Method for preparing high-strength ceramic membrane by one-time co-firing

A ceramic membrane and high-strength technology, which is applied in the field of ceramic membranes, can solve the problems of low bonding strength between ceramic membranes and supports, increased energy consumption, and shedding of ceramic membrane layers, so as to ensure the effect of filtration and dust removal, equipment maintenance and operating costs Low, thorough regeneration effect

Active Publication Date: 2016-03-09
湖南科一环保科技股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problems brought by this method are firstly that the secondary firing increases the energy consumption of the preparation process, which is not conducive to energy saving and environmental protection; secondly, the bonding strength between the ceramic membrane and the support body is not high, and the ceramic membrane layer is prone to fall off during use. The phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-strength ceramic membrane by one-time co-firing
  • Method for preparing high-strength ceramic membrane by one-time co-firing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for preparing high-strength ceramic membranes by one-time co-firing, specifically:

[0033] (1) The raw material of the ceramic membrane support is composed of 48% by weight calcined bauxite, 25% high plasticity clay, 15% china clay and 12% feldspar. The hard raw materials in the formula are calcined bauxite and feldspar Select the powder that has been crushed to an average particle size below 10 microns, mix the hard raw material powder with other raw materials, and then ball mill for 5 hours to obtain a support body slurry;

[0034] (2) After sieving the support body slurry and removing iron, add rice bran as a pore-forming material. Before adding, the rice bran needs to be crushed to a fineness of 320 mesh, and then add an appropriate amount of water to disperse evenly with a high-speed mixer, and press filter to obtain mud after dehydration. cake.

[0035] (3) The mud cake is aged for more than 24 hours after roughing, and then vacuum-extruded into a wet b...

Embodiment 2

[0041] A method for preparing high-strength ceramic membranes by one-time co-firing, specifically:

[0042] (1) The raw material of the ceramic membrane support is composed of 40% calcined bauxite, 30% high plasticity clay, 20% china clay and 10% feldspar by weight percentage, and the hard raw materials in the formula are calcined bauxite and feldspar Select the powder that has been crushed to an average particle size below 10 microns, mix the hard raw material powder with other raw materials, and then ball mill for 5 hours to obtain a support body slurry;

[0043] (2) After sieving the support body slurry and removing iron, add straw as a pore-making material. Before adding, the straw needs to be crushed to a fineness of 250 mesh, and then add an appropriate amount of water to disperse evenly with a high-speed mixer, and press filter to obtain mud after dehydration cake.

[0044] (3) The mud cake is aged for more than 24 hours after roughing, and then vacuum-extruded into a ...

Embodiment 3

[0050] The method for preparing a high-strength ceramic membrane by co-firing at one time is specifically:

[0051] (1) The raw material of the ceramic membrane support is composed of 35% calcined bauxite, 35% high plasticity clay, 15% china clay and 15% feldspar by weight percentage, and the hard raw materials in the formula are calcined bauxite and feldspar Select the powder that has been crushed to an average particle size below 10 microns, mix the hard raw material powder with other raw materials, and then ball mill for 5 hours to obtain a support body slurry;

[0052] (2) After sieving the support body slurry and removing iron, add straw as a pore-making material. Before adding, the straw needs to be crushed to a fineness of 250 mesh, and then add an appropriate amount of water to disperse evenly with a high-speed mixer, and press filter to obtain mud after dehydration. cake.

[0053] (3) The mud cake is aged for more than 24 hours after roughing, and then vacuum-extrude...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The present invention provides a method of burning high -intensity ceramic membranes. This method is to mix the ceramic puree with burn aluminum alum and high -plastic clay as the main raw material.The membrane supports the body of the body. After drying, spray ceramic membrane slurry on the surface of the blank body, and then burn together in the roller kiln.The intensity of the support body of the ceramic film is provided by highly densely deduced the compound ceramic material for enhanced phases by the mockest granular and in -situ.The structure of the plant that is completely burned at high temperature is adjusted and controlled, so it has a good hole -connecting characteristics, so as to obtain a ceramic film support body with high intensity and high -connecting pore structure.The binding intensity between the supporting body is high, the service life is long, and it also has the characteristics of low preparation costs and energy saving.

Description

technical field [0001] The invention relates to the technical field of ceramic membranes, and further refers to a preparation method of high-strength ceramic membranes. Background technique [0002] The bag filter is the most widely used dust removal equipment in dust filtration, but it also has the following problems. First, it is not resistant to high temperature. When the gas temperature exceeds 200 ° C, it cannot be used. Even the bag filter made of glass fiber cannot It can only be used below 400°C; second, when the gas humidity is high (humid), the dust adheres to the bag and is difficult to fall off, making the dust removal equipment unable to operate normally; third, dust recovery is easy to generate secondary dust, and the regeneration of the bag is not complete. Reduce dust removal efficiency. [0003] Ceramic membranes have been widely used in sewage treatment, high-temperature flue gas treatment and dust collection, and have played an important role in environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/10C04B33/13
Inventor 肖汉宁李格郭文明
Owner 湖南科一环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com