part of dye and 0.1-0.2 part of vinyl acetate. The preparation method comprises the following steps: proportionally weighing the components, mixing the components in a mixing barrel, stirring at the speed of 110-120 r / min under vacuum conditions for 40-50 minutes while controlling the temperature at 30-40 DEG C, filtering the uniform mixed solution with a paper filter, and storing in a sealed state in a dark place. The colored adhesive ink for 3D printers has the characteristics of simple preparation technique, high adhesive strength, high adhesion speed and low corrosivity, and can satisfy the requirements of flowability, adhesive strength, adhesion time, color, transparency, corrosivity, safety and the like for the 3D printers.

Description

technical field [0001] The invention relates to 3D printer consumables, in particular to a color adhesive ink for a 3D printer and a preparation method thereof. Background technique [0002] 3D printer, a machine of rapid prototyping manufacturing technology, is a technology based on digital model files, using bondable materials such as powdered metal or plastic, to construct objects by layer-by-layer printing. The printing process of each layer of 3D printing technology is divided into two steps. First, a layer of special glue is sprayed on the area that needs to be formed. The glue droplet itself is very small and not easy to spread; It will quickly solidify and bond, and the area without glue will remain loose. In this way, the solid model will be "printed" under the alternation of a layer of glue and a layer of powder. After printing, just sweep away the loose powder to "plan" out of the model, and the remaining powder can be recycled. The printing materials used by 3D...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/00C09J11/06C09J11/08
Inventor 刘可武
Owner HUNAN SURPLUS BO DIGITAL TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com