A kind of ultraviolet curing repair glue and preparation method thereof
A repair glue and ultraviolet light technology, applied in the direction of adhesives, epoxy resin glue, adhesive types, etc., can solve the problems of short service cycle, long curing time, high price, etc., to achieve lasting repair effect, save manpower, convenient The effect of on-site operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0026] The preparation method of the UV-curable repair glue includes the steps of preparing component A, the step of preparing component B, and the step of mixing component A and component B. The specific steps of the preparation method of the repair glue are as follows:
[0027] (1) Preparation of epoxy acrylic resin
[0028] Weigh epoxy resin and acrylic acid in proportion, wherein: the molar ratio of epoxy group to carboxyl group is 1-5:1, mix epoxy resin with a small amount of hydroquinone, the content of which is 0.1wt% -0.3wt%, heat to 80-90°C, then slowly drop the mixture of acrylic acid and benzyltriethylammonium bromide, wherein the content of benzyltriethylammonium bromide is 0.6wt%-1.5wt%, to control the reaction The temperature is below 100°C, after the dropwise addition, the temperature is raised to 100-105°C, and the reaction takes two hours. After the reaction, the temperature is lowered to below 80° C., and the thinner tripropylene glycol diacrylate (TPGDA) is...
Embodiment 1
[0040] (1) take by weighing 25 grams of epoxy resin and 9 grams of acrylic acid, the addition of hydroquinone is 0.2wt%, the addition of benzyltriethylammonium bromide is 0.9wt%, epoxy resin and p-phenylene Mix the diphenols, heat to 80-90°C, then slowly drop the mixture of acrylic acid and benzyltriethylammonium bromide, control the reaction temperature below 100°C, after the addition, raise the temperature to 100-105°C, and react two times Hour. After the reaction, the temperature was lowered to below 80° C., and 9 grams of dipropylene glycol diacrylate (TPGDA) was mixed in.
[0041] (2) Take by weighing 1.2 grams of fumed silica, mix it in 20 milliliters of absolute ethanol, and make the white carbon black evenly dispersed in the ethanol by means of ultrasonic waves, then pour it into the reaction solution obtained in the step (1), Heat to reflux for 10-20 minutes, then distill under reduced pressure to remove ethanol, and cool down to 60°C.
[0042] (3) Mixed with UV cur...
Embodiment 2
[0051] (1) take by weighing 25 grams of epoxy resin and 5.3 grams of acrylic acid, the addition of hydroquinone is 0.2wt%, the addition of benzyltriethylammonium bromide is 0.9wt%, epoxy resin and p-phenylene Mix the diphenols, heat to 80-90°C, then slowly drop the mixture of acrylic acid and benzyltriethylammonium bromide, control the reaction temperature below 100°C, after the addition, raise the temperature to 100-105°C, and react two times Hour. After the reaction, the temperature was lowered to below 80° C., and 6 grams of dipropylene glycol diacrylate (TPGDA) was mixed in.
[0052] (2) Weigh 1 gram of fumed silica, mix it into 20 milliliters of absolute ethanol, and use ultrasonic waves to uniformly disperse the fumed silica in ethanol, and then pour it into the reaction solution obtained in step (1) , heated to reflux for 10-20 minutes, and then distilled under reduced pressure to remove ethanol, and lower the temperature to 60°C.
[0053] (3) Mixed with UV curing epo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com