A woven bag and flat yarn technology, applied in the field of materials, can solve the problems of easy aging, short service life, poor anti-ultraviolet function, etc., and achieve the effect of increasing service life

Inactive Publication Date: 2015-02-25
LIAONING TENGHUA PLASTIC
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing woven bag products are easy to age, have a short service life, and have poor anti-ultr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation method of sunscreen woven bag flat yarn comprises the steps of: taking 100 parts of polypropylene, 1.5 parts of antiaging agent, 1 part of coupling agent, and 0.4 part of antioxidant DLTP (dilauryl thiodipropionate) by weight. , 14 parts of nano calcium carbonate, 10 parts of polyoxymethylene, 22 parts of linear low density polyethylene, 1.5 parts of polyethylene wax, 3.3 parts of ethylene-methyl acrylate copolymer (EMA1125AC), 1.5 parts of tributyl citrate, 0.7 parts of turpentine 6 parts, 6 parts of ultraviolet absorber (UV-531) and 3.3 parts of additives for batching, then put the prepared material into the mixing tank and stir evenly, use the suction feeding system to suck the raw material to the extruder, and pass the material The barrel is heated to 235°C, and the raw material is plasticized into a molten state under the mutual shear of the screw and the barrel, and extruded into a film through the extruder die head. The extruder pressure is 8Mpa, ...

Embodiment 2

[0022] The preparation method of sunscreen woven bag flat yarn comprises the steps of: taking 100 parts of polypropylene, 1.2 parts of antiaging agent, 0.8 part of coupling agent, and 0.2 part of antioxidant DLTP (dilauryl thiodipropionate) by weight. , 12 parts of nano calcium carbonate, 9 parts of polyoxymethylene, 20 parts of linear low density polyethylene, 1.3 parts of polyethylene wax, 3.1 parts of ethylene-methyl acrylate copolymer (EMA1125AC), 1.3 parts of tributyl citrate, turpentine 0.5 parts, 5 parts of ultraviolet absorber (UV-531) and 3.1 parts of additives are used for compounding, and then the prepared materials are put into the mixing tank and stirred evenly, and the raw materials are sucked and sent to the extruder by using the suction feeding system. The barrel is heated to 230°C, and the raw material is plasticized into a molten state under the mutual shear of the screw and the barrel, and extruded into a film through the die head of the extruder. 6 times th...

Embodiment 3

[0025] The preparation method of sunscreen woven bag flat yarn comprises the steps of: taking 100 parts of polypropylene, 3 parts of antiaging agent, 1.2 parts of coupling agent, and 0.6 part of antioxidant DLTP (dilauryl thiodipropionate) by weight. , 16 parts of nano-calcium carbonate, 11 parts of polyoxymethylene, 24 parts of linear low-density polyethylene, 1.6 parts of polyethylene wax, 3.6 parts of ethylene-methyl acrylate copolymer (EMA1125AC), 1.7 parts of tributyl citrate, turpentine 0.9 parts, 7 parts of ultraviolet absorber (UV-531) and 3.6 parts of additives for compounding, then put the prepared materials into the mixing tank and stir evenly, use the suction feeding system to suck the raw materials to the extruder, after The barrel is heated to 240°C, and the raw material is plasticized into a molten state under the mutual shear of the screw and the barrel, and extruded into a film through the extruder die head. When extruding into a film, the pulling speed of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sun-proof woven bag tape yarn and woven bag production method and a woven bag. Tape yarn is produced by means of uniformly mixing polypropylene, aging proof agent, coupling agent, antioxidant, nano calcium carbonate, polyoxymethylene, linear low density polyethylene, polyethylene wax, ethylene-methyl acrylate copolymer, tributyl citrate, turpentine, ultraviolet absorbent and auxiliaries, plastifying the materials at the temperature of 230-240 DEG C to be fused, extruding the fused materials into a film, cooling, cutting the cooled film into blank yarn and stretching the blank yarn into the tape yarn. The produced tape yarn is woven into the sun-proof woven bag, the produced sun-proof woven bag tape yarn has high breaking strength retention rate and breaking elongation retention rate and good sun-proof performance after being exposed to the outdoor atmosphere for one year, performance of the woven bag woven with the tape yarn is improved, service life of the woven bag is prolonged, and toughness and tensile strength of original tape yarn are kept.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to a preparation method of sunscreen woven bag flat yarn and woven bag, and also relates to a product prepared by the method. Background technique [0002] Woven bags are packaging materials for fertilizers, chemical products and other items. The main production process is to use plastic raw materials to extrude film, cut, and unidirectionally stretch into flat yarn, and then weave warp and weft to obtain the product. However, the existing woven bag products are easy to age, have a short service life, and have poor anti-ultraviolet function and low tensile force, which makes the loaded items easily corrupted. Difficult to sort. Therefore, there is an urgent need to improve the performance of woven bag materials, improve the weaving technology of woven bags, improve the sun protection function of woven bags, prolong life and improve tensile properties. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/46D01F1/10D01D5/42D01D5/12D03D15/00D03D13/00D03D15/292D03D15/46D03D15/50
Inventor 姜虹褚良昌臧常久王丹
Owner LIAONING TENGHUA PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap