Multipurpose convenient cement

A multi-purpose, cement technology, applied in the field of building materials, can solve the problems of inaccurate measurement on the construction site, poor water retention capacity of mortar, high construction repair rate, etc., achieve good water retention capacity, increase thixotropy and bioresistance, and low labor intensity Effect

Inactive Publication Date: 2015-03-18
JILIN DINGXI NEW BUILDING MATERIAL
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now the mortar used in the construction industry is made by mixing cement, sand and water on site. This kind of mortar has the following defects. One, it needs to use manual or equipment to transport cement sand to the room and then mix it. A lot of labor is wasted like this and work efficiency is low
Second, the water retention capacity of the mortar is poor. When laying tiles indoors, the tiles need to be soaked or pre-wetted before use.
Third, the traditional cement mortar is operated on the construction site, and the natural sand is screened on site, so that it has not been washed with water, and the soil content is large, which affects the strength of the cement and produces a large amount of construction waste
In addition, the measurement at the construction site is inaccurate, resulting in problems such as cracking, hollowing, shedding, leakage, dust and sand on the ground, and high construction repair rate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] In terms of 100kg product, natural fine sand is selected and sieved. After washing, it is transported to a drying furnace by a conveyor belt for drying. After it comes out, it is dry sand. Then add 30kg of cement, 66.65kg of dry sand, 2.5kg of calcium carbonate, 0.2kg of cellulose ether, 0.5kg of redispersible latex powder, 0.05kg of anti-slip additive, and 0.1kg of starch ether. Pour it into a dry mixer for stirring, and after stirring for 10 minutes, put it into a storage tank for storage, and then fill it with an automatic filling machine to produce the above-mentioned multi-purpose convenient cement.

Embodiment 2

[0022] In terms of 100kg product, natural fine sand is selected and sieved. After washing, it is transported to a drying furnace by a conveyor belt for drying. After it comes out, it is dry sand. Then add 40kg of cement, 53.27kg of dry sand, 5kg of calcium carbonate, 0.35kg of cellulose ether, 1.0kg of redispersible latex powder, 0.08kg of anti-slip additive, and 0.3kg of starch ether. Pour it into a dry mixer for stirring, and after stirring for 10 minutes, put it into a storage tank for storage, and then fill it with an automatic filling machine to produce the above-mentioned multi-purpose convenient cement.

Embodiment 3

[0024] In terms of 100kg product, natural fine sand is selected and sieved. After washing, it is transported to a drying furnace by a conveyor belt for drying. After it comes out, it is dry sand. Then 50kg of cement, 41.9kg of dry sand, 5kg of calcium carbonate, 0.5kg of cellulose ether, 2.0kg of redispersible latex powder, 0.1kg of anti-slip additive, and 0.5kg of starch ether. Pour it into a dry mixer for stirring, and after stirring for 10 minutes, put it into a storage tank for storage, and then fill it with an automatic filling machine to produce the above-mentioned multi-purpose convenient cement.

[0025] Usage and dosage of multi-purpose convenient cement:

[0026] 1. Mix this product with clean water (ratio: cement to water ratio is 4:1) and stir evenly, stand still for 5-10 minutes, and stir again. Add water if too thick.

[0027] 2. The reference dosage varies according to the specific conditions of the project. For example, the amount of pasting tiles: use a 3×3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to multipurpose convenient cement. The multipurpose convenient cement is composed of the following raw materials in parts by weight: 20-50 parts of cement, 41.9-66.65 parts of dry sand, 2-10 parts of calcium carbonate, 0.1-0.5 part of cellulose ether, 0.5-4.5 parts of redispersible latex powder, 0.05-0.1 part of an anti-skid auxiliary agent, and 0.1-0.5 part of starch ether. The product is prepared by screening natural sand, washing with water and sending to a baking rotary furnace to baking the natural sand to form dry sand, then pouring the above raw materials into an electric dry mixer according to the above ratios, stirring, after 10 min, conveying the uniformly-stirred raw materials into a material storage tank and packaging by a packager. The cement is environment-friendly, and has the fluidity, the volume density, the water retention property, the water-adsorption gas content, the plastic cracking property, the dry shrinkage, the compressive strength, the rupture strength, the adhesive strength, the flexibility, the impact resistance and the like all substantially better than those of common cement dry-mixed products.

Description

technical field [0001] The invention relates to a building material, in particular to a multi-purpose convenient cement. Background technique [0002] Against the background of accelerated domestic urbanization and the gradual maturity of international contracting business, my country's construction industry has broad prospects for development. The raw materials for construction, such as cement and sand, also developed accordingly. In modern society, with the development of cities and the improvement of people's living conditions, residential buildings are gradually developing to high-rise buildings. If you use the previous cement mortar, because of its poor water retention and viscosity, you need a thick layer of mortar and a large load, so you need a new type of cement material. Keep up with architectural development needs. Now the mortar used in the construction industry is made by mixing cement, sand and water on site. This kind of mortar has the following defects. One...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/38
Inventor 朱玉臣刘国泽
Owner JILIN DINGXI NEW BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products