Steel rust inhibitor and preparation method thereof

A technology of anti-rust agent and steel, which is applied in the field of steel surface treatment, can solve the problems of high cost, high price and complicated production of anti-rust agent, and achieve the effect of low production cost, easy viscosity and easy availability of raw materials

Inactive Publication Date: 2015-03-04
一站工材(常州)互联网科技有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent No. CN03111171.8 proposes a formula to replace sodium nitrite, but it is complicated to make and inconvenient to use; Large, more expensive, the cost of antirust agent is much higher than that of sodium nitrite antirust agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The iron and steel rust inhibitor of the present embodiment is made from the following raw materials in parts by weight: 17 parts of phytic acid ester, 14 parts of barium petroleum sulfonate, 3 parts of aluminum naphthenate, 12 parts of sodium tripolyphosphate, 6 parts of diethanolamine Parts, 7 parts of surfactant, 7 parts of zinc dialkyl dithiophosphate, 6 parts of sodium molybdate, 6 parts of amino trimethylene phosphonic acid, 2 parts of tolyltriazole, 6 parts of thickener, acetylcitric acid 7 parts of triethyl ester and 96 parts of deionized water. The thickener is diatomaceous earth, bentonite or aluminum silicate. The surfactant is polyoxyethylene fatty alcohol ether or coconut oil fatty acid diethanolamide.

[0015] The antirust agent for iron and steel of this embodiment includes the following steps: weighing each raw material according to the weight ratio, adding it into a reaction kettle, turning on the reaction kettle and stirring at 65° C., and stirring fo...

Embodiment 2

[0018] The iron and steel rust inhibitor of the present embodiment is made from the following raw materials in parts by weight: 10 parts of phytic acid ester, 10 parts of barium petroleum sulfonate, 2 parts of aluminum naphthenate, 3 parts of sodium tripolyphosphate, 2 parts of diethanolamine Parts, 5 parts of surfactant, 5 parts of zinc dialkyldithiophosphate, 4 parts of sodium molybdate, 5 parts of amino trimethylene phosphonic acid, 1 part of tolyltriazole, 5 parts of thickener, acetylcitric acid 4 parts of triethyl ester and 90 parts of deionized water. The thickener is diatomaceous earth, bentonite or aluminum silicate. The surfactant is polyoxyethylene fatty alcohol ether or coconut oil fatty acid diethanolamide.

[0019] The antirust agent for iron and steel of this embodiment includes the following steps: weighing each raw material according to the weight ratio, adding it into a reaction kettle, turning on the reaction kettle and stirring at 70° C., stirring for 3 hou...

Embodiment 3

[0022] The iron and steel rust inhibitor of the present embodiment is made from the following raw materials in parts by weight: 20 parts of phytic acid ester, 15 parts of barium petroleum sulfonate, 4 parts of aluminum naphthenate, 15 parts of sodium tripolyphosphate, 8 parts of diethanolamine Parts, 8 parts of surfactant, 9 parts of zinc dialkyldithiophosphate, 8 parts of sodium molybdate, 7 parts of amino trimethylene phosphonic acid, 3 parts of tolyltriazole, 7 parts of thickener, acetylcitric acid 9 parts of triethyl ester and 100 parts of deionized water. The thickener is diatomaceous earth, bentonite or aluminum silicate. The surfactant is polyoxyethylene fatty alcohol ether or coconut oil fatty acid diethanolamide.

[0023] The antirust agent for iron and steel of this embodiment includes the following steps: weighing each raw material according to the weight ratio, adding it into a reaction kettle, turning on the reaction kettle and stirring at 65° C., stirring for 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a steel rust inhibitor and a preparation method thereof. The preparation method comprises the following steps: weighing phytate, barium petroleum sulfonate, aluminum naphthenate, sodium tripolyphosphate, diethanolamine, surfactant, zinc dialkyl dithiophosphate, sodium molybdate, amino trimethylene phosphonic acid, tolyl triazole, thickener, acetyl triethyl citrate and deionized water according to parts by weight, adding into a middle, and starting the reaction kettle to stir at 65-70 DEG C until the components are completely dissolved. The steel rust inhibitor is free of harmful components to the human body, has the advantages of favorable rust inhibition property, simple treatment technique, accessible raw materials and low production cost, and is convenient to use. Under the condition of satisfying the operating conditions, the viscosity of the rust inhibitor should be reduced to the lowest value. The steel rust inhibitor with low viscosity is easy for coating, can effectively lower the thickness, and achieves the goals of saving and loss reduction.

Description

technical field [0001] The invention relates to a steel surface treatment technology, in particular to a steel antirust agent and a preparation method thereof. Background technique [0002] At present, with the continuous development of industry, the use of steel is also increasing. However, during the production process or the storage process of finished products, steel plates are easily oxidized and rusted when encountering humid air and rainy days, which affects the appearance quality of products. This has brought problems to the use of steel, and the annual loss of steel due to corrosion is very alarming. In order to prevent surface corrosion, antirust treatment must be carried out; Protective oil film, so as to isolate the corrosion of metal by water vapor in the air, and achieve the purpose of rust prevention. However, the use of antirust oil requires a large amount of oil raw materials, which intensifies energy consumption and increases costs. Therefore, it is only us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/00
Inventor 尤为
Owner 一站工材(常州)互联网科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap