A kind of iron-based constant magnetic permeability nanocrystalline magnetic core and preparation method thereof

A nanocrystalline and magnetic core technology, applied in the manufacture of inductors/transformers/magnets, magnetic materials, magnetic objects, etc., can solve the problems affecting the continuous preparation of strips, insufficient fluidity of molten steel, and high brittleness of strips. Simple and fast production process, low coercivity, high corrosion resistance and thermal stability

Active Publication Date: 2018-02-23
ADVANCED TECHNOLOGY & MATERIALS CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the preparation process of nanocrystalline alloy strips with this composition, the continuous preparation of strips is often affected due to insufficient fluidity of molten steel; or the fluidity of molten steel is increased by increasing the temperature of molten steel, but due to excessive overheating The prepared strip is brittle and poor in usability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of iron-based constant magnetic permeability nanocrystalline magnetic core and preparation method thereof
  • A kind of iron-based constant magnetic permeability nanocrystalline magnetic core and preparation method thereof
  • A kind of iron-based constant magnetic permeability nanocrystalline magnetic core and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Embodiment 1 is used to prepare the alloy of magnetic core to be Fe 73.5 Cu 1 Nb 3 Si 15.5 B 7

[0062] In this embodiment, 6 groups of tests were carried out, wherein the first four groups (1-4) were products of the present invention, and the latter two groups (5-6) were comparative examples.

[0063] The preparation method is as follows:

[0064](1) According to the composition and raw material ratio of each experimental combination of gold in Table 1, the alloy raw materials were vacuum smelted at 1350 ° C to prepare a master alloy ingot; then the master alloy ingot was put into a vacuum induction furnace for secondary melting Then under the protection of argon, while maintaining the constant pressure in the furnace, the quenched amorphous alloy thin strip with a width of 30 mm and a thickness of 22 μm is made by using a single roll quenching method, wherein the roll is a copper roll, and the surface speed of the roll is 25 m / s;

[0065] (2) Cut the thin stri...

Embodiment 2

[0078] Each group of magnetic cores in Example 1 is made into a current transformer through processes such as surface treatment, packaging, copper wire winding, and testing. The performance parameters of the obtained current transformers are shown in Table 2. The relative error RE and phase difference θ in the table are tested by the transformer calibrator, and the rated primary current of the test is 60A.

[0079] Table 2 Alloy heat treatment method and performance data of current transformer

[0080]

[0081] Magnetic core provided by the present invention can be used for current transformer, see Figure 10 , which is an equivalent circuit diagram of a known current transformer. The current transformer includes the magnetic core provided by the present invention, and additionally has a primary winding and at least one secondary winding. The primary winding usually has one turn. As can be seen from Table 2, the current transformer of the present invention has a small abs...

Embodiment 3

[0083] Each group of magnetic cores in Example 1 is made into a current compensation choke coil through processes such as surface treatment, packaging, copper wire winding, and testing. The performance parameters of the obtained current transformers are shown in Table 3.

[0084] Table 3 Alloy heat treatment method and performance data of current compensation choke coil

[0085]

[0086] The magnetic core provided by the present invention can be used for current compensation choke coil, see Figure 11 , which is a working principle diagram of the known current compensation choke coil. The current compensation choke coil of the present invention has the above-mentioned magnetic core. Phase or multi-phase current has more than three windings with the same turns and the same direction. The current compensation choke coil provided by the invention has strong anti-saturation capability, and the loss value is less than 50W / kg under the condition of 500mT / 20kHz.

[0087] Based ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
loss valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an iron-based constant magnetic permeability nanocrystalline magnetic core and a preparation method thereof. The magnetic core is made of iron-based alloy. The molecular formula of the iron-based alloy is FeaCubNbcSidBeMfXg, wherein M is at least one of the elements V, Ti, Mn, Cr, and Mo, and X is the element C, Ge, P and impurities. at least one of . The preparation method of the magnetic core of the present invention is to apply tensile stress along the strip length direction while the amorphous alloy thin strip is heat-treated; then the strip is wound to make a magnetic core of a certain size; It is required to adjust the magnetic domain structure and distribution in the strip during the crystallization process by adjusting the tension and temperature values ​​in the heat treatment process, so as to obtain constant magnetic permeability, and the magnetic permeability is high in DC and AC. Adjustable magnetic core. The relative initial magnetic permeability of the magnetic core is 50 to 2000 under the DC condition by using the simulated impact test method.

Description

technical field [0001] The invention relates to a constant magnetic permeability core, in particular to an iron-based constant magnetic permeability nanocrystalline magnetic core and a preparation method thereof, that is, it has a constant relative magnetic permeability, and the magnetic permeability is highly adjustable for AC and DC components The Fe-based nanocrystalline magnetic core and its preparation method, and the application of this magnetic core in anti-DC current transformer and current compensation choke coil. Background technique [0002] In current transformers and current compensation chokes, it is required that the magnetic permeability of the applied magnetic core has a high degree of modulability to the AC and DC components. Among them, in view of the development of power electronic technologies such as electronic smart meters and frequency conversion air conditioners, the current transformers used in their circuits are required to have a strong ability to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/147H01F27/255H01F41/02C22C33/04B22F1/00H01F38/28
Inventor 吴晓荣薄希辉李准冯硕倪晓俊李德仁卢志超
Owner ADVANCED TECHNOLOGY & MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com