A kind of preparation method of antibacterial polyester fabric

A polyester fabric, water washing technology, applied in the direction of textiles and papermaking, fiber treatment, fiber type, etc., can solve the problems of fabric antibacterial durability is not ideal, nano-silver fastness defects, etc., to achieve good antibacterial effect, broad-spectrum antibacterial Good effect of sex and firmness

Active Publication Date: 2016-05-04
MAANSHAN JINZI TEXTILE OMAMENT +1
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above method is directly applied to the preparation of antibacterial fabrics. Although a certain degree of antibacterial properties can be obtained, there are still defects in the firmness of nano-silver on the base fabric, which often leads to unsatisfactory antibacterial durability of fabrics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: antibacterial rate 95~98.3% antibacterial polyester fabric preparation method, the concrete steps of this method are as follows:

[0015] (1) The polyester fabric is immersed in 2% Na by mass fraction as it is. 2 CO 3 After soaking in the solution for 30 minutes, washing with a large amount of distilled water, and drying at 40°C, a modified polyester fabric A was obtained.

[0016] (2) At 80°C, soak modified polyester fabric A in a mixed solution composed of alizarin red and cyclamate for 1 hour, wash with a large amount of water, and dry at 40°C to obtain modified polyester fabric B. The molar concentration of alizarin red in a mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 , the molar concentration of cyclamate in the mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 .

[0017] (3) Immerse the modified polyester fabric B in a mixed solution composed of hydrochloric acid and aniline. After stirring at room ...

Embodiment 2

[0023] Embodiment 2: antibacterial rate 97~99.7% antibacterial polyester fabric preparation method, the concrete steps of this method are as follows:

[0024] (1) The polyester fabric is immersed in 2% Na by mass fraction as it is. 2 CO 3 After soaking in the solution for 30 minutes, washing with a large amount of distilled water, and drying at 40°C, a modified polyester fabric A was obtained.

[0025] (2) At 80°C, soak modified polyester fabric A in a mixed solution composed of alizarin red and cyclamate for 1 hour, wash with a large amount of water, and dry at 40°C to obtain modified polyester fabric B. The molar concentration of alizarin red in a mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 , the molar concentration of cyclamate in the mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 .

[0026] (3) Immerse the modified polyester fabric B in a mixed solution composed of hydrochloric acid and aniline. After stirring at room ...

Embodiment 3

[0032] Embodiment 3: antibacterial rate 95.4~98.2% antibacterial polyester fabric preparation method, the specific steps of this method are as follows:

[0033] (1) The polyester fabric is immersed in 2% Na by mass fraction as it is. 2 CO 3 After soaking in the solution for 30 minutes, washing with a large amount of distilled water, and drying at 40°C, a modified polyester fabric A was obtained.

[0034] (2) At 80°C, soak modified polyester fabric A in a mixed solution composed of alizarin red and cyclamate for 1 hour, wash with a large amount of water, and dry at 40°C to obtain modified polyester fabric B. The molar concentration of alizarin red in a mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 , the molar concentration of cyclamate in the mixed solution composed of alizarin red and cyclamate is 0.01mmol L -1 .

[0035] (3) Immerse the modified polyester fabric B in a mixed solution composed of hydrochloric acid and aniline. After stirring at roo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of antibacterial polyester fabrics and belongs to the technical field of textile materials. The preparation method comprises the following steps: after sequentially carrying out continuous modification treatment on polyester fabric original samples including clothing, tablecloth and curtains by virtue of a Na2CO3 solution, a mixed solution of alizarin red and sodium cyclamate, a mixed solution of aniline, hydrochloride and ammonium persulfate, a mixed solution of DL-mercaptosuccinic acid and D-penicillamine and a nano-silver solution, putting the treated polyester fabric original samples into a silver tetrafluoroborate aqueous solution, carrying out reaction at room temperature for 30 minutes, washing the product by a great deal of water, and drying at the temperature of 40 DEG C to obtain the antibacterial polyester fabrics. The antibacterial polyester fabrics prepared by the preparation method have the broad-spectrum antibacterial property, are good in antibacterial effect particularly on staphylococcus aureus, bacillus subtilis, Escherichia coli and pseudomonas aeruginosa, are strong in persistence and have the single-strain inhibitory rate reaching 95-99.7 percent after being washed for 30 times.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and in particular relates to a preparation method of an antibacterial polyester fabric. Background technique: [0002] With the strengthening of people's health awareness, textiles that are beneficial to health and have health care functions are more and more favored by people, and exploring functional textiles has become a research hotspot in the textile industry (Li Zhizhi et al., "Nano silver antibacterial fiber in textile industry application", "Knitting Industry", 2013, 7, 65-66). Whether it is clothing and apparel textiles, or decorative textiles such as tablecloths and curtains, human secretions such as sweat, sebum flakes, oil stains, and traces of food will inevitably adhere to them during use. A good medium (Chinese CN103774265A "An antibacterial fiber and its preparation method"). Therefore, preparing and developing antibacterial fabrics is a problem to be solved urgently ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/82D06M11/83D06M13/325D06M13/252D06M11/60D06M13/335D06M11/11D06M13/256D06M11/76D06M101/32
Inventor 夏友谊陈治才吴祖坡古绪鹏陈乐柱乔红斌
Owner MAANSHAN JINZI TEXTILE OMAMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com