Anticorrosive self-cleaning paint

A coating and self-cleaning technology, used in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve problems such as damage to electronic components, and achieve the effects of high sealing, good insulation and moderate hardness

Inactive Publication Date: 2015-04-01
JIANGSU NUOFEI NEW MATERIAL TECH
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing anti-corrosion and self-cleaning coatings will shrink and release heat wh

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The anti-corrosion self-cleaning coating is prepared by reacting the following raw materials in parts by weight:

[0026] 45 parts of diphenyldimethoxysilane;

[0027] 10 parts vinyl;

[0028] 1 part of methyl ethyl ketone;

[0029] 5 parts of ethoxyethanol;

[0030] 0.5 parts of iron oxide;

[0031] 0.5 parts of catalyst;

[0032] 5 parts of dimethylpropane.

Embodiment 2

[0034] An anti-corrosion self-cleaning coating is prepared by reacting the following raw materials in parts by weight:

[0035] 60 parts of diphenyldimethoxysilane;

[0036] 15 parts vinyl;

[0037] 5 parts of methyl ethyl ketone;

[0038] 8 parts of ethoxyethanol;

[0039] 0.8 parts of iron oxide;

[0040] 1 part catalyst;

[0041] 15 parts of dimethyl propane.

Embodiment 3

[0043] An anti-corrosion self-cleaning coating is prepared by reacting the following raw materials in parts by weight:

[0044] 55 parts of diphenyldimethoxysilane;

[0045] 13 parts vinyl;

[0046] 3 parts of methyl ethyl ketone;

[0047] 7 parts of ethoxyethanol;

[0048] 0.6 parts of iron oxide;

[0049] 0.8 parts of catalyst;

[0050] 11 parts of dimethyl propane.

[0051] The preparation method of above each embodiment:

[0052] (1) Add diphenyldimethoxysilane, vinyl, methyl ethyl ketone to the kneader in order, and stir evenly;

[0053] (2) Continue to add dimethyl propane, heat up and vacuumize and stir, and it is worth the base material;

[0054] (3) Grinding the prepared base material into a powder base material with a grinder;

[0055] (4) Put the powdery base material into the stirring tank, then add ethoxyethanol, catalyst and iron oxide, and stir evenly under vacuum to prepare the self-cleaning coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a self-cleaning paint, particularly an anticorrosive self-cleaning paint. The anticorrosive self-cleaning paint is prepared from the following raw materials in parts by weight: 20-30 parts of tetramethyldivinyl disiloxane, 25-40 parts of methylethoxy silicon oil, 10-15 parts of hydroxy hydrogenous silicon oil, 15-20 parts of chlorotoluene, 1-5 parts of ethanedioic acid, 0.1-0.5 part of cyclopentanol and 0.3-0.7 part of catalyst. The anticorrosive self-cleaning paint can not generate shrinkage or release heat, and has the advantages of moderate hardness, favorable thermal conductivity, favorable electric insulativity and high sealability.

Description

technical field [0001] The invention relates to self-cleaning coatings, especially anti-corrosion self-cleaning coatings. Background technique [0002] With the increasingly high integration requirements of electronic equipment products, more and more electronic products adopt packaging structure, and the use of self-cleaning coatings to encapsulate electronic components can strengthen the integrity of electronic devices and improve the resistance to external shocks and vibrations. Resistance, improving the insulation between internal components and circuits, is conducive to the miniaturization and weight reduction of devices, avoiding direct exposure of components and circuits to the environment, and improving the waterproof and moisture-proof performance of devices. [0003] The existing anti-corrosion self-cleaning coatings will produce shrinkage and exothermic phenomena when they are cured into elastomers, which may easily cause damage to electronic components. Content...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/06C09D183/07C09D183/05C09D183/04C09D7/12C09D5/08C09D5/16
Inventor 邹玥
Owner JIANGSU NUOFEI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap