Multifunctional antibacterial compound preparation and application thereof

A compound preparation and multi-functional technology, applied in the application, biocide, disinfectant and other directions, can solve the problems of limited antibacterial range, limited bactericidal effect, and poor immobilization, and achieve broad antibacterial spectrum, increased specific surface area, and immobilization. solid effect

Inactive Publication Date: 2015-03-25
BEIJING ZHONGKE LANGMAI NANO TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Silver-based zeolite inorganic antibacterial agent has high efficiency and safety, but it also has certain disadvantages: if it is not firmly loaded, it is not resistant to washing when it is used as a textile additive; the antibacterial range has certain limitations
But the disadvantage is that the bactericidal effect is limited when used alone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional antibacterial compound preparation and application thereof
  • Multifunctional antibacterial compound preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of multifunctional antibacterial composite preparation of the present embodiment is made up of silver-zinc nano-zeolite powder and tourmaline superfine powder;

[0038] Wherein, the described silver-loaded zinc nano-zeolite powder is prepared by the following method:

[0039] One, 100g zeolite is pulverized to 200 order, then the mass concentration of preparation sodium hydroxide is 5%, the mass concentration of sodium metaaluminate is 500mL of mixed solution; Sodium aluminate mixed solutions were mixed, stirred at 100°C for 4 hours, rinsed with pure water until the pH value was 8, and dried at 120°C;

[0040]Two, the mass concentration of preparation silver nitrate is 0.3%, the mass concentration of zinc nitrate is 1.7% mixed solution 500mL, in silver nitrate-zinc nitrate mixed solution, add 15g instant aluminum sol; Mix the silver nitrate-zinc nitrate mixed solution after the aluminum sol, grind to 100mm-500mm through a wet ultrafine grinder, then wash with pu...

Embodiment 2

[0043] A kind of multifunctional antibacterial composite preparation of the present embodiment is made up of silver-zinc nano-zeolite powder and tourmaline superfine powder;

[0044] Wherein, the described silver-loaded zinc nano-zeolite powder is prepared by the following method:

[0045] One, 60g zeolite is pulverized to 200 order, then the mass concentration of preparation sodium hydroxide is 2%, the mass concentration of sodium metaaluminate is 500mL of the mixed solution that the mass concentration of sodium metaaluminate is 1.5%; Sodium aluminate mixed solutions were mixed, stirred at 100°C for 6 hours, rinsed with pure water until the pH value was 8.5, and dried at 120°C;

[0046] Two, the mass concentration of preparing silver nitrate is 0.4%, the mass concentration of zinc nitrate is 1.6% mixed solution 500mL, in silver nitrate-zinc nitrate mixed solution, add 25g instant aluminum sol; Mix the silver nitrate-zinc nitrate mixed solution after the aluminum sol, grind t...

Embodiment 3

[0049] A kind of multifunctional antibacterial composite preparation of the present embodiment is made up of silver-zinc nano-zeolite powder and tourmaline superfine powder;

[0050] Wherein, the described silver-loaded zinc nano-zeolite powder is prepared by the following method:

[0051] One, 50g zeolite is pulverized to 200 order, then the mass concentration of preparation sodium hydroxide is 1%, the mass concentration of sodium metaaluminate is 0.3% mixed solution 500mL; Sodium aluminate mixed solutions were mixed, stirred at 100°C for 5 hours, rinsed with pure water until the pH value was 7.5, and dried at 120°C;

[0052] Two, the mass concentration of preparation silver nitrate is 0.8%, the mass concentration of zinc nitrate is 1.2% mixed solution 500mL, in silver nitrate-zinc nitrate mixed solution, add 10g instant aluminum sol; Mix the silver nitrate-zinc nitrate mixed solution after the aluminum sol, grind to 100mm-500mm through a wet ultrafine grinder, then wash wit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a multifunctional antibacterial compound preparation and an application thereof, relates to an antibacterial compound preparation containing silver / zinc ions and an application of the compound preparation, in particular to an antibacterial compound preparation containing silver / zinc loaded nano-zeolite and tourmaline and an application of the compound preparation, and aims to provide the antibacterial compound preparation which has good antibacterial effect, low cost and firmly loaded silver / zinc ions and the application of the compound preparation. The multifunctional antibacterial compound preparation comprises silver / zinc loaded nano-zeolite powder and tourmaline super micro-powder and has anti-radiation, antibacterial and deodorization functions, components supplement each other and have synergetic antimicrobial effect, the effect is good, the antibacterial compound preparation is used for preparing antibacterial fabric, harmful bacteria on the fabric can be killed, and disease spread can be avoided; and further, the compound preparation has safety, non-toxic function and stable characteristic, so that the requirements for practical application can be met very well, and the multifunctional antibacterial compound preparation can be applied to the field of preparation of an antibacterial product.

Description

technical field [0001] The invention relates to an antibacterial compound preparation containing silver and zinc ions and its application, in particular to an antibacterial compound preparation containing silver-loaded zinc nanometer zeolite and tourmaline and its application. Background technique [0002] At present, there are many applications and published documents and open patents on the market, and the better effects are as follows: [0003] 1. Silver zeolite inorganic antibacterial agent. The mechanism of silver-based inorganic antibacterial agents is: ① Inorganic antibacterial agents are mainly based on metal ions. Metal ions are positively charged. When trace amounts of metal ions contact the cell membrane of microorganisms, Coulomb attraction occurs with the negatively charged cell membrane. Metal ions penetrate the cell membrane and enter the bacteria to react with sulfhydryl groups and amino groups on proteins in the bacteria. The active center of the protein i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A01N59/16A01N25/00A01N25/08A01P1/00A01N59/14
Inventor 姜英杰马良子姜雪
Owner BEIJING ZHONGKE LANGMAI NANO TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com