A kind of mercapto-modified graphene oxide and preparation method thereof

A graphene and graphene sheet technology, applied in the field of nanomaterials, achieves the effects of simple preparation process, widened synthesis means and application fields, and less time-consuming and energy-consuming

Active Publication Date: 2016-04-27
ZHEJIANG TANGUSHANGXI MATERIAL SCI & TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there is still relatively little work on mercapto-containing graphene oxide and its preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mercapto-modified graphene oxide and preparation method thereof
  • A kind of mercapto-modified graphene oxide and preparation method thereof
  • A kind of mercapto-modified graphene oxide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Take 2 mL of a 100 mg / mL graphene oxide solution dissolved in DMF and a powder particle size of 40 μm in a 25 mL flask, add 12 mL of deionized water and 300 μL of triethylamine to it, and add 20 mg of thiol during 20 minutes of nitrogen gas flow. Sodium acetate, stirred and reacted at room temperature for 2 days to obtain thioester-modified latent sulfur graphene oxide. The obtained product was washed with deionized water and stirred for 24 hours to obtain mercapto-modified graphene oxide. The obtained mercapto-modified graphene oxide product was characterized by XPS spectrum, infrared spectrum and Raman spectrum. The XPS spectrum of the mercapto-modified graphene oxide ( figure 2 ) and the XPS spectrum of graphene oxide ( figure 1 ) for comparison, it can be found that 1.06% of sulfur elements appeared in the mercapto-modified graphene oxide product, indicating that the introduction of mercapto groups may be successful; the infrared spectrum of the mercapto-modified...

Embodiment 2

[0021] Take 2 mL of 100 mg / mL graphene oxide solution dissolved in DMF in a 25 mL flask, add 12 mL of deionized water and 300 μL of triethylamine to it, add 60 μL of thioacetic acid during 20 minutes of nitrogen gas flow, and put The reaction was stirred for 2 days to obtain thioester-modified latent sulfur graphene oxide. The obtained product was washed with deionized water and stirred for 24 hours to obtain mercapto-modified graphene oxide.

Embodiment 3

[0023] Take 2 mL of 100 mg / mL graphene oxide solution dissolved in DMSO in a 25 mL flask, add 12 mL of deionized water and 300 μL of triethylamine to it, add 60 μL of thioacetic acid during 20 minutes of blowing nitrogen gas, and incubate at 40 °C The reaction was stirred for 2 days to obtain thioester-modified latent sulfur graphene oxide. Add 100 mL of 5% dilute hydrochloric acid to the obtained product, then wash with deionized water, and stir for 24 hours to obtain mercapto-modified graphene oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a thiol-modified graphene oxide and a preparation method thereof. The mercapto-modified graphene oxide is a modified graphene oxide product obtained by introducing mercapto groups into the graphene oxide sheet structure. The preparation method is: after mixing graphene oxide solution, solvent and triethylamine evenly, add thiocarboxylic acid or thiocarboxylate under nitrogen protection; react at 10-70 degrees Celsius for 1-7 days to obtain thioester Modified latent sulfur graphene oxide; the thioester modified latent sulfur graphene is centrifugally washed with deionized water to obtain thiol-modified graphene oxide; or the thioester modified latent sulfur graphene is mixed with dilute After the hydrochloric acid is mixed evenly, it is centrifuged and washed with deionized water to obtain mercapto-modified graphene oxide. The preparation process of the present invention is simple, safe and controllable, less time-consuming and energy-consuming, and the mercapto-modified graphene oxide is prepared, which further broadens the synthesis means and application fields of graphene-derived materials and sulfur-containing compounds.

Description

technical field [0001] The invention relates to the field of nanomaterials, in particular to a mercapto-modified graphene oxide and a preparation method. Background technique [0002] Since the advent of monolithic graphite in 2010, its excellent electrical, mechanical, optical, thermal and other properties have attracted widespread attention from scholars all over the world, and a large number of graphene-based materials and work have emerged. As the precursor of graphene, graphene oxide is the most important intermediate for the macroscopic assembly and modification of graphene materials. Most of the macro-assembly materials fibers, films, and aerogels that have been realized so far are prepared through graphene oxide intermediates. [0003] Mercapto compounds are a class of compounds with one or more SH groups. They play an important role in the artificial synthesis of life sciences and natural products. They are important industrial raw materials and are widely used in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/04
Inventor 高超彭蠡金昱李嘉辰魏杨扬郑耀臣
Owner ZHEJIANG TANGUSHANGXI MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap